High-ductility cement-based composite material for repairing hydraulic concrete structure

A technology of hydraulic concrete and composite materials, applied in the field of building materials, can solve the problems of insufficient durability and weak synergy, and achieve the effects of excellent durability, efficient and uniform dispersion, and improved bending deformation resistance and earthquake resistance.

Active Publication Date: 2017-12-08
NANJING HYDRAULIC RES INST
View PDF3 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the problems of insufficient durability of traditional repair materials under severe service conditions and weak synergy with existing structures, the present invention provides a hydraulic concrete structure repair with high durability, high bonding capacity and high deformation capacity high ductility cementitious composites

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The material composition ratio is shown in Table 1:

[0035] Table 1 Mixing ratio of high ductility cement-based composite materials for repairing hydraulic concrete structures (mass parts)

[0036] cement

fly ash

slag

light calcium powder

nano-SiO 2

fine aggregate

water

Superplasticizer

polyvinyl alcohol fiber

20

20

60

5

1

25

40

0.1

0.5

[0037] The cement is P·O 42.5 ordinary Portland cement of Nanjing Conch Cement Co., Ltd.; the fly ash is Class I F fly ash of Nanjing Thermal Power Plant; the finely ground slag is S75 grade slag of Maanshan Iron and Steel Co., Ltd.; Chenyang Yuhuashi Filter Material Co., Ltd.’s finely ground quartz sand has a maximum particle size of 1.18mm; light calcium powder is produced by Zibo Longchang Fine Chemical Factory, with an average particle size of 20μm; nano-SiO 2 Produced by Beijing Deke Daojin Technology Co., Ltd., active SiO 2 The content is 95%, and th...

Embodiment 2

[0040] The material composition ratio is shown in Table 2:

[0041] Table 2 Mixing ratio of high ductility cement-based composite materials for hydraulic concrete structure repair (mass parts)

[0042] cement

fly ash

slag

light calcium powder

nano-SiO 2

fine aggregate

water

Superplasticizer

polyvinyl alcohol fiber

60

20

20

10

5

40

20

1

2.5

[0043]The cement is R·SAC 42.5 sulfoaluminate cement from Nanjing Conch Cement Co., Ltd.; the fly ash is Class II F fly ash of Nanjing Thermal Power Plant; the finely ground slag is S95 class slag from Maanshan Iron and Steel Co., Ltd.; the fine aggregate is Nanjing local Natural river sand with a maximum particle size of 5mm; light calcium powder produced by Zibo Longchang Fine Chemical Factory with an average particle size of 45μm; nano-SiO 2 Produced by Beijing Deke Daojin Technology Co., Ltd., active SiO 2 The content is 95%, and the volume average diameter...

Embodiment 3

[0046] The material composition ratio is shown in Table 3:

[0047] Table 3 Mixing ratio of high ductility cement-based composite materials for hydraulic concrete structure repair (mass parts)

[0048] cement

fly ash

slag

light calcium powder

nano-SiO 2

fine aggregate

water

Superplasticizer

polyvinyl alcohol fiber

20

80

0

7.5

2.5

35

30

0.75

2

[0049] The cement is P·MH 42.5 medium-heat cement from Jiahua Special Cement Co., Ltd.; the fly ash is Class I F fly ash of Nanjing Thermal Power Plant; the fine aggregate is artificial sand produced in Nanjing Liuhe, with a maximum particle size of 2.5mm; The powder is produced by Zibo Longchang Fine Chemical Factory, with an average particle size of 35 μm; nano-SiO 2 Produced by Beijing Deke Daojin Technology Co., Ltd., active SiO 2 The content is 97%, and the average volume diameter D(4,3) is 85nm; the water reducing agent is Nanjing Ruidi High-tech Co., ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Equivalent diameteraaaaaaaaaa
Tensile strengthaaaaaaaaaa
Elastic modulusaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-ductility cement-based composite material for repairing a hydraulic concrete structure. The cement-based composite material is prepared from the following components in parts by mass: 20 to 60 parts of cement, 0 to 80 parts of fly ash, 0 to 80 parts of pulverized slag powder, 5 to 10 parts of light-weight calcium powder, 1 to 5 parts of nanometer SiO2, 25 to 40 parts of a fine aggregate, 20 to 40 parts of water, 0.1 to 1 part of a water reducing agent and 0.5 to 2.5 parts of polyvinyl alcohol fibers. According to the high-ductility cement-based composite material for repairing the hydraulic concrete structure, the air content of a mixture is 7 to 10 percent; at the 28-day age, the uniaxial tensile strain is greater than or equal to 5.0 percent, the cube compressive strength is greater than or equal to 60MPa, the frost resistance is greater than or equal to F500, the sulfate corrosion resistance is greater than or equal to KS300, the chloride ion penetration resistance DRCM is less than or equal to 2.0*10<-12>m<2> / s, and the tensile bonding strength with base structure concrete is greater than or equal to 5.0MPa. Under the condition of not mixing any air-entraining agent, preservative or thickening agent, the high-ductility cement-based composite material for repairing the hydraulic concrete structure provided by the invention has high durability, enhanced capability in synergistically acting with an existing structure and a remarkable repairing and reinforcing effect.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a high-ductility cement-based composite material for repairing hydraulic concrete structures and an application thereof. Background technique [0002] my country's water conservancy and hydropower projects have exerted huge social and economic benefits in hydropower generation, flood control and disaster reduction, industrial and agricultural water use, shipping, aquatic products, and environmental protection tourism. Like other buildings, hydraulic concrete buildings gradually enter the "middle-aged and old age" after they are completed and put into operation. Various aging and disease problems have gradually emerged, and some have seriously affected the safe operation of the project. The repair and reinforcement of hydraulic concrete buildings has become a very prominent problem in my country's current water conservancy and hydropower projects. [0003] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04C04B28/06C04B14/28C04B14/06C04B16/06C04B111/74C04B111/20
CPCC04B14/062C04B14/28C04B16/0641C04B28/04C04B28/06C04B2111/20C04B2111/2015C04B2111/74C04B2201/10C04B2201/50C04B18/08C04B18/141C04B14/06C04B22/002C04B24/24C04B14/068
Inventor 陈波郭丽萍白银宁逢伟
Owner NANJING HYDRAULIC RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com