TPE/PVAC composite fresh-keeping box cover and preparation method thereof

A composite preservation and box lid technology, applied in the field of fresh-keeping box lids, can solve the problems of lack of high-temperature resistance performance of the fresh-keeping box cover, deformation of the fresh-keeping box, and inability to seal the fresh-keeping box.

Inactive Publication Date: 2017-09-22
ANHUI YUEERWEI PLASTIC MACHINE CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the lid of the crisper is mainly made of polymer, which can basically meet the market demand, but in the process of use, it is often found that the crisper cannot be sealed immediately after filling the high-temperature food, otherwise it will cause the deformation of the crisper , it can be seen that there are still some deficiencies in the high temperature resistance of the current crisper lid

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0012] The invention provides a preparation method of a TPE / PVC composite fresh-keeping box cover, comprising:

[0013] 1) mixing soluble aluminum salt, soluble magnesium salt, soluble zirconium salt, urea and water to make a salt solution, and then performing a hydrothermal reaction to obtain a hydrothermal product;

[0014] 2) ball milling the hydrothermal product in a silane coupling agent to obtain a modified hydrothermal product;

[0015] 3) Mix TPE (thermoplastic rubber), PVCA (polyvinyl chloride vinyl acetate), bentonite, stearic acid, paraffin oil, diisononyl phthalate, silicon micropowder, modified hydrothermal product and oleic acid Refining and molding to make the TPE / PVCA composite fresh-keeping box cover.

[0016] In step 1) of the above-mentioned preparation method, the consumption of each material can be selected in a wide range, but in order to further improve the high temperature resistance of the prepared fresh-keeping box cover, preferably, in step 1), rela...

Embodiment 1

[0028] 1) Mix soluble aluminum salt (aluminum chloride), soluble magnesium salt (magnesium chloride), soluble zirconium salt (zirconium chloride), urea and water according to the dosage ratio of 1mmol: 0.6mmol: 0.2mmol: 4mmol: 8mL Salt solution, followed by hydrothermal reaction at 180°C for 16h to obtain a hydrothermal product;

[0029] 2) Ball mill the hydrothermal product and silane coupling agent (silane coupling agent Kh550) at a molar ratio of 1:0.15 (the number ratio of large balls to small balls is 2:1, and the mass ratio of grinding balls to materials is 10:2.3, the rotating speed is 900rpm, the ball milling time is 50min) to obtain the modified hydrothermal product;

[0030] 3) Mix TPE (SBS), PVCA, bentonite, stearic acid, paraffin oil, diisononyl phthalate, silicon micropowder, modified hydrothermal product and oleic acid according to the ratio of 100:75:13:29:23: The weight ratio of 28:5:6:34 was kneaded at 210°C for 5 hours, and then extruded to obtain TPE / PVCA c...

Embodiment 2

[0032] 1) Mix soluble aluminum salt (aluminum nitrate), soluble magnesium salt (magnesium nitrate), soluble zirconium salt (zirconium nitrate), urea and water according to the dosage ratio of 1mmol: 0.5mmol: 0.1mmol: 3mmol: 5mL to make salt solution, followed by a hydrothermal reaction at 170°C for 12 hours to obtain a hydrothermal product;

[0033] 2) Ball mill the hydrothermal product and silane coupling agent (silane coupling agent Kh560) at a molar ratio of 1:0.1 (the number ratio of large balls to small balls is 2:0.8, and the mass ratio of grinding balls to materials is 10:2, rotating speed is 800rpm, ball milling time is 40min) to obtain modified hydrothermal product;

[0034] 3) Mix TPE (TEO), PVCA, bentonite, stearic acid, paraffin oil, diisononyl phthalate, silicon micropowder, modified hydrothermal product and oleic acid according to the ratio of 100:70:5:25:20: The weight ratio of 22:4:4:30 was mixed at 200°C for 4 hours and extruded to obtain TPE / PVCA composite c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a TPE / PVAC composite fresh-keeping box cover and a preparation method thereof. The preparation method comprises: 1) mixing a soluble aluminum salt, a soluble magnesium salt, a soluble zirconium salt, urea and water into a salt solution, and then carrying out hydrothermal reaction to obtain a hydrothermal product; 2) subjecting the hydrothermal product to ball milling in a silane coupling agent to obtain a modified hydrothermal product; and 3) subjecting TPE (thermoplastic elastomer), PVAC (polyvinyl acetate), bentonite, stearic acid, paraffin oil, diisononyl phthalate, silica powder, the modified hydrothermal product and oleic acid to mixing, and performing molding so as to obtain the TPE / PVAC composite fresh-keeping box cover. The TPE / PVAC composite fresh-keeping box cover has excellent high-temperature resistance, and the preparation method also has the advantages of simple process and easily available raw materials.

Description

technical field [0001] The invention relates to a fresh-keeping box cover, in particular to a TPE / PVCA composite fresh-keeping box cover and a preparation method thereof. Background technique [0002] The lid of the crisper is an important component of the crisper, which not only determines the sealing performance of the crisper, but also directly affects the freshness of the crisper. At present, the lid of the crisper is mainly made of polymer, which can basically meet the market demand, but in the process of use, it is often found that the crisper cannot be sealed immediately after filling the high-temperature food, otherwise it will cause the deformation of the crisper Therefore, it can be seen that there is still a certain deficiency in the high temperature resistance of the current crisper lid. Contents of the invention [0003] The object of the present invention is to provide a TPE / PVCA composite fresh-keeping box cover and a preparation method thereof. The TPE / PVC...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L53/02C08L27/06C08L91/06C08L101/12C08K13/06C08K9/06C08K9/00C08K3/22C08K5/12C08K3/34
CPCC08L53/02C08K2003/2224C08K2003/2227C08K2003/2244C08L101/12C08L2201/08C08L2205/03C08L27/06C08L91/06C08K13/06C08K9/06C08K9/00C08K3/22C08K5/12C08K3/346
Inventor 钱万水
Owner ANHUI YUEERWEI PLASTIC MACHINE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com