Aluminum alloy material surface treatment method
A technology for aluminum alloy materials and aluminum alloy surfaces, applied in the field of aluminum alloy materials, can solve the problems of difficult maintenance of galvanizing process operation, shorten the service life of electroless nickel plating solution, etc., so as to reduce the non-uniformity of corrosion and reduce the alkali etching treatment process. , the effect of high production efficiency
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0024] Example 1
[0025] A surface treatment method of aluminum alloy material includes the following treatment steps:
[0026] a. Pretreatment of aluminum alloy surface;
[0027] b. Polish the aluminum alloy surface with chemical reagents;
[0028] c. Conduct polar oxidation treatment on the surface of aluminum alloy;
[0029] d. Plating the aluminum alloy surface.
[0030] The pretreatment of step a is: removing oil stains on the surface of the aluminum alloy with an alkaline degreasing solution, the temperature of the alkaline degreasing solution is 50°C, and the decontamination is continued for 5 minutes.
[0031] The alkaline degreasing solution is Na3PO4 solution.
[0032] Step a: After pretreatment, wash with hot water at 60° C. and then wash with cold water until the surface of the aluminum alloy is free of water droplets.
[0033] The polishing treatment of step b is: cleaning the surface of the aluminum alloy at a temperature of 45°C with an alkaline washing solution to remove th...
Example Embodiment
[0037] Example 2
[0038] A surface treatment method of aluminum alloy material includes the following treatment steps:
[0039] a. Pretreatment of aluminum alloy surface;
[0040] b. Polish the aluminum alloy surface with chemical reagents;
[0041] c. Conduct polar oxidation treatment on the surface of aluminum alloy;
[0042] d. Plating the aluminum alloy surface.
[0043] The pretreatment of step a is: removing oil stains on the surface of the aluminum alloy with an alkaline degreasing solution, the temperature of the alkaline degreasing solution is 45°C, and the decontamination is continued for 5 minutes.
[0044] The alkaline degreasing liquid is Na2CO3 solution.
[0045] Step a: After pretreatment, wash with hot water at 40° C. and then wash with cold water until the surface of the aluminum alloy is free of water droplets.
[0046] The polishing treatment of step b is: cleaning the surface of the aluminum alloy at a temperature of 45°C with an alkaline washing solution to remove the ...
Example Embodiment
[0050] Example 3
[0051] A surface treatment method of aluminum alloy material includes the following treatment steps:
[0052] a. Pretreatment of aluminum alloy surface;
[0053] b. Polish the aluminum alloy surface with chemical reagents;
[0054] c. Conduct polar oxidation treatment on the surface of aluminum alloy;
[0055] d. Plating the aluminum alloy surface.
[0056] The pretreatment of step a is: removing oil stains on the surface of the aluminum alloy with an alkaline degreasing solution, the temperature of the alkaline degreasing solution is 50° C., and the decontamination is continued for 10 minutes.
[0057] The alkaline degreasing solution is Na5P3O10 solution.
[0058] Step a: After pretreatment, wash with hot water at 60° C. and then wash with cold water until the surface of the aluminum alloy is free of water droplets.
[0059] The polishing treatment of step b is: cleaning the aluminum alloy surface at a temperature of 50°C with an alkaline washing solution to remove the ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap