An environmentally friendly and cement technology, applied in the field of cement and environmentally friendly decorative cement, can solve the problems of cracking and alkali return of decorative cement, and achieve the effect of reducing the risk of cracking, increasing the strength, and improving the workability of construction.

Inactive Publication Date: 2017-12-22
JIAHUA SPECIAL CEMENT
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The present invention aims to solve the technical problems that the decorative cement in the prior art is prone to cracking and alkali return, and provides a new environment-friendly decorative cement, which can prevent cracking and alkali return through the selection of raw materials and specific ratio design. problems, and has good compatibility and adhesion, and also has good environmental protection, can absorb and decompose the peculiar smell in the air, purify the air, have the effects of humidity control, deodorization, sound insulation, waterproof and heat insulation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly decoration cement

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] An environment-friendly decorative cement, which consists of the following raw materials in parts by weight: 42.5-51 parts of Portland cement, 4 parts of expansion agent, 8 parts of metakaolin, 6 parts of silica fume, 1 part of whisker, and redispersible latex Powder 8 parts, water reducer 1.5 parts, defoamer 0.37 parts, cellulose ether 0.13 parts, heavy calcium 5 parts, shell activated carbon 15 parts.

[0032]In this embodiment, the expansion agent is a sulphoaluminate expansion agent.

[0033] In this embodiment, the redispersible latex powder is a redispersible latex powder with a glass transition temperature of -3°C.

[0034] In this embodiment, the cellulose ether is hydroxypropyl methylcellulose with a viscosity of 300 mpa.s.

[0035] In this embodiment, the whiskers are calcium sulfate whiskers with an average diameter of 1 um and an average length of 30 um.

[0036] In this embodiment, the average particle diameter of heavy calcium is 1 μm.

[0037] In this ...

Embodiment 2

[0040] An environment-friendly decorative cement, which is composed of the following raw materials in parts by weight: 42.5-55 parts of Portland cement, 2 parts of expansion agent, 9.9 parts of metakaolin, 3 parts of silica fume, 2 parts of whiskers, and redispersible latex 10 parts of powder, 2 parts of water reducer, 1 part of defoamer, 0.1 part of cellulose ether, 5 parts of heavy calcium, and 10 parts of diatomaceous earth.

[0041] In this embodiment, the expansion agent is a sulphoaluminate expansion agent.

[0042] In this embodiment, the redispersible latex powder is a redispersible latex powder with a glass transition temperature of 0°C.

[0043] In this embodiment, the cellulose ether is hydroxypropyl methylcellulose with a viscosity of 400 mpa.s.

[0044] In this embodiment, the whiskers are calcium sulfate whiskers with an average diameter of 8 um and an average length of 200 um.

[0045] In this embodiment, the average particle diameter of heavy calcium is 10 μm...

Embodiment 3

[0049] An environment-friendly decorative cement, which consists of the following raw materials in parts by weight: Portland cement 52.5-45 parts, expansion agent 4 parts, metakaolin 8.88 parts, silica fume 6 parts, whiskers 3 parts, redispersible latex 10 parts of powder, 2 parts of water reducer, 1 part of defoamer, 0.12 parts of cellulose ether, 10 parts of heavy calcium, 5 parts of shell activated carbon, and 5 parts of calcium carbide powder.

[0050] In this embodiment, the expansion agent is a sulphoaluminate expansion agent.

[0051] In this embodiment, the redispersible latex powder is a redispersible latex powder with a glass transition temperature of 5°C.

[0052] In this embodiment, the cellulose ether is hydroxypropyl methylcellulose with a viscosity of 500 mpa.s.

[0053] In this embodiment, the whiskers are calcium sulfate whiskers with an average diameter of 6 um and an average length of 100 um.

[0054] In this embodiment, the average particle diameter of he...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
viscosityaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses environment-friendly decoration cement and belongs to the technical field of building materials. The environment-friendly decoration cement is prepared from the following raw materials in parts by weight: 45-60 parts of Portland cement, 0-4 parts of an expanding agent, 4-10 parts of metakaolin, 2-6 parts of silicon powder, 1-3 parts of crystal whiskers, 5-10 parts of redispersible emulsion powder, 1-2 parts of a water reducer, 0.3-1.0 part of a defoaming agent, 0.1-0.15 part of cellulose ether, 5-10 parts of ground calcium carbonate and 10-15 parts of an environment-friendly material. The environment-friendly decoration cement disclosed by the invention has no problems such as alkali efflorescence and cracking and has good peaceability, corrosion resistance and environment-friendly performance.

Description

technical field [0001] The invention relates to cement, in particular to an environment-friendly decorative cement, which belongs to the technical field of building materials. Background technique [0002] Industrial buildings are mostly concrete structures, steel-concrete structures, steel structures, etc., and their exterior wall materials may be steel plates, wood panels, or calcium-silicon panels. The environment is also more in line with the aesthetic style of modern people, which is confirmed by more and more fair-faced concrete construction industries. Existing decorative cements include white cement and colored cement, which are mainly used in construction projects. It can be formulated into colored mortar or made into various colored and white concrete. Compared with natural decorative materials, it has the advantages of convenient use, easy color adjustment and low price, but its adhesion is poor, and it is easy to fall off the surface of steel plates, wood board...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B28/30C04B111/20C04B111/34
CPCC04B28/04C04B28/30C04B2111/00017C04B2111/20C04B2111/343C04B2201/10C04B2201/50C04B14/106C04B18/146C04B14/383C04B24/32C04B24/383C04B14/28C04B14/022C04B20/008C04B20/006C04B2103/302C04B2103/0068C04B14/08C04B14/202C04B14/322
Inventor 王宁
Owner JIAHUA SPECIAL CEMENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com