Waterproof plastering gypsum and preparation method thereof

A plaster plaster and waterproof technology, which is applied in the field of plaster plaster, can solve the problems of easy moisture shedding, poor water release ability, etc., achieve the best physical properties, improve adhesion, and prolong the effect of setting time

Inactive Publication Date: 2017-10-03
HEFEI GUANGMIN BUILDING MATERIAL CO LTD
View PDF3 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current plaster plaster has poor water release ability and is easy to fall off due to moisture.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A kind of waterproof plaster plaster of the present embodiment, comprises the raw material of following weight part:

[0027] 60 parts of desulfurized gypsum, 25 parts of silica sand, 14 parts of heavy calcium carbonate, 13 parts of cement, 8 parts of polytrimethylene terephthalate fiber, 10 parts of ceramic fiber, 7 parts of modified magnesium hydroxide, 6 parts of diatomite , 5 parts of starch, 1 part of hydroxypropyl methylcellulose, 3 parts of silicone water repellent, 1 part of retarder, 2 parts of antibacterial agent, 14 parts of acrylic emulsion, and 5 parts of water.

[0028] In this embodiment, the length of the polytrimethylene terephthalate fiber and the ceramic fiber is 0.2 mm, and the diameter is 0.08 mm.

[0029] In this example, the modified magnesium hydroxide is obtained by the following method: bake the magnesium hydroxide at 100°C for 3 hours, add distilled water to the magnesium hydroxide powder, keep the mass fraction of the magnesium hydroxide slur...

Embodiment 2

[0040] A kind of waterproof plaster plaster of the present embodiment, comprises the raw material of following weight part:

[0041] 65 parts of desulfurized gypsum, 28 parts of silica sand, 16 parts of heavy calcium carbonate, 14 parts of cement, 9 parts of polytrimethylene terephthalate fiber, 11 parts of ceramic fiber, 8 parts of modified magnesium hydroxide, 7 parts of diatomaceous earth , 6 parts of starch, 2 parts of hydroxypropyl methylcellulose, 4 parts of silicone water repellent, 1.5 parts of retarder, 3 parts of antibacterial agent, 15 parts of acrylic emulsion, and 10 parts of water.

[0042] In this embodiment, the length of the polytrimethylene terephthalate fiber and the ceramic fiber is 0.3 mm, and the diameter is 0.09 mm.

[0043] In this example, the modified magnesium hydroxide is obtained by the following method: bake the magnesium hydroxide at 100°C for 3 hours, add distilled water to the magnesium hydroxide powder, keep the mass fraction of the magnesium ...

Embodiment 3

[0054] A kind of waterproof plaster plaster of the present embodiment, comprises the raw material of following weight portion:

[0055] 70 parts of desulfurized gypsum, 30 parts of silica sand, 18 parts of heavy calcium carbonate, 15 parts of cement, 10 parts of polytrimethylene terephthalate fiber, 12 parts of ceramic fiber, 9 parts of modified magnesium hydroxide, 8 parts of diatomaceous earth , 7 parts of starch, 3 parts of hydroxypropyl methylcellulose, 5 parts of silicone water repellent, 2 parts of retarder, 4 parts of antibacterial agent, 16 parts of acrylic emulsion, and 15 parts of water.

[0056] In this embodiment, the length of the polytrimethylene terephthalate fiber and the ceramic fiber is 0.4 mm, and the diameter is 0.1 mm.

[0057] In this example, the modified magnesium hydroxide is obtained by the following method: bake the magnesium hydroxide at 100°C for 3 hours, add distilled water to the magnesium hydroxide powder, keep the mass fraction of the magnesium...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a waterproof plastering gypsum, and belongs to the technical field of plastering gypsums. The plastering gypsum comprises the following raw materials in parts by weight: 60-70 parts of desulphurization gypsum, 25-30 parts of silica sand, 14-18 parts of calcium carbonate, 13-15 parts of cement, 8-10 parts of polytrimethylene terephthalate fiber, 10-12 parts of ceramic fiber, 7-9 parts of modified magnesium hydroxide, 6-8 parts of kieselguhr, 5-7 parts of starch, 1-3 parts of hydroxy propyl methyl cellulose, 3-5 parts of an organosilicone water repellent, 1-2 parts of a retarder, 2-4 parts of an antibacterial agent, 14-16 parts of an acrylic emulsion and 5-15 parts of water. The invention further discloses a preparation method of the waterproof plastering gypsum, the preparation is simple, and the waterproof plastering gypsum has excellent waterproof, fireproof and high temperature resistant capabilities after being solidified.

Description

technical field [0001] The invention relates to the technical field of plaster plaster, in particular to a waterproof plaster plaster and a preparation method thereof. Background technique [0002] Gypsum plaster is an ancient building material and belongs to one of the three traditional inorganic cementitious materials. my country has a long history of using gypsum cementitious materials, but the scope of application is limited. With the improvement of living standards, people's awareness and requirements for building materials such as energy saving, safety and non-toxicity have increased, and gypsum materials have a series of technical advantages. , making it an energy-saving green material that is respected internationally. The gypsum plastering layer hardens quickly, and the surface layer can be constructed within 1h-2h after the bottom layer is completed, which greatly shortens the construction period. After construction, no maintenance is required, which is conducive t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14
CPCC04B28/144C04B2111/20C04B2111/2092C04B2111/27C04B2111/28C04B2111/763C04B14/06C04B14/28C04B7/02C04B16/0683C04B14/46C04B14/08C04B22/066C04B24/38C04B24/383C04B24/42C04B2103/67C04B2103/22C04B24/26
Inventor 黄洋
Owner HEFEI GUANGMIN BUILDING MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com