Early strength concrete for power line mounting and preparation method of early strength concrete

A technology for power lines and installation, which is applied in the field of early-strength concrete for power line installation and its preparation, can solve the problems of short curing time, inconspicuous high-temperature resistance, and high early-strength of super-early-strength concrete, so as to improve the antifreeze ability, The effect of short curing time and high early strength

Inactive Publication Date: 2017-11-07
HEFEI ANLI ELECTRIC POWER ENG CO LTD
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The super early strength concrete prepared by the method described in the invention has the advantages of short curing time and high early strength; but the high temperature resistance of the invention is not obvious

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of early-strength concrete for power line installation of the present embodiment comprises the following raw materials in parts by weight:

[0028] 80 parts of sulfoaluminate cement, 45 parts of steel fiber, 30 parts of glass fiber, 22 parts of ceramic hollow microspheres, 14 parts of cast stone powder, 20 parts of quartz powder, 250 parts of aggregate, 8 parts of zinc oxide, 3 parts of molybdenum disulfide , 1 part of triisopropanolamine, 1 part of lithium carbonate, 2 parts of aluminum sulfate, 0.5 parts of sodium hydroxide, 7 parts of water reducing agent, 1 part of defoamer, 2 parts of antifreeze, 30 parts of water.

[0029] In this embodiment, the steel fibers and glass fibers have a length of 0.4 mm and a diameter of 0.1 mm; the particle diameter of the ceramic hollow microspheres is 0.3 mm.

[0030] In this embodiment, the aggregate includes stones and sand, the sand rate of the aggregate is 35%, the particle size of the stone is 5 mm, the sand is natural ...

Embodiment 2

[0042] A kind of early-strength concrete for power line installation of the present embodiment comprises the following raw materials in parts by weight:

[0043] 90 parts of sulfoaluminate cement, 48 parts of steel fiber, 35 parts of glass fiber, 24 parts of ceramic hollow microspheres, 15 parts of cast stone powder, 23 parts of quartz powder, 260 parts of aggregate, 9 parts of zinc oxide, 5 parts of molybdenum disulfide , 2 parts of triisopropanolamine, 1.5 parts of lithium carbonate, 3 parts of aluminum sulfate, 0.8 parts of sodium hydroxide, 8 parts of water reducer, 1.5 parts of defoamer, 3 parts of antifreeze, 40 parts of water.

[0044] In this embodiment, the steel fibers and glass fibers have a length of 0.5 mm and a diameter of 0.2 mm; the particle diameter of the ceramic hollow microspheres is 0.4 mm.

[0045] In this embodiment, the aggregate includes stones and sand, the sand rate of the aggregate is 40%, the particle size of the stone is 15mm, the sand is natural ...

Embodiment 3

[0057] A kind of early-strength concrete for power line installation of the present embodiment comprises the following raw materials in parts by weight:

[0058] 100 parts of sulphoaluminate cement, 50 parts of steel fiber, 40 parts of glass fiber, 25 parts of ceramic hollow microspheres, 16 parts of cast stone powder, 25 parts of quartz powder, 270 parts of aggregate, 10 parts of zinc oxide, 7 parts of molybdenum disulfide , 3 parts of triisopropanolamine, 2 parts of lithium carbonate, 4 parts of aluminum sulfate, 1 part of sodium hydroxide, 9 parts of water reducer, 2 parts of defoamer, 4 parts of antifreeze, and 50 parts of water.

[0059] In this embodiment, the steel fibers and glass fibers have a length of 0.6 mm and a diameter of 0.3 mm; the particle diameter of the ceramic hollow microspheres is 0.5 mm.

[0060] In this embodiment, the aggregate includes stones and sand, the sand rate of the aggregate is 45%, the particle size of the stone is 25 mm, the sand is natural...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses early strength concrete for power line mounting, and belongs to the technical field of concrete. The early strength concrete comprises the following raw materials in parts by weight: 80-100 parts of sulfate aluminium cement, 45-50 parts of steel fiber, 30-40 parts of glass fiber, 22-25 parts of ceramic hollow beads, 14-16 parts of glass-ceramic powder, 20-25 parts of quartz powder, 250-270 parts of aggregate, 8-10 parts of zinc oxide, 3-7 parts of molybdenum disulfide, 1-3 parts of triisopropanolamine, 1-2 parts of lithium carbonate, 2-4 parts of aluminum sulfate, 0.5-1 part of sodium hydroxide, 7-9 parts of a water reducing agent, 1-2 parts of a defoaming agent, 2-4 parts of an anti-freezing agent and 30-50 parts of water. The invention further discloses a preparation method of the early strength concrete for power line mounting. The early strength concrete is relatively good in early strength, excellent in high temperature resistance, excellent in anti-freezing property and short in maintenance time.

Description

technical field [0001] The invention relates to the technical field of concrete, in particular to an early-strength concrete for installing power lines and a preparation method thereof. Background technique [0002] At present, in order to solve the problems of low early strength and long curing time of cast-in-place concrete in the foundation construction process, people usually use high-strength Portland cement concrete instead of ordinary-strength Portland cement concrete or use high-strength silicate Salt cement concrete is used to replace ordinary strength Portland cement concrete and at the same time, early strength agent is added to improve early strength. [0003] By using high-strength Portland cement concrete instead of ordinary-strength Portland cement concrete, the early strength of high-strength concrete is higher than that of ordinary-strength concrete. The disadvantage of this method is that the later strength is too high, and its strength is not fully utilize...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/06C04B111/20
CPCC04B28/065C04B2111/29C04B2201/05C04B2201/52C04B14/02C04B14/068C04B14/48C04B14/42C04B18/027C04B14/04C04B14/06C04B14/30C04B14/36C04B24/122C04B22/10C04B22/148C04B22/062C04B24/18C04B24/226C04B24/223C04B24/166C04B24/42C04B24/08C04B24/32C04B24/04C04B24/126C04B24/02C04B24/124C04B24/128C04B24/003
Inventor 殷世尧
Owner HEFEI ANLI ELECTRIC POWER ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com