Durable granulated blast furnace slag building block

A blast furnace slag, durable technology, used in building components, buildings, building structures, etc., can solve problems such as poor mechanical properties and durability, improve mechanical properties and durability, improve fluidity, and enhance contact. site effect

Inactive Publication Date: 2018-01-12
杨忠华
View PDF9 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The main technical problem to be solved by the invention is to provide a durable blast furnace slag block in view of the poor mechanical properties and durability of the traditional blast furnace slag block

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0023]Add chitosan and water into No. 1 beaker at a mass ratio of 1:100, stir and mix with a glass rod for 30 minutes, let it stand for swelling for 4 hours, and then move No. , under the condition of rotating speed of 500r / min, heat and stir to dissolve for 50min to obtain chitosan liquid; add agar and water into the No. Then move the No. 2 beaker into a magnetic stirrer with digital display speed measurement and constant temperature, and heat and stir to dissolve for 50 minutes at a temperature of 100°C and a speed of 500r / min to obtain agar liquid; place the coconut shell fiber in an oven and dry it until it contains water The ratio is 8% to obtain dry coconut shell fiber; put dry coconut shell fiber and tetraethyl orthosilicate in a No. 3 beaker at a mass ratio of 1:30, stir and mix and impregnate for 40 minutes at a rotating speed of 300r / min. Filtrate to obtain pretreated coconut shell fiber; put the pretreated coconut shell fiber in a carbonization furnace and feed nitr...

example 2

[0025] Add chitosan and water into No. 1 beaker at a mass ratio of 1:100, stir and mix with a glass rod for 30 minutes, let it stand for swelling for 4 hours, and then move No. , under the condition of rotating speed of 500r / min, heat and stir to dissolve for 50min to obtain chitosan liquid; add agar and water into the No. Then move the No. 2 beaker into a magnetic stirrer with digital display speed measurement and constant temperature, and heat and stir to dissolve for 50 minutes at a temperature of 100°C and a speed of 500r / min to obtain agar liquid; place the coconut shell fiber in an oven and dry it until it contains water The ratio is 8% to obtain dry coconut shell fiber; put dry coconut shell fiber and tetraethyl orthosilicate in a No. 3 beaker at a mass ratio of 1:30, stir and mix and impregnate for 40 minutes at a rotating speed of 300r / min. Filtrate to obtain pretreated coconut shell fiber; put the pretreated coconut shell fiber in a carbonization furnace and feed nit...

example 3

[0027] Add chitosan and water into No. 1 beaker at a mass ratio of 1:100, stir and mix with a glass rod for 30 minutes, let it stand for swelling for 4 hours, and then move No. , under the condition of rotating speed of 500r / min, heat and stir to dissolve for 50min to obtain chitosan liquid; add agar and water into the No. Then move the No. 2 beaker into a magnetic stirrer with digital display speed measurement and constant temperature, and heat and stir to dissolve for 50 minutes at a temperature of 100°C and a speed of 500r / min to obtain agar liquid; place the coconut shell fiber in an oven and dry it until it contains water The ratio is 8% to obtain dry coconut shell fiber; put dry coconut shell fiber and tetraethyl orthosilicate in a No. 3 beaker at a mass ratio of 1:30, stir and mix and impregnate for 40 minutes at a rotating speed of 300r / min. Filtrate to obtain pretreated coconut shell fiber; put the pretreated coconut shell fiber in a carbonization furnace and feed nit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention discloses a durable granulated blast furnace slag building block and belongs to the technical field of a building material. The durable granulated blast furnace slag building block is prepared according to the following steps: crushing granulated blast furnace slag and sieving, thereby acquiring refined granulated blast furnace slag; mixing and stirring the acquired refined granulated blast furnace slag and sulfuric acid, soaking and filtering, thereby acquiring the pretreated granulated blast furnace slag; stirring, mixing and fermenting paper-making black liquor, chitosan solution, soybean protein powder and biogas slurry, thereby acquiring a fermentation liquor; mixing the pretreated granulated blast furnace slag and the fermentation liquor, soaking and filtering, therebyacquiring the modified granulated blast furnace slag; mixing and stirring the modified granulated blast furnace slag, gypsum, quicklime, cement, water, modified charring cocoanut fiber and silane coupling agent, thereby acquiring a mixed slurry; injecting the mixed slurry into a mold, pressing and forming, thereby acquiring a blank; placing the blank into a curing chamber and curing, thereby acquiring the durable granulated blast furnace slag building block. The durable granulated blast furnace slag building block provided by the invention has excellent mechanical properties and durability.

Description

technical field [0001] The invention discloses a durable blast furnace slag block, which belongs to the technical field of building materials. Background technique [0002] With the development of the construction industry and the increasing emphasis on the quality of construction projects, the quality and quantity of construction sand, which is one of the basic components of concrete and mortar, has an increasingly obvious impact on the construction industry. On the one hand, the market has higher and higher requirements on the quality of sand, and the quantity is increasing; on the other hand, natural sand resources that meet the quality requirements are becoming less and less, and engineering problems caused by this occur from time to time. With the gradual shortage of natural sand resources and the country's restrictions on the mining of natural sand, as one of the necessary components for concrete preparation, the source of natural sand will be limited, and its market w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14E04C1/00
Inventor 杨忠华殷小祥张琳
Owner 杨忠华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com