A technology with high content and quartz, which is applied in the field of green porcelain glaze, can solve the problems of no high transparency and high gloss, and achieve the effect of uniform glaze layer, good gloss and low cost

Active Publication Date: 2020-08-18
马聚魁
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Chai porcelain is a kiln mouth named after Shizong Chai Rong's surname during the Five Dynasties. It is a famous porcelain kiln in history and is revered as the crown of all kilns. Mirror, thin as paper, and sound like a chime", it is infinitely yearning. The existing light-colored glazes are mainly high-temperature colored glazes produced in Jingdezhen, while there are almost no high-transparency, high-moisture, and high-gloss glazes in medium-temperature colored glazes. visual effect; therefore, it is very necessary to provide a firewood green glaze with medium temperature, fast firing, low cost, uniform glaze layer and good gloss.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Chai Porcelain Bicui Glaze is made of the following components by weight: 21.26 parts of quartz, 33.11 parts of feldspar, 12.35 parts of calcite, 20.85 parts of green ash, 3.58 parts of phosphorus bone powder, 3.60 parts of agate stone, and sapphire stone 2.25 copies, 3.00 copies of Wujin soil.

[0017] The quartz is quartz sand.

[0018] The feldspar is albite.

[0019] The content of iron oxide in the black gold soil is 30%-32%, and the content of manganese oxide is 8%-9%.

[0020] The preparation method of Chai Porcelain Beicui glaze includes the following steps:

[0021] a. Make ingredients according to the mass ratio of each component and each component;

[0022] b. Mix the components evenly, add 20-22 parts of water, wet ball milling for 16-18 hours, the glaze after ball milling passes through a 250-mesh sieve, and then adjust to a glaze slurry of 60-65 Baume degree , and then spray the glaze slurry on the incense ash body, then heat it up at room temperature ...

Embodiment 2

[0027] Chai Porcelain Bicui Glaze is made of the following components by weight: 21.26 parts of quartz, 33.11 parts of feldspar, 12.35 parts of calcite, 20.85 parts of green ash, 3.58 parts of phosphorus bone powder, 3.60 parts of agate stone, and sapphire stone 2.25 copies, 3.00 copies of Wujin soil.

[0028] The quartz is quartz sand.

[0029] The feldspar is potassium feldspar.

[0030] The content of iron oxide in the black gold soil is 30%-35%, and the content of manganese oxide is 8%-10%.

[0031] The preparation method of Chai Porcelain Beicui glaze includes the following steps:

[0032] a. Make ingredients according to the mass ratio of each component and each component;

[0033] b. Mix the components evenly, add 20-22 parts of water, wet ball milling for 18-20 hours, the glaze after ball milling passes through a 250-mesh sieve, and then adjust to a glaze slurry of 60-65 Baume degree , and then spray the glaze slurry on the incense ash body, then heat it up at room...

Embodiment 3

[0038] Chai Porcelain Bicui Glaze is made of the following components by weight: 21.26 parts of quartz, 33.11 parts of feldspar, 12.35 parts of calcite, 20.85 parts of green ash, 3.58 parts of phosphorus bone powder, 3.60 parts of agate stone, and sapphire stone 2.25 copies, 3.00 copies of Wujin soil.

[0039] The quartz is quartz sand.

[0040] The feldspar is a combination of albite and potassium feldspar.

[0041] The content of iron oxide in the black gold soil is 32%-35%, and the content of manganese oxide is 9%-10%.

[0042] The preparation method of Chai Porcelain Beicui glaze includes the following steps:

[0043] a. Make ingredients according to the mass ratio of each component and each component;

[0044] b. Mix the components evenly, add 20-22 parts of water, wet ball milling for 18-20 hours, the glaze after ball milling passes through a 250-mesh sieve, and then adjust to a glaze slurry of 60-65 Baume degree , and then spray the glaze slurry on the incense ash b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to green glaze for wood-fired porcelains. The green glaze is prepared by the following components in parts by weight: 21.26 parts of quartz, 33.11 parts of feldspar, 12.35 parts of calcite, 20.85 parts of graphite, 3.58 parts of phosphorus bone powder, 3.60 parts of agate, 2.25 parts of water bone stone and 3.00 parts of black golden earth, wherein the quartz is quartz sand, the feldspar is one or combination of sodium feldspar and potassium feldspar, the content of ferric oxide in the black golden earth is 30%-35%, and the content of manganese oxide in the black golden earth is 8%-10%. A preparation method of the green glaze for the wood-fired porcelains comprises the following steps: (a) carrying out batching according to all the components and the mass proportion thereof; (b) mixing all the components uniformly, adding 20-22 parts of water, carrying out wet-process ball grinding for 16-20 hours, filtering the ball-ground glaze by a sieve of 250 meshes, mixing into glaze slip with baume degrees of 60-65, then spraying the glaze slip onto incense ash base, rising temperature from normal temperature to 1180-1250 DEG C, cooling, drawing out of a kiln and standing for about 15 hours. The green glaze has the advantages of fast firing at a medium temperature, lower cost, uniform and clean glaze layer, good glossiness and strong decorative conception.

Description

technical field [0001] The invention belongs to the technical field of ceramics, and in particular relates to a jade porcelain jade glaze. Background technique [0002] Chai Porcelain is a kiln named after the surname of Sejong Chai Rong during the Five Dynasties. It is a famous porcelain kiln in history and is respected as the crown of all kilns. "Mirror, thin as paper, sound like a chime", people yearn for infinitely. The existing light-colored glazes are mainly high-temperature color glazes produced in Jingdezhen. Among the medium-temperature color materials, there are almost no high-transparency, high-moisture, and high-gloss glazes. Therefore, it is very necessary to provide a kind of Chai Porcelain Bicui glaze with fast firing at medium temperature, low cost, uniform glaze layer and good gloss. SUMMARY OF THE INVENTION [0003] The purpose of the present invention is to overcome the deficiencies of the prior art, and provide a kind of Chai Porcelain Bi-Cui glaze wit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/14
CPCC03C8/14
Inventor 马聚魁马得原马铭
Owner 马聚魁
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap