Reflective paint for led street lamp and preparation method of reflective paint

A technology of led street lights and reflective coatings, applied in reflective/signal coatings, coatings, lampshades, etc., can solve the problems of nighttime accidents, poor reflectivity, poor environmental protection of solvent-based coatings, etc., to avoid accidents and high peeling resistance. , the effect of reducing casualties

Inactive Publication Date: 2017-07-25
JIANGXI ZHUOZHAO OPTOELECTRONICS TECH
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the development of logistics, and the deep-rooted reasons such as the lag of China's highway construction, in order to improve the interest rate of the highway, the number of traffic and pedestrians at night is increasing. The reflective layer of street lamps currently on the market is composed of topcoat and primer. The top coat is a reflective coating, mainly solvent-based polyurethane coating. The solvent-based polyurethane coating film has the characteristics of high hardness, strong adhesion, high wear resistance and good solvent resistance, but its reflective rate is 60%, which is relatively low. Poor, easily lead to the occurrence of accidents at night; and solvent-based coatings are poor in environmental protection, so in order to continuously improve the reflective effect of street lamps, ensure the safety of driving and pedestrians, and improve environmental protection, the present invention has studied a reflective coating for led street lamps and its Preparation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of reflective paint for led street lamp, it is made of the following raw materials by weight:

[0020] 2-thiolbenzimidazole 2, mannitol 5-7, alkylated diphenylamine 2, hollow glass microspheres 6, tetrakisphosphonium sulfate 3, dodecafluoroheptylpropyltrimethoxysilane 1, Methylcellulose 4, 4-chloromethyl styrene 150, aluminum isopropoxide 16, reflective powder 3, 12% hydrogen peroxide solution 27-30, phytate 3, stannous sulfide 1, Nano titanium dioxide 15, chlorinated paraffin 9, dicumyl peroxide 4.

[0021] A preparation method for reflective paint for led street lamps, comprising the following steps:

[0022] (1) Take 2-mercaptobenzimidazole, add it to 30 times its weight in absolute ethanol, stir evenly, raise the temperature to 65°C, add dodecafluoroheptylpropyltrimethoxysilane, keep stirring In 20 minutes, the silanol dispersion was obtained;

[0023] (2) Take aluminum isopropoxide, add it to deionized water 50 times its weight, stir evenly, add dropwise ...

Embodiment 2

[0031] A kind of reflective paint for led street lamp, it is made of the following raw materials by weight:

[0032] 2-thiolbenzimidazole 1, mannitol 5, alkylated diphenylamine 2, hollow glass microspheres 6, tetrakisphosphonium sulfate 2, dodecafluoroheptylpropyltrimethoxysilane 1, methyl Cellulose 4, 4-chloromethyl styrene 130, aluminum isopropoxide 16, reflective powder 3, 10% hydrogen peroxide solution 27, phytic acid ester 3, stannous sulfide 1-2, nano titanium dioxide 10. Chlorinated paraffin 7. Dicumyl peroxide 4.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a reflective paint for a led street lamp. The reflective paint is prepared from the following raw materials in parts by weight: 1-2 parts of 2-mercaptobenzimidazole, 5-7 parts of mannitol, 2-3 parts of alkylated diphenylamine, 6-8 hollow glass beads, 2-3 parts of tetrakis hydroxymethyl phosphonium sulfate, 1-2 parts of dodecyl trimethoxysilane, 4-6 parts of methylcellulose, 130-150 parts of 4-chloromethyl styrene, 16-20 parts of aluminum isopropoxide, 3-4 parts of reflective powder, 27-30 parts of 10-12% hydrogen peroxide solution, 3-4 parts of inositol hexaphosphate, 1-2 parts of stannous sulfide, 10-15 parts of nanometer titania, 7-9 parts of chlorinated paraffin and 4-6 parts of dicumyl peroxide. The reflective powder is taken as a reflective assistant, so that the reflective paint has a good reflective effect, and the obtained coating is good in tenacity, high in cohesiveness on the surface of a street lamp shade, high in peel strength, environment-friendly and free of pollution.

Description

technical field [0001] The invention belongs to the field of coatings, in particular to a reflective coating for LED street lamps and a preparation method thereof. Background technique [0002] With the development of logistics, and the deep-rooted reasons such as the lag of China's highway construction, in order to improve the interest rate of the highway, the number of traffic and pedestrians at night is increasing. The reflective layer of street lamps currently on the market is composed of topcoat and primer. The top coat is a reflective coating, mainly solvent-based polyurethane coating. The solvent-based polyurethane coating film has the characteristics of high hardness, strong adhesion, high wear resistance and good solvent resistance, but its reflective rate is 60%, which is relatively low. Poor, easily lead to the occurrence of accidents at night; and solvent-based coatings are poor in environmental protection, so in order to continuously improve the reflective effec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D151/02C09D5/33C09D7/12C08F251/02C08F212/14C08F2/44F21V3/04
CPCC08F2/44C08F251/02C08K2003/2227C08K2003/2241C08K2201/011C09D5/004C09D151/02C09D7/61C09D7/63C09D7/65F21V3/10C08L91/06C08K13/04C08K7/28C08K3/22C08F212/14
Inventor 彭智斌
Owner JIANGXI ZHUOZHAO OPTOELECTRONICS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products