PVC (polyvinyl chloride) biomass foaming composite and preparation method thereof

A composite material and biomass technology, applied in the field of new PVC biomass foam composite material and its preparation, can solve the problems of weak corrosion resistance, poor toughness, narrow processing temperature range, etc.

Active Publication Date: 2017-08-11
江西板森新材料科技有限公司
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The Chinese invention patent application with publication number CN105001555A discloses a PVC-M pipe with high impact resistance and aging resistance. This document discloses the use of raw materials such as PVC, light calcium carbonate, MBS, calcium sulfate whiskers, and carbon black. , the synergistic effect of 6-tert-butyl-p-propanol and ethanethiol to make aging-resistant PVC plastic products, but the preparation process of this technology is complicated to operate, and light calcium carbonate and calcium carbonate whiskers are used. In the middle, the current is high, the energy consumption is large, and the ribs formed by calcium carbonate are irregular
The Chinese invention patent application with the publication number 102010552A discloses a PVC / whisker calcium sulfate composite material and its preparation method. The composite material is made by combining PVC and whisker calcium sulfate, which increases the strength of PVC, but the composition used The foaming of the composite material formed by sub-combination is irregular, so it is difficult to meet higher requirements in terms of strength, and the PVC material in the prior art also has the problems of poor toughness, narrow processing temperature range, and weak corrosion resistance
Some people have also tried to use natural anhydrite and light calcium carbonate to prepare higher-strength polyvinyl chloride pipes. For example, the Chinese invention patent application with publication number CN103740015A discloses a high-strength polyvinyl chloride pipe, but the natural anhydrite Compared with light calcium carbonate and acrylic resin, the foaming effect is poor, and high-strength profiles with smooth and uniform foaming cannot be obtained

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PVC (polyvinyl chloride) biomass foaming composite and preparation method thereof
  • PVC (polyvinyl chloride) biomass foaming composite and preparation method thereof
  • PVC (polyvinyl chloride) biomass foaming composite and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-7

[0035] In terms of parts by weight, the composition of the new PVC biomass foamed profiles of Examples 1-7 of the present invention is as follows according to the serial number 1-7:

[0036] Table 1

[0037]

Embodiment 1-3

[0038] Embodiment 1-3 The technique of producing novel PVC biomass foamed profiles is as follows:

[0039] Step 1. Put the ingredients in the table into a high-speed mixer and mix them thoroughly at high speed until the temperature reaches 110-120°C. Then transfer the mixture from the high-speed mixer to a low-speed cold mixing pot, and lower the temperature to 40-60°C to obtain a mixed material;

[0040] Step 2, kneading and extruding the mixture in a counter-rotating conical twin-screw extruder;

[0041] Step 3, pass the extruded material through the heating mold (the temperature of the heating mold is 165-180°C), and then pump negative pressure to cool and shape it;

[0042] Step 4, the shaped and cooled material is drawn and cut into products of a certain size by the auxiliary machine. The working parameters of the counter-rotating conical twin-screw extruder in this embodiment are as follows: the processing temperature is 156°C in the first zone, 165°C in the second zone,...

Embodiment 4-7

[0047] Embodiment 4-7 The technique of producing novel PVC biomass foamed profiles is as follows:

[0048] Step 1: Put the ingredients listed in the table into the high-speed mixer and mix them thoroughly at high speed until the temperature reaches 110-120°C, then transfer the mixture from the high-speed mixer to a low-speed cold mixing pot, and lower the temperature to 40-60°C to obtain a mixture material;

[0049] Step 2, kneading and extruding the mixture in a counter-rotating conical twin-screw extruder;

[0050] Step 3, pass the extruded material through the heated mold and then pump negative pressure to cool and shape it;

[0051] Step 4, the shaped and cooled material is drawn and cut into products of a certain size by the auxiliary machine. The process parameters of the counter-rotating conical twin-screw extruder in this example are as follows: the processing temperature is 156°C in the first zone, 165°C in the second zone, 175°C in the third zone, 180°C in the four...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a composite, in particular to a PVC (polyvinyl chloride) biomass foaming composite and a preparation method thereof. The novel PVC biomass foaming composite is prepared from components of preparation raw materials in parts by weight as follows: 100 parts of PVC, 10-100 parts of PVC renewable materials, 5-30 parts of biomass powder, 10-50 parts of calcium sulfate, 3-8 parts of a stabilizer, 0.6-3.5 parts of a foaming agent, 2-15 parts of a foaming regulator, 0.3-2.0 parts of an internal lubricant, 0.3-2.0 parts of an external lubricant, 1.0-1.5 parts of a PVC processing aid and 0.3-1.2 parts of a coupling agent. By means of the formula, the filler content of a PVC foaming system can be increased by 20%-50%, the weight of the product per meter is basically unchanged, and the material has higher cost performance. With the adoption of technique principles of new materials, the PVC biomass foaming composite has creativity of new material application, has characteristics of resource utilization, energy conservation, environmental protection and green economy and is suitable for industrial production.

Description

technical field [0001] The invention relates to composite materials, in particular to a novel PVC biomass foamed composite material and a preparation method thereof. Background technique [0002] PVC wood-plastic materials are environmentally friendly products, and the processing technology is very mature. Through molds and co-extrusion, products with novel shapes and appearances can be designed, and the appearance is very close to wood, and some are even more beautiful than wood. The material can be recycled and reused, which brings good economic and social effects in terms of promoting resource recycling, energy conservation and emission reduction, and sustainable economic development. However, existing PVC wood-plastic materials still have shortcomings such as excessive production cost pressure, poor material mechanical properties and weather resistance, poor corrosion resistance, and high production energy consumption, which limits its application field. my country is a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L51/04C08K13/02C08K3/30C08J9/10C08J9/06
CPCC08J9/06C08J9/103C08J2203/04C08J2203/18C08J2327/06C08J2451/04C08L27/06C08L2203/14C08L2205/035C08L2207/20C08L51/04C08K13/02C08K2003/3045
Inventor 彭梅醒苏胜培骆仁锋杨治刘连斌
Owner 江西板森新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products