Novel heat insulation material and preparation method thereof

A thermal insulation material and a new type of technology, applied in the field of new thermal insulation materials and their preparation, can solve the problems of not very long use time, accompanied by thunderstorms, and high cost of thermal insulation materials, and achieve extended service life, good insulation effect, and improved insulation. The effect of thermal insulation

Inactive Publication Date: 2017-11-03
伊婕
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The serious trend of global warming has made insulation materials more and more popular among people. Whether it is construction or decoration, a large number of insulation materials are used for heat insulation, especially in summer, when there are thunderstorms after exposure to the sun. The requirements for thermal materials are very high, not only must have a good heat insulation effect, but also have water resistance. At present, there are many heat insulation materials, but the special high-quality heat insulation materials are not only expensive, but also have a short service life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A new type of heat insulation material and its preparation method. The composition of the raw materials is composed of the following proportions in parts by weight: 35 parts of seaweed mud, 15 parts of plant fiber, 15 parts of nano-ceramic hollow microspheres, 10 parts of vitrified microbead thermal insulation mortar, 3 parts of redispersible latex powder, 10 parts of seaweed powder, 8 parts of putty rubber powder, 3 parts of talcum powder, 5 parts of pregelatinized starch, 10 parts of nano silicon, 10 parts of polyvinyl alcohol, 30 parts of deionized water, ceramic powder 35 servings.

[0015] Its preparation method is as follows:

[0016] A. Put seaweed mud, plant fiber and vitrified microbead thermal insulation mortar into a pulverizer for crushing, use a 4mm sieve to sieve, add deionized water to the sieved mixture and mix to obtain mixture A, stirring speed 850r / min;

[0017] B. Stir the redispersible latex powder, putty rubber powder, talcum powder and pregelati...

Embodiment 2

[0021] A new type of heat insulation material and its preparation method. The composition of raw materials is composed of the following proportions in parts by weight: 30 parts of seaweed mud, 10 parts of plant fiber, 12 parts of nano-ceramic hollow microspheres, 6 parts of vitrified microsphere insulation mortar, 8 parts of redispersible latex powder, 10 parts of seaweed powder, 9 parts of putty rubber powder, 5 parts of talcum powder, 4 parts of pregelatinized starch, 7 parts of nano-silicon, 10 parts of polyvinyl alcohol, 50 parts of deionized water, ceramic powder 35 servings.

[0022] Its preparation method is as follows:

[0023] A. Put seaweed mud, plant fiber and vitrified microbead thermal insulation mortar into a pulverizer for crushing, use a 3mm sieve to sieve, add deionized water to the sieved mixture and mix to obtain mixture A, stirring speed 900r / min;

[0024] B. Stir the redispersible latex powder, putty rubber powder, talcum powder and pregelatinized starch...

Embodiment 3

[0028] A new type of heat insulation material and its preparation method. The composition of raw materials is composed of the following proportions in parts by weight: 30 parts of seaweed mud, 10 parts of plant fiber, 15 parts of nano-ceramic hollow microspheres, 10 parts of vitrified microsphere insulation mortar, 3 parts of redispersible latex powder, 6 parts of seaweed powder, 5 parts of putty rubber powder, 4 parts of talcum powder, 3 parts of pregelatinized starch, 5 parts of nano silicon, 7 parts of polyvinyl alcohol, 25 parts of deionized water, ceramic powder 30 servings.

[0029] Its preparation method is as follows:

[0030] A. Put the seaweed mud, plant fiber and vitrified microbead thermal insulation mortar into the pulverizer for crushing, use a 5mm sieve for sieving, add deionized water to the sieved mixture and mix to obtain mixture A, stirring speed 800r / min;

[0031] B. Stir the redispersible latex powder, putty rubber powder, talcum powder and pregelatinize...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a novel heat insulation material and a preparation method thereof. The raw material components are composed of the following proportions in parts by weight: 30-50 parts of seaweed mud, 10-20 parts of plant fiber, 5-15 parts of nano-ceramic hollow microspheres, 5‑10 parts of vitrified bead insulation mortar, 3‑8 parts of redispersible latex powder, 6‑10 parts of seaweed powder, 5‑9 parts of putty rubber powder, 3‑5 parts of talcum powder, 3‑5 parts of pregelatinized starch 5-10 parts of nano silicon, 6-10 parts of polyvinyl alcohol, 20-50 parts of deionized water, 30-35 parts of ceramic powder. The material of the present invention is easy to obtain, the preparation method is simple, the maximum can withstand -50-180 °C, the insulation effect is good, and the wear resistance is strong. By electroplating ceramic powder, not only the hardness of the surface is improved, but also the absorption of sunlight can be prevented, and the heat insulation can be improved. Effect, the internal structure has high viscosity and tight combination, and it is not easy to burst and peel after exposure to the sun. The surface is smooth, healthy and environmentally friendly, reducing water absorption, low cost, and high comprehensive economic benefits.

Description

technical field [0001] The invention relates to a novel heat insulating material and a preparation method thereof. Background technique [0002] The serious trend of global warming has made insulation materials more and more popular among people. Whether it is construction or decoration, a large number of insulation materials are used for heat insulation, especially in summer, when there are thunderstorms after exposure to the sun. The requirements for thermal materials are very high. Not only must they have good heat insulation effect, but also have water resistance. At present, there are many heat insulation materials, but the special high-quality heat insulation materials are not only expensive, but also have a short service life. Invention content: [0003] The object of the present invention is to provide a novel heat insulating material and a preparation method thereof in order to overcome the above disadvantages. [0004] The technical scheme of the present inventi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/28
CPCC04B26/28
Inventor 伊婕
Owner 伊婕
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap