High-whiteness bone china for daily use and preparation method thereof

A technology of bone china and high whiteness, which is applied in the field of high-whiteness daily-use bone china and its preparation, which can solve the problems of poor thixotropy of bone china slurry, affecting the overall quality of ceramics, and unsatisfactory quality, so as to promote the mixing of components Reaction, good moisture absorption effect, effect of improving catalytic mixing effect

Inactive Publication Date: 2017-09-08
ANHUI QINGHUAFANG FINE BONE PORCELAIN
View PDF4 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But at present, the production of bone ash china is not common in my country, and the quality of production is not ideal. The bone ash china slurry use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A high-whiteness bone china for daily use, which is made of the following components: kaolin 22.5%, feldspar 8%, quartz 12%, sepiolite fiber 1.8%, brucite 1%, diatomite 4% %, sodium alginate 0.58%, dispersant 0.15%, bone ash powder balance. It also includes 0.3% of crop starch, which is selected from rice starch and potato starch compositions, and amylose in the crop starch accounts for 40 wt%. The dispersant is talcum powder and light calcium carbonate with a mass ratio of 2:3.

[0026] High-whiteness daily-use bone china, the preparation steps are as follows:

[0027] 1) Weigh the raw materials according to the mass ratio, pour water into diatomaceous earth and mix well until it becomes a thin paste, inject an appropriate amount of warm water at 38-40°C into sodium alginate and stir until dissolved, set aside;

[0028] 2) Add the dissolved sodium alginate solution into diatomaceous earth paste under the condition of stirring, keep stirring at 60°C for 20min, then ad...

Embodiment 2

[0033] A high-whiteness bone china for daily use, which is made of the following components: kaolin 24%, feldspar 10%, quartz 13%, sepiolite fiber 2.4%, brucite 1.2%, diatomite 3% %, sodium alginate 0.48%, dispersant 0.22%, bone ash powder balance. It also includes 1.6% of crop starch, the crop starch is selected from corn starch, and the amylose in the crop starch accounts for 30wt%. The dispersant is talcum powder and light calcium carbonate with a mass ratio of 2:3.

[0034] High-whiteness daily-use bone china, the preparation steps are as follows:

[0035] 1) Weigh the raw materials according to the mass ratio, pour water into diatomaceous earth and mix well until it becomes a thin paste, inject an appropriate amount of warm water at 38-40°C into sodium alginate and stir until dissolved, set aside;

[0036] 2) Add the dissolved sodium alginate solution into diatomaceous earth paste under stirring condition, keep stirring at 60°C for 30 minutes, then add sepiolite fiber i...

Embodiment 3

[0041] A high-whiteness bone china for daily use, which is made of the following components: kaolin 21.7%, feldspar 7%, quartz 14%, sepiolite fiber 2%, brucite 0.8%, diatomite 2% %, sodium alginate 0.56%, dispersant 0.2%, bone ash powder balance. It also includes 2% of crop starch, the crop starch is selected from corn starch and wheat starch composition, and the amylose in the crop starch accounts for 40wt%. The dispersant is talcum powder and light calcium carbonate with a mass ratio of 2:3.

[0042] High-whiteness daily-use bone china, the preparation steps are as follows:

[0043] 1) Weigh the raw materials according to the mass ratio, pour water into diatomaceous earth and mix well until it becomes a thin paste, inject an appropriate amount of warm water at 38-40°C into sodium alginate and stir until dissolved, set aside;

[0044] 2) Add the dissolved sodium alginate solution into diatomaceous earth paste under stirring condition, keep stirring at 60°C for 30 minutes, t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a high-whiteness bone china for daily use, and a preparation method thereof. The high-whiteness bone china for daily use is prepared from the following components in percentage content: 21 to 24 percent of kaolin, 7 to 11 percent of feldspar, 10 to 15 percent of quartz, 1.3 to 2.6 percent of sepiolite fiber, 0.3 to 1.2 percent of brucite, 2 to 5 percent of diatomite, 0.48 to 0.65 percent of sodium alginate, 0.15 to 0.25 percent of a dispersing agent and the balance of bone ash powder, through the steps of mixing, heating, precalcining, crushing, ball-milling, sintering and the like. The high-whiteness bone china for daily use has high thermoplasticity, high heat stability and high processability; and the prepared product has flat and smooth appearance, the mechanical strength and the light-transmitting property are remarkably improved, the whiteness can reach 82 percent, the rate of finished products can reach above 95 percent, and the comprehensive quality of the china for daily use is effectively improved.

Description

technical field [0001] The invention relates to the technical field of daily-use ceramics, in particular to a high-whiteness daily-use bone china and a preparation method thereof. Background technique [0002] The ceramic industry is a high-energy-consuming industry. With the rapid development of the ceramic industry, the problem of serious energy consumption has become increasingly prominent. According to statistics, in the ceramic industry, my country's energy consumption is 3.1 times the world average, 4.3 times that of OECD (Organization for Economic Cooperation and Development) countries and regions, and 9 times that of Japan. In the process of ceramic production, a large amount of raw materials such as kaolin are consumed every year, and the situation of depletion of kaolin and other resources is very serious. With the country's attention to environmental protection and the emphasis on the rational use of resources, the structural adjustment of the ceramic industry ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B33/16C04B33/135C04B33/36C04B33/13
CPCC04B33/1305C04B33/131C04B33/1355C04B33/16C04B33/36C04B2235/3206C04B2235/3418C04B2235/3463C04B2235/442C04B2235/5232C04B2235/96C04B2235/9607Y02P40/60
Inventor 裴仕林
Owner ANHUI QINGHUAFANG FINE BONE PORCELAIN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap