A kind of preparation method of cationic dyeable polyester poy yarn

A cationic and polyester technology, applied in the field of polyester spinning, can solve the problems affecting the continuity and safety of the production process, the rapid rise of the pressure difference of the filter, and the reduction of the service life of the filter, so as to ensure the spinnability, The effect of reducing coordination and reducing impurities

Active Publication Date: 2020-10-02
JIANGSU HENGKE ADVANCED MATERIALS CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, due to the addition of the third component in the CDP melt, its apparent viscosity is relatively large, and the impurities produced in the production process also increase accordingly, causing the pressure of some spinning components and the pressure difference of the filter to rise faster. There are carbonized cokes on the inner wall of the pipeline. These carbonized cokes adhere to the inner wall of the pipeline, which is easy to cause blockage of the pipeline system and is not easy to be removed, which brings great difficulties to the dredging of the pipeline. In addition, in the production of this kind of fiber In the process, the service life of the filter is greatly reduced, generally only one week, while the service life of some other spinning components is generally only 10 days, so it is necessary to clean and replace the spinning components frequently, which will not only increase the operating cost, but also Will affect the continuity and safety of the entire production process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A preparation method of cationic dyeable polyester POY yarn, the steps are as follows:

[0048] a) preparing a spinning melt;

[0049] (1) transesterification reaction prepares bishydroxyethyl isophthalate-5-sodium sulfonate;

[0050] First, dimethyl isophthalate-5-sodium benzenesulfonate and ethylene glycol with a molar ratio of 10:1 are put into the preparation kettle, and the catalyst Zn(Ac) is added. 2 Carry out the transesterification reaction at 176°C with the anti-ether agent NaAc until the distilled amount of water reaches 91% of the theoretical value, and obtain bishydroxyethyl isophthalate-5-sodium sulfonate, then add ethylene glycol and Potassium ethylene glycol is modulated to obtain the ethylene glycol solution containing 30.4wt% bishydroxyethyl isophthalate-5-sodium sulfonate, wherein catalyst Zn(Ac) 2 The addition amount is 0.5wt% of the addition amount of dimethyl isophthalate-5-sodium benzenesulfonate, and the addition amount of anti-ether agent NaAc ...

Embodiment 2

[0067] A preparation method of cationic dyeable polyester POY yarn, the steps are as follows:

[0068] a) preparing a spinning melt;

[0069] (1) transesterification reaction prepares bishydroxyethyl isophthalate-5-sodium sulfonate;

[0070] First, put dimethyl isophthalate-5-sodium benzenesulfonate and ethylene glycol in a molar ratio of 10.5:1 into the preparation kettle, add the catalyst Zn(Ac) 2 Carry out the transesterification reaction at 178 ℃ after the anti-ether agent NaAc until the distilled amount of water reaches 92% of the theoretical value, and obtain bishydroxyethyl isophthalate-5-sodium sulfonate, then add ethylene glycol and Sodium ethylene glycol modulates to obtain the ethylene glycol solution containing 31wt% bishydroxyethyl isophthalate-5-sodium sulfonate, wherein catalyst Zn(Ac) 2 The addition amount is 0.2wt% of the addition amount of dimethyl isophthalate-5-sodium benzenesulfonate, the addition amount of anti-ether agent NaAc is the addition amount of...

Embodiment 3

[0085] A preparation method of cationic dyeable polyester POY yarn, the steps are as follows:

[0086] a) preparing a spinning melt;

[0087] (1) transesterification reaction prepares bishydroxyethyl isophthalate-5-sodium sulfonate;

[0088] First, put dimethyl isophthalate-5-sodium benzenesulfonate and ethylene glycol into the preparation kettle with a molar ratio of 11:1, add the catalyst Zn(Ac) 2 Carry out the transesterification reaction at 175°C with the anti-ether agent NaAc until the distilled amount of water reaches 90% of the theoretical value, to obtain bishydroxyethyl isophthalate-5-sodium sulfonate, then add ethylene glycol and Calcium ethylene glycol is modulated to obtain the ethylene glycol solution containing 30wt% bishydroxyethyl isophthalate-5-sodium sulfonate, wherein catalyst Zn(Ac) 2 The addition amount is 0.3wt% of the addition amount of dimethyl isophthalate-5-sodium benzenesulfonate, the addition amount of anti-ether agent NaAc is the addition amount ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of cation dyeable POY (Polyester Pre-Oriented Yarn). The method comprises the following steps: firstly, mixing dimethyl isophthalate-5-sodium benzenesulfonate, ethylene glycol, a catalyst and an anti-ether agent, performing transesterification, and adding the ethylene glycol and a complex ion modifier for preparation after the transesterification is ended; secondly, mixing terephthalic acid, the ethylene glycol, the catalyst, a stabilizer and a delustering agent, performing esterification reaction, adding a product obtained by preparation after theesterification reaction into a reaction system already reaching a reaction endpoint of the esterification reaction, and performing condensation polymerization to obtain a spinning melt; finally, metering, extruding, cooling, oiling and winding the spinning melt to obtain the cation dyeable POY. The method reduces the generation of impurities in a production process, thereby reducing pressure riseof a spinning assembly and a filter, prolonging the service life, ensuring the continuity and safety of the whole production flow, and achieving a good economic value and promotion value.

Description

technical field [0001] The invention belongs to the field of polyester spinning, and in particular relates to a cationic dyeable polyester POY yarn. Background technique [0002] Due to the high crystallinity, high degree of orientation and high glass transition temperature of PET fibers, it is difficult for dyes to diffuse into PET molecules in the presence of normal pressure and no carrier, and it is difficult to dye. Therefore, the dyeing of PET fibers needs to be done under high temperature and high pressure. or in the presence of a carrier. Cationic dye-dyeable PET chip (CDP) is a copolymer formed by introducing a third component into the macromolecular chain of PET, which overcomes the shortcomings of polyester that is not easy to dye, and has become the next best choice for bright and semi-dull PET. Another important PET variety after slicing, in which the third component generally contains a strongly acidic sodium sulfonate group -SO 3 Na, the sodium sulfonate grou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/92D01F1/10C08G63/688C08G63/78C08K9/10C08K3/22D01D5/08
Inventor 朱冬妹于涛丛茂鹏胡江顺
Owner JIANGSU HENGKE ADVANCED MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products