New material for inner liner of fire hose and preparation method of material

A new type of material, fire hose technology, applied in building thermal insulation materials, building components, buildings, etc., can solve the problems of difficult bonding between synthetic fibers and fiber bases, expensive polyurethane rubber linings, and weather-resistant linings. , to achieve the effect of good fluidity, strong anti-aging ability and long service life

Inactive Publication Date: 2017-09-22
合肥轻风飏电气科技有限责任公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are mainly three kinds of rubber materials for the lining of fire hoses, natural rubber, ethylene-propylene rubber and polyurethane rubber. Synthetic fibers are difficult to bond with the fiber base and are more expensive, and the polyurethane rubber lining is also expensive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] This embodiment provides a new type of material for the inner lining of fire hoses. The new material for inner linings of fire hoses includes the following raw materials in parts by weight: 20-39 parts of phenolic resin, 16-31 parts of acrylic resin, light 2-7 parts of calcium carbonate, 3-11 parts of carbon nanofiber, 2-6 parts of activated clay waste residue, 5-5 parts of silicon whisker, 2-5 parts of flame retardant, 0.3-6 parts of curing agent, anti-aging agent 0.11-4 parts, binder 1-3.6 parts.

[0025] Wherein, the flame retardant is compounded by melamine melamine salt, coupling agent and char-forming accelerator, and the percentages of the above-mentioned components in the total weight of the flame retardant are: 92% of melamine melamine salt, 92% of coupling agent 3%, charring accelerator 5%.

[0026] A flame retardant is added to the formula, and the added amount of the flame retardant is now reduced by 10% compared with the prior art, which reduces the cost a...

Embodiment 2

[0039] This embodiment provides a new type of material for the inner lining of fire hoses. The new material for inner linings of fire hoses includes the following raw materials in parts by weight: 20-39 parts of phenolic resin, 16-31 parts of acrylic resin, light 2-7 parts of calcium carbonate, 3-11 parts of carbon nanofiber, 2-6 parts of activated clay waste residue, 5-5 parts of silicon whisker, 2-5 parts of flame retardant, 0.3-6 parts of curing agent, anti-aging agent 0.11-4 parts, binder 1-3.6 parts.

[0040] Wherein, the flame retardant is compounded by melamine melamine salt, coupling agent and char-forming accelerator, and the percentages of the above-mentioned components in the total weight of the flame retardant are: 93% of melamine melamine salt, 93% of coupling agent 2%, charring accelerator 5%.

[0041] A flame retardant is added to the formula, and the added amount of the flame retardant is now reduced by 10% compared with the prior art, which reduces the cost a...

Embodiment 3

[0054] This embodiment provides a new type of material for the inner lining of fire hoses. The new material for inner linings of fire hoses includes the following raw materials in parts by weight: 20-39 parts of phenolic resin, 16-31 parts of acrylic resin, light 2-7 parts of calcium carbonate, 3-11 parts of carbon nanofiber, 2-6 parts of activated clay waste residue, 5-5 parts of silicon whisker, 2-5 parts of flame retardant, 0.3-6 parts of curing agent, anti-aging agent 0.11-4 parts, binder 1-3.6 parts.

[0055] Wherein, the flame retardant is compounded by melamine melamine salt, coupling agent and char-forming accelerator, and the percentages of the above-mentioned components in the total weight of the flame retardant are: melamine melamine salt 89%, coupling agent 5%, charcoal accelerator 6%.

[0056] A flame retardant is added to the formula, and the added amount of the flame retardant is now reduced by 10% compared with the prior art, which reduces the cost and does no...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of fire-fighting equipment, and provides a new material for an inner liner of a fire hose and a preparation method of the material. The material comprises the following raw materials, by weight part, 20-39 parts of a phenolic resin, 16-31 parts of an acrylic resin, 2-7 parts of light calcium carbonate, 3-11 parts of nanometer carbon fiber, 2-6 parts of activated clay waste residue, 5-5 parts of silicon crystal whiskers, 2-5 parts of a fire retardant, 0.3-6 parts of a curing agent, 0.11-4 parts of an anti-aging agent, and 1-3.6 parts of a binder. The fire retardant, binder, and anti-aging agent are added in the formula, and inorganic and organic matters are added at the same time. The materials are prepared according to a reasonable ratio, and the inner liner has high temperature and pressure resistance, aging resistance, and long service life.

Description

technical field [0001] The invention belongs to the technical field of fire-fighting equipment, and in particular relates to a new type of material for the inner lining of a fire-fighting hose and a preparation method thereof. Background technique [0002] The fire hose is a kind of hose used to transport water or foam mixture in fire facilities. The traditional fire hose is lined with rubber and the outer surface is wrapped with flax braid. Advanced fire hoses are made of polymeric materials such as polyurethane. The fire hose uses high-strength synthetic fibers as the base layer, and there is a layer of lining inside. Because the lining is a structural layer that directly contacts the water or foam mixture used for fire extinguishing, the material of the lining directly determines the use of the fire hose. performance. At present, there are mainly three types of rubber materials for the inner lining of fire hoses, natural rubber, ethylene-propylene rubber and polyurethan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L61/06C08L33/00C08L91/00C08L23/06C08L95/00C08L23/12C08L23/16C08L25/06C08K13/04C08K7/06C08K3/26C08K5/3492C08K3/36C08K3/22C08K3/34C08K5/42
CPCC08L61/06C08K2003/2227C08K2003/2241C08K2003/265C08K2201/011C08K2201/014C08L33/00C08L2201/02C08L2201/08C08L2205/025C08L2205/035C08L2205/16C08L91/00C08L23/06C08L95/00C08L23/12C08L23/0815C08L25/06C08K13/04C08K7/06C08K3/26C08K5/34928C08K3/36C08K3/22C08K3/34C08K5/42
Inventor 张玉成
Owner 合肥轻风飏电气科技有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products