A kind of preparation method of pet/pp composite sound-absorbing material

A technology of sound-absorbing material and hopper is applied in the field of preparation of PET/PP composite sound-absorbing material, which can solve the problems of complex production process, pollute the environment and high cost, and achieve the effect of small cavity volume, better sound absorption effect and good fit.

Active Publication Date: 2019-03-01
宁波尚唯汽车饰件有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Chinese patent application number 201210478186.2 discloses a PET fiber / polyacrylonitrile fiber composite sound-absorbing cotton, which is made of the following raw materials in parts by weight: PET fiber 70-80, polyacrylonitrile fiber 40-50, emulsifier OP-20 10 -15, Pingpingjia O-15 5-10, PP 80-100, SEBS 30-40, calcined clay 15-20, modified diatomite 10-15, stearic acid 2-3, diisophthalic acid Octyl ester 5-8, tricresyl phosphate 4-6, polyethylene wax 2-3, vinyl tris (β-methoxyethoxy) silane 1-2, calcium stearate 2-3, dimethyl Isooctyl tin dimercaptoacetate 1-2, antioxidant ODA 0.5-1.5, antioxidant 1035 1-2, although the sound-absorbing cotton prepared by this method has a certain flame-retardant and sound-absorbing effect, but in the production process due to A large number of organic polymer materials are used, resulting in heavy odor and polluting the environment
However, the production process of this material is complicated and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A preparation method of PET / PP composite sound-absorbing material, comprising the steps of:

[0027] (1) First put PET and PP into the hopper of the melt-blown machine at a mass ratio of 3:6, and after being extruded and filtered, they are in a molten state, and the centrifugal cotton mesh surface is continuously sprayed with a melt-blown spinneret , forming a network structure, after the spinning is finished, it is rolled, cooled, and rolled into a flat sound-absorbing material. Before the spinning process, the centrifugal cotton mesh surface is also laid with an activated carbon fiber mesh surface;

[0028] (2) The sound-absorbing material prepared in step (1) is spread in the steam mold, and the steam mold is closed, and the steam engine is used to steam the sound-absorbing material through the steam mold. The pressure of the steam engine is 27Mpa, and the heating temperature of the steam mold Control at 225°C, and keep the heating time at 45s;

[0029] (3) Spread t...

Embodiment 2

[0034] A preparation method of PET / PP composite sound-absorbing material, comprising the steps of:

[0035] (1) First put PET and PP into the hopper of the melt-blown machine at a mass ratio of 3:7, and after being extruded and filtered, they are in a molten state, and the centrifugal cotton mesh surface is continuously sprayed with a melt-blown spinneret , forming a network structure, after the spinning is finished, it is rolled, cooled, and rolled into a flat sound-absorbing material. Before the spinning process, the centrifugal cotton mesh surface is also laid with an activated carbon fiber mesh surface;

[0036] (2) The sound-absorbing material to be made in step (1) is laid in the steam mold, and the steam mold is closed, and the steam engine is used to steam the sound-absorbing material through the steam mold. The pressure of the steam engine is 28Mpa, and the heating temperature of the steam mold Control at 230°C, and keep the heating time at 43s;

[0037] (3) Spread t...

Embodiment 3

[0042] A preparation method of PET / PP composite sound-absorbing material, comprising the steps of:

[0043] (1) First put PET and PP into the hopper of the melt-blown machine at a mass ratio of 3:8, and after being extruded and filtered, they are in a molten state, and the centrifugal cotton mesh surface is continuously sprayed by a melt-blown spinneret , forming a network structure, after the spinning is finished, it is rolled, cooled, and rolled into a flat sound-absorbing material. Before the spinning process, the centrifugal cotton mesh surface is also laid with an activated carbon fiber mesh surface;

[0044] (2) The sound-absorbing material prepared in step (1) is spread in the steam mold, and the steam mold is closed, and the steam engine is used to steam the sound-absorbing material through the steam mold. The pressure of the steam engine is 29Mpa, and the heating temperature of the steam mold Control at 225°C, and keep the heating time at 45s;

[0045] (3) Spread the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a PET / PP composite sound-absorbing material preparation method, and relates to the technical field of vehicle interior decoration member processing, wherein the sound insulation pad comprises two layers of sound insulation cotton felts, and the preparation method comprises: melt spinning of a PET / PP mixture, steam mold pre-molding, cooling setting, water cutting and packaging warehousing. According to the present invention, the PET / PP composite sound-absorbing material is formed by compounding the multiple layer sound absorbing materials, comprises six layers, has characteristics of good sound absorbing effect, good fitting degree and good aesthetics; and in the preparation method, the high temperature steam is introduced into the interior of the sound absorbing material by using the steam mold and the steam engine so as to completely absorb water, the PET / PP composite mesh surface can fully expand and coil so as to fill the entire molding cavity, and the shaping with the cold mold is performed, such that the sound insulation pad prepared from the sound absorbing material can be attached to the vehicle front enclose member, the volume of the cavity is small,and the sound transmission medium (air) is reduced; and through the tight attachment of the sound insulation pad, the vibration of the attached surface is reduced, and the noise is reduced.

Description

technical field [0001] The invention relates to the technical field of processing automotive interior parts, in particular to a preparation method of a PET / PP composite sound-absorbing material. Background technique [0002] At present, the size of the car noise has reflected the quality and technical performance of the car. The more advanced the car is, the more the noise and vibration of the car must be transmitted to the passenger compartment as little as possible, which is often said in terminology to match the NVH performance of the whole car. NVH is a comprehensive issue to measure the quality of automobile manufacturing. It also gives the most intuitive feeling to automobile users and is an important part of automobile design and manufacturing. [0003] There are many sources of car noise, such as engines, gearboxes, drive axles, drive shafts, compartments, glass windows, tires, relays, horns, stereos, etc., and these parts will generate noise when they are working. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/02B32B27/12B32B37/08B32B17/02B32B17/12B32B37/12B32B37/10B32B27/36B32B37/06B32B38/00B32B27/32B32B38/18B60R13/08
Inventor 陈伟王明
Owner 宁波尚唯汽车饰件有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com