Preparation method of mold release agent durable in storage

The technology of a release agent and fluorodecyltrimethoxysilane is applied in the field of preparation of a storage-resistant release agent, which can solve the problems of easy delamination, easy oxidation, poor stability, etc. The effect of heat resistance

Active Publication Date: 2017-07-18
江苏康姆罗拉特种陶瓷有限公司
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Most of the existing release agent technologies have the disadvantages of poor stability, easy delamination, and easy oxidation. Therefore, it is necessary to develop a release agent product that can be stored for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of mold release agent durable in storage

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] In a 2000L reactor, add 100Kg of full (17) fluorodecyl trimethoxysilane, 12Kg of methoxy polyethylene glycol methacrylate, 4Kg of poly-4-methyl-1-pentene, and methyl iso Butyl methanol 200Kg, hydroxypropyl methylcellulose phthalate 5Kg, 5,7-difluoro-2,3-dihydrobenzofuran 5Kg, N-tert-butoxycarbonyl-N(imidazole)- (4-Methylbenzenesulfonyl)-L-histidine 0.05Kg, stirred at a speed of 1200rpm for 1h to obtain a release agent product. Number M-1.

Embodiment 2

[0016] In a 2000L reactor, add 100Kg of full (17) fluorodecyltrimethoxysilane, 5Kg of methoxypolyethylene glycol methacrylate, 1Kg of poly-4-methyl-1-pentene, and methyl iso Butyl methanol 100Kg, hydroxypropyl methylcellulose phthalate 1Kg, 5,7-difluoro-2,3-dihydrobenzofuran 1Kg, N-tert-butoxycarbonyl-N (imidazole)- (4-Methylbenzenesulfonyl)-L-histidine 0.01Kg, stirred at a speed of 1200rpm for 0.5h to obtain a release agent product. Number M-2.

Embodiment 3

[0018] In a 2000L reactor, add 100Kg of full (17) fluorodecyl trimethoxysilane, 20Kg of methoxy polyethylene glycol methacrylate, 8Kg of poly-4-methyl-1-pentene, and methyl iso Butyl methanol 300Kg, hydroxypropyl methylcellulose phthalate 10Kg, 5,7-difluoro-2,3-dihydrobenzofuran 10Kg, N-tert-butoxycarbonyl-N (imidazole)- 0.1Kg of (4-methylbenzenesulfonyl)-L-histidine was stirred for 1.5h at a speed of 1200rpm to obtain a release agent product. Number M-3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation method of a mold release agent durable in storage. A mold release agent product is obtained by adding (heptadecafluoro-1,1,2,2-tetradecyl)trimethoxysilane, poly(ethylene glycol) methyl ether meth-acrylate, poly-4-methyl-1-amylene, methyl isobutyl carbinol, hydroxypropyl methylcellulose phthalate, 5,7-difluoro-2,3-dihydrobenzofuran and N-(tert-butoxycarbonyl)-1-[(4-methylphenyl)sulfonyl]-L-histidine in an agitated vessel to be stirred and diffused.

Description

Technical field [0001] The invention relates to a method for preparing a release agent, in particular to a method for preparing a storage resistant release agent. Background technique [0002] The release agent is a coating applied between the casting and the mold, and its function is to make the surface of the casting product smooth and easy to leave the mold. Alloy metal products, such as alloy equipment parts, automobile manufacturing related products, etc., require higher temperatures during die casting, and higher heat resistance is required for corresponding release agent products. At present, the most widely used release agent product is the water-based emulsion release agent, which has better heat resistance and can be widely used in the die casting of larger metal castings. [0003] CN100571926 discloses a mold release agent used in die casting industries such as aluminum alloys, and particularly relates to a heat-resistant mold release agent, which contains 0.1-50% by we...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22C3/00
CPCB22C3/00
Inventor 王琪宇王新
Owner 江苏康姆罗拉特种陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com