Bacterial cellulose-polylactic acid composite film and its preparation method, drug-carrying gauze based on composite film and its preparation method

A technology of bacterial cellulose and polylactic acid film, applied in biochemical equipment and methods, methods based on microorganisms, coatings, etc., can solve the problems of increasing patient pain, unfavorable post-injury healing, easy adhesion of wounds, etc., and achieve good tissue Compatibility, good product stability, and good skin compatibility

Pending Publication Date: 2017-09-19
SHAANXI UNIV OF SCI & TECH
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it is easy to stick to the wound during use, which is not conducive to post-injury healing. In se

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0050] Example 1

[0051] A medical gauze based on a bacterial cellulose-polylactic acid composite film and a preparation method thereof, including the following steps:

[0052] (1) Prepare polylactic acid film (Polylacticacid film, PLA film) by electrospinning method: prepare a mixed solvent of chloroform and ethanol (2:1, v / v) to dissolve PLA to obtain a PLA solution with a mass concentration of 30%; take Inject 4.5mL PLA solution into a glass syringe syringe; cut Φ5cm tin foil paper, clamp it on the receiving end to form a receiver and connect one end of the wire to the receiving end; turn on the electrospinning machine, adjust the receiving distance to 10cm, and the spinning temperature to 40℃; install Injector, connect the voltage wire, open the voltage control area to apply voltage to the receiving end and the tip of the syringe; adjust the advancing speed to 0.1mm / s, start spinning, and form a PLA film on the receiver; after the film is dry, use tweezers to gently remove the...

Example Embodiment

[0055] Example 2

[0056] A medical gauze based on a bacterial cellulose-polylactic acid composite film and a preparation method thereof, including the following steps:

[0057] (1) Prepare polylactic acid membrane (Polylacticacid membrane, PLA membrane) by electrospinning method: prepare a mixed solvent of chloroform and ethanol (3:1, v / v) to dissolve PLA to obtain a PLA solution with a mass concentration of 35%; take Inject 5.5mL PLA solution into the glass syringe syringe; cut Φ7cm tin foil paper, clamp it on the receiving end to form a receiver and connect one end of the wire to the receiving end; turn on the electrostatic spinning machine, adjust the receiving distance to 15cm, and the spinning temperature to 50℃; install Injector, connect the voltage wire, open the voltage control area to apply voltage to the receiving end and the tip of the syringe; adjust the advancing speed to 0.2mm / s, start spinning, and form a PLA film on the receiver; after the film is dry, use tweezers...

Example Embodiment

[0060] Example 3

[0061] A medical gauze based on a bacterial cellulose-polylactic acid composite film and a preparation method thereof, including the following steps:

[0062] (1) Prepare polylactic acid film (Polylacticacid film, PLA film) by electrospinning method: prepare a mixed solvent of chloroform and ethanol (4:1, v / v) to dissolve PLA to obtain a PLA solution with a mass concentration of 40%; take Inject 6.5mL PLA solution into a glass syringe syringe; cut Φ10cm tin foil paper, clamp it on the receiving end to form a receiver and connect one end of the wire to the receiving end; turn on the electrostatic spinning machine, adjust the receiving distance to 20cm and the spinning temperature to 60℃; install Injector, connect the voltage wire, open the voltage control area to apply voltage to the receiving end and the tip of the syringe; adjust the advancing speed to 0.3mm / s, start spinning, and form a PLA film on the receiver; after the film is dry, use tweezers to gently rem...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a bacterial cellulose-polylactic acid composite film and its preparation method. The preparation method includes steps of (1), preparing a polylactic acid film by a static spinning method; (2), preparing a bacterial cellulose-polylactic acid composite film by an in-situ composite method. The bacterial cellulose-polylactic acid composite film avoids use of toxic chemical crosslinking agent in preparation process, and has high compounding efficiency and good product stability. The invention further provides a drug-carrying gauze based the bacterial cellulose-polylactic acid composite film and its preparation method; the preparation method includes steps of A), preparing the bacterial cellulose-polylactic acid composite film; preparing a drug solution; B), soaking the bacterial cellulose-polylactic acid composite film in the drug solution, and performing oscillation absorption under a vacuum condition; C), taking out the bacterial cellulose-polylactic acid composite film. The drug-carrying gauze has good drug-carrying performance and can be degraded in a body.

Description

technical field [0001] The invention relates to the field of biological materials, in particular to a bacterial cellulose-polylactic acid composite film, a drug-loaded gauze based on the bacterial cellulose-polylactic acid composite film and a preparation method. Background technique [0002] Bacterial cellulose (BC) is a polysaccharide natural polymer synthesized by bacteria. It is a new type of biological material that has been widely studied at present. Its nano-network structure can prevent the invasion of microorganisms, and its porous structure makes it With high water holding capacity, it can absorb wound exudate, keep the wound dry, avoid wound infection, promote cell regeneration, good mechanical properties make it have better shape retention, and can be designed according to the application. At the same time, the cultivation process is simple, degradable, environmentally friendly, and can realize large-scale practical application of the product. Polylactic acid (P...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08J5/18C08J7/04C08L67/04C12P19/04C12R1/02
CPCC12P19/04C08J5/18C08L67/04C08J2301/02C08J2367/04C08J2467/04C08J7/0427Y02W90/10
Inventor 张雯余婷婷彭晓雪沈文刘艺秀李亚蕊
Owner SHAANXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap