Waterproof mildew-proof inner wall powder paint and the production process thereof

A powder coating, waterproof and mildew-proof technology, which is applied in the field of building materials, can solve the problems of simple functions and narrow uses, and achieve the effects of reducing weight, reducing heat loss, and improving heat storage and heat preservation capabilities

Inactive Publication Date: 2017-11-24
HEFEI GUANGMIN BUILDING MATERIAL CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the existing interior wall powder coatings, mos

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A waterproof and mildew-proof interior wall powder coating, comprising the following raw materials: 75g of diatomite, 82g of fly ash, 25g of montmorillonite, 26g of talcum powder, 14g of aluminum hydroxide powder, 7g of bamboo charcoal fiber, and 3g of antimony trioxide , sodium hypochlorite 1.3g, nano-zinc oxide 2g, Cathone 0.3g, dispersant sodium polyphosphate 0.2g, wetting agent Dynol 980 0.5g, defoamer polydimethylsiloxane 0.1g.

[0024] The production process of the above-mentioned waterproof and mildew-proof interior wall powder coating comprises the following steps:

[0025] (1) After natural drying, weathering and crushing of diatomite, soak in deionized water for 35 minutes, centrifuge for 8 minutes, filter with 20-40 mesh filter cloth, and dry the filtrate at 55°C for 7 hours to obtain purified silicon Algal earth, keep the moisture content below 5%;

[0026] (2) Mix the purified diatomite, talc powder, aluminum hydroxide powder, bamboo charcoal fiber, and an...

Embodiment 2

[0029] A waterproof and mildew-proof interior wall powder coating, comprising the following raw materials: 66g of diatomite, 78g of fly ash, 20g of montmorillonite, 22g of talcum powder, 12g of aluminum hydroxide powder, 7g of bamboo charcoal fiber, and 3g of antimony trioxide , Sodium hypochlorite 1.5g, Nano-zinc oxide 1g, Cathone 0.5g, Dispersant sodium polyphosphate 0.3g, Wetting agent Dynol 960 0.6g, Defoamer polyoxypropylene glyceryl ether 0.1g.

[0030] The production process of the above-mentioned waterproof and mildew-proof interior wall powder coating comprises the following steps:

[0031] (1) Naturally dry, weather and pulverize diatomite, soak in deionized water for 30 minutes, centrifuge for 10 minutes, filter with 20-40 mesh filter cloth, and dry the filtrate at 60°C for 6 hours to obtain purified silica Algal earth, keep the moisture content below 5%;

[0032] (2) Mix the purified diatomaceous earth, talcum powder, aluminum hydroxide powder, bamboo charcoal fib...

Embodiment 3

[0035] A waterproof and mildew-proof interior wall powder coating, comprising the following raw materials: 74g of diatomite, 86g of fly ash, 23g of montmorillonite, 26g of talcum powder, 15g of aluminum hydroxide powder, 5g of bamboo charcoal fiber, and 3g of antimony trioxide , sodium hypochlorite 0.9g, nano-zinc oxide 2g, Cathone 0.3g, dispersant sodium polyphosphate 0.2g, wetting agent Dynol 980 0.5g, defoamer polydimethylsiloxane 0.3g.

[0036] The production process of the above-mentioned waterproof and mildew-proof interior wall powder coating comprises the following steps:

[0037] (1) Naturally dry, weather and pulverize diatomite, soak in deionized water for 40 minutes, centrifuge for 10 minutes, filter with 20-40 mesh filter cloth, and dry the filtrate at 50°C for 8 hours to obtain purified silica Algal earth, keep the moisture content below 5%;

[0038] (2) Mix the purified diatomite, talcum powder, aluminum hydroxide powder, bamboo charcoal fiber, and antimony tri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses waterproof mildew-proof inner wall powder paint and a production process thereof. The powder paint comprises the following raw materials in parts by weight: 60 to 80 parts of diatomaceous earth, 70 to 90 parts of fly ash, 20 to 30 parts of talc, 15 to 30 parts of montmorillonite, 8 to 20 parts of aluminum hydroxide powder, 5 to 10 parts of bamboo charcoal fiber, 1 to 5 parts of antimony trioxide, 0.6 to 2 parts of sodium hypochlorite, 1 to 3 parts of nano-zinc oxide, 0.2 to 0.6 part of Kathon, 0.1 to 0.5 part of a dispersant, 0.2 to 0.8 part of a wetting agent and 0.1 to 0.3 part of a defoaming agent. The production process includes diatomaceous earth purification and mixed ball milling. The waterproof mildew-proof inner wall powder paint has the advantages of safety, environmental friendliness, bacteria resistance and bacteriostasis, water proofness, mildew proofness, good fire-proofing performance and simple production process and is suitable as inner wall powder paint.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a waterproof and mildewproof interior wall powder coating and a production process thereof. Background technique [0002] Today, low-carbon environmental protection, energy conservation and emission reduction are the basic principles for the sustainable economic development of various countries in the world. With the development of society and the improvement of living standards, people's awareness of environmental protection and health has been significantly enhanced, and the requirements for the comfort and safety of the living environment are getting higher and higher. Indoor temperature, air relative humidity, and air quality are important environmental parameters for living comfort. When the indoor temperature is 20-23°C, the relative humidity is 50-60%, the VOC content is low, and the negative ion content is high, the human body feels comfortable and beneficial ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00C04B111/20C04B111/27C04B111/28C04B111/52
CPCC04B28/001C04B2111/00482C04B2111/20C04B2111/27C04B2111/28C04B2111/52C04B14/08C04B18/08C04B22/06C04B18/248C04B14/042C04B14/30C04B22/124C04B24/005C04B24/008C04B22/16C04B24/42C04B2103/0068
Inventor 黄洋
Owner HEFEI GUANGMIN BUILDING MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap