TPU film with good moisture permeation rate as well as manufacturing method and application of TPU film

A technology of moisture permeability and film, applied in the field of TPU film and its manufacturing, can solve the problems of inability to quickly discharge sweat from the skin, low moisture permeability, inability to block rainwater protection, etc., to ensure long-term wearability and excellent waterproofness. , the effect of good puncture resistance

Inactive Publication Date: 2017-08-15
ZHEJIANG HUANLONG NEW MATERIAL SCI & TECH
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the moisture permeability rate of products produced by TPU materials is low. In hot weather, the sweat emitted by the human body cannot be quickly discharged to give the skin a dry and comfortable feeling. In rainy weather, it cannot prevent rainwater from entering the clothing to protect it. function, thus having to be tied to the weather while exercising

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] This embodiment provides a TPU film with good moisture permeability, which includes the following materials according to the mass fraction ratio:

[0038] 30 parts of perfluoropolyether diols;

[0039] 15 parts of chain extender;

[0040] 50 parts of aliphatic diisocyanate;

[0041] 10 parts of TPO resin;

[0042] 5 parts of masterbatch;

[0043] Antioxidant 2 parts;

[0044] 4 parts of anti-yellowing agent;

[0045] 0.5 parts of erucamide;

[0046] 0.5 parts of oleic acid amide;

[0047] 0.5 parts of stearic acid.

Embodiment 2

[0049] This embodiment provides a TPU film with good moisture permeability, which includes the following materials according to the mass fraction ratio:

[0050] 60 parts of perfluoropolyether diols;

[0051] 10 parts of chain extender;

[0052] Aliphatic diisocyanate 80 parts;

[0053] 4 parts of TPO resin;

[0054] 8 parts of masterbatch;

[0055] Antioxidant 1 part;

[0056] Anti-yellowing agent 2 parts;

[0057] 1 part erucamide;

[0058] 1 part of oleic acid amide;

[0059] 1 part stearic acid.

Embodiment 3

[0061] This embodiment provides a TPU film with good moisture permeability, which includes the following materials according to the mass fraction ratio:

[0062] 40 parts of perfluoropolyether diols;

[0063] 12 parts of chain extender;

[0064] 60 parts of aliphatic diisocyanate;

[0065] 8 parts of TPO resin;

[0066] 6 parts of masterbatch;

[0067] 1.2 parts of antioxidant;

[0068] 3 parts of anti-yellowing agent;

[0069] 0.7 parts of erucamide;

[0070] 0.7 parts of oleic acid amide;

[0071] 0.7 parts of stearic acid.

[0072] Preferably, the color masterbatch is TPU color masterbatch.

[0073] Preferably, the antioxidant is antioxidant TNP.

[0074] Preferably, the anti-yellowing agent is 2-(2'-hydroxyl-3',5'-dicumylphenyl)benzotriazole.

[0075] The invention also discloses a preparation method of a TPU film with good moisture permeability, comprising the following steps:

[0076] 1) Prepare fluorine-containing TPU by perfluoropolyether diol, chain extende...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention discloses a TPU film with a good moisture permeation rate as well as a manufacturing method and application of the TPU film. The TPU film contains the following materials: perfluoropolyether diol, a chain extender, aliphatic diisocyanate, TPO resin, master batches, an antioxidant, a light stabilizer, an anti-yellowing agent, erucamide, oleamide and stearic acid. The preparation method of the TPU film comprises the following steps: (1) preparing fluorine-containing TPU; (2) uniformly stirring fluorine-containing TPU with the TPO resin, the master batches, the antioxidant, the light stabilizer, the anti-yellowing agent, erucamide, oleamide and stearic acid; and (3) adding the material obtained in the step (2) into an internal mixer, carrying out internal mixing for 5-10 minutes, and extruding by virtue of an extruder. The TPU film is used as a fabric of garments and shoes. The TPU film utilizing the technical scheme has a good moisture permeation rate and excellent water tolerance, and a product is safe, environment-friendly and comfortable.

Description

technical field [0001] The invention relates to a TPU film with good moisture permeability and its manufacturing method and application, belonging to the technical field of TPU material application. Background technique [0002] TPU (Thermoplastic polyurethanes) is called thermoplastic polyurethane elastomer rubber. It is mainly divided into polyester type and polyether type. It has a wide range of hardness (60HA-85HD), wear resistance, oil resistance, transparency, and good elasticity. It is widely used in daily necessities and sporting goods. , toys, decorative materials and other fields are widely used, halogen-free flame-retardant TPU can also replace soft PVC to meet the environmental protection requirements of more and more fields. The so-called elastomer refers to a polymer material with a glass transition temperature lower than room temperature, an elongation at break > 50%, and better recovery after external force is removed. Polyurethane elastomers are a rela...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/08C08L23/00C08L75/04C08K5/20C08K5/09C08G18/50
CPCC08L75/08C08G18/5015C08J5/18C08J2375/08C08J2423/00C08K2201/014C08L2203/16C08L2205/02C08L2205/03C08L23/00C08L75/04C08K5/20C08K5/09
Inventor 黄林志鄢志亮
Owner ZHEJIANG HUANLONG NEW MATERIAL SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap