Low-separation bonding shining silver powder coating and preparation method thereof

A technology of silver powder and coating, applied in the field of low-separation bonding flash silver powder coating and its preparation, can solve the problems of easy separation, low adhesion rate, affecting the aesthetics of the coated object, etc., to eliminate pinholes and improve the surface Tension, effect of excellent mechanical properties

Inactive Publication Date: 2017-11-10
浙江绿能塑粉科技股份有限公司
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the above-mentioned deficiencies in the prior art, provide a kind of low-separation bonding glitter silver powder coating and preparation method thereof, it aims at solving the low binding rate of the metal pigment in the metal powder coating in the prior art , easy to separate, technical problems that affect the aesthetics of the coated object

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A low-separation bonding flash silver powder coating, its raw materials include the following components in parts by weight: 30 parts of epoxy resin; 30 parts of carboxyl-terminated polyester resin; 12.5 parts of hydroxyl polyester resin; 2 parts of polyacrylate; 1.2 parts of silane coupling agent; 12.5 parts of barium sulfate; 7.5 parts of light calcium carbonate; 1.5 parts of titanium dioxide; 3.5 parts of surface-coated aluminum powder;

[0029] S1. Weighing ingredients: Weigh epoxy resin, carboxyl-terminated polyester resin, hydroxyl polyester resin, polyacrylate, benzoin, silane coupling agent, barium sulfate, light calcium carbonate and titanium dioxide in parts by weight .

[0030] S2. Pre-mixing: Put the weighed raw materials into a high-speed mixer and mix them evenly. The temperature in the high-speed mixer is set at 50-60°C.

[0031] S3. Melt extrusion: put the mixed and stirred raw materials into a screw extruder to melt and homogenize, and extrude and tabl...

Embodiment 2

[0038] A low-separation bonding flash silver powder coating, its raw materials include the following components in parts by weight: 25 parts of epoxy resin; 25 parts of carboxyl-terminated polyester resin; 10 parts of hydroxyl polyester resin; 1 part of polyacrylate; 0.3 part of algae; 1 part of silane coupling agent; 10 parts of barium sulfate; 5 parts of light calcium carbonate; 1 part of surface-coated aluminum powder;

Embodiment 3

[0040] A low-separation bonding flash silver powder coating, its raw materials include the following components in parts by weight: 35 parts of epoxy resin; 35 parts of carboxyl-terminated polyester resin; 15 parts of hydroxyl polyester resin; 3 parts of polyacrylate; 0.5 part of algae; 1.5 parts of silane coupling agent; 15 parts of barium sulfate; 10 parts of light calcium carbonate; 3 parts of titanium dioxide; 6 parts of surface-coated aluminum powder; .

[0041]The invention discloses a low-separation bonding flash silver powder coating and a preparation method thereof, which adopt epoxy resin, carboxyl-terminated polyester resin, and hydroxyl polyester resin, have high reactivity, high bonding strength, and excellent mechanical properties; polyacrylic acid Esters and benzoin melt each other, strengthen and improve the surface tension of the coating film, adjust the surface leveling of the coating film, not only eliminate pinholes and shrinkage holes caused by raw and aux...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
Login to View More

Abstract

The invention discloses a low-separation bonding shining silver powder coating. The low-separation bonding shining silver powder coating is prepared from, by weight, 25-35 parts of epoxy resin, 25-35 parts of carboxyl-terminated polyester resin, 10-15 parts of hydroxyl polyester resin, 1-3 parts of polyacrylate, 0.3-0.5 part of benzoin, 1-1.5 parts of silane coupling agent, 10-15 parts of barium sulfate, 5-10 parts of light calcium carbonate, 0-3 parts of titanium dioxide, 1-6 parts of surface-coated aluminum powder and 1-2 parts of bonding additive. The invention further provides a preparation method of the low-separation bonding shining silver powder coating. Through ingredient weighing, premixing, melting extrusion, grinding, screening, bonding, screening and finished product packaging, the low-separation bonding shining silver powder coating is obtained; through adjustment of the melting viscosity, glass transition temperature, bonding temperature and bonding time of the powder, the powder fully bonds with particles of the aluminum powder, so that the bonding rate reaches 98-100%, the separation rate of the aluminum powder is reduced, and the service life of coating film is prolonged.

Description

【Technical field】 [0001] The invention relates to the technical field of powder coatings, in particular to a low-separation bonding flash silver powder coating and a preparation method thereof. 【Background technique】 [0002] Powder coating exists in the state of fine powder. It is a new type of solvent-free 100% solid powder coating. It is solvent-free, pollution-free, recyclable, environmentally friendly, saves energy and resources, reduces labor intensity and mechanical strength of the coating film. advanced features. The powder coating is sprayed on the surface of the coated object in powder form, melted and leveled by baking, and solidified to form a film. Due to the advantages of improving coating performance, reducing costs, and eliminating the generation of volatile organic compounds, powder coatings have been continuously and rapidly developed. [0003] Metal powder coatings refer to various powder coatings containing metal pigments (such as: copper-gold powder, s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D167/00C09D7/12C09D5/03
CPCC09D163/00C08K2003/0812C08K2003/2241C08K2003/265C08K2003/3045C08L2205/025C08L2205/035C09D5/033C09D167/00C08L67/00C08L33/04C08K13/06C08K9/10C08K3/08C08K5/07C08K3/26C08K3/22C08K3/30C08L63/00
Inventor 范若谷周光阳徐锦丽江红兵丁武轩周天明徐能峰张爱华杨建芬
Owner 浙江绿能塑粉科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products