Ceiling filter cotton treatment agent and preparation method
A technology of filter cotton and treatment agent, which is applied in fiber treatment, plant fiber, textiles and papermaking, etc., can solve the problems that there is no disclosure of canopy filter cotton treatment agent technology, and achieve the maximum dust holding capacity and good adhesion , the effect of strong transparency
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0025] (1) Add 1350 parts of deionized water, 50 parts of emulsifier sodium dodecyl benzene sulfonate, 165 parts of emulsifier fatty alcohol polyoxyethylene ether, 910 parts of ethyl acrylate, 180 parts of isooctyl acrylate into the emulsification kettle , 490 parts of terpene resin, 60 parts of methyl methacrylate, 260 parts of vinyl acetate, 110 parts of methacrylic acid, 60 parts of glyceryl dimethacrylate, stirred and emulsified for 21 minutes to make an emulsion;
[0026] (2) 450 parts of deionized water were added to the reaction kettle, 727 parts of the emulsion were added to the reaction kettle, stirred and heated to 77°C, and an aqueous potassium persulfate solution prepared by 0.7 parts of potassium persulfate and 3 parts of deionized water was added, Stir, be warmed up to 86 ℃, then control temperature at 85-90 ℃, drip the remaining 2908 parts of emulsion, dropwise add the potassium persulfate aqueous solution prepared by 2 parts of potassium persulfate and 30 parts ...
Embodiment 2
[0029] (1) Add 1370 parts of deionized water, 52 parts of emulsifier sodium dodecyl benzene sulfonate, 168 parts of emulsifier fatty alcohol polyoxyethylene ether, 920 parts of ethyl acrylate and 185 parts of isooctyl acrylate into the emulsification kettle , 500 parts of terpene resin, 65 parts of methyl methacrylate, 267 parts of vinyl acetate, 115 parts of methacrylic acid, 62 parts of glyceryl dimethacrylate, stirred and emulsified for 24 minutes to make an emulsion;
[0030] (2) 460 parts of deionized water were added to the reaction kettle, 742 parts of the emulsion were added to the reaction kettle, stirred and heated to 78°C, and the potassium persulfate aqueous solution prepared by 0.72 parts of potassium persulfate and 3.5 parts of deionized water was added, Stir, be warmed up to 86 ℃, then control temperature at 85-90 ℃, drip the remaining 2968 parts of emulsion, dropwise add the potassium persulfate aqueous solution prepared by 2.2 parts of potassium persulfate and ...
Embodiment 3
[0033] (1) Add 1400 parts of deionized water, 56 parts of emulsifier sodium dodecyl benzene sulfonate, 173 parts of emulsifier fatty alcohol polyoxyethylene ether, 930 parts of ethyl acrylate, 190 parts of isooctyl acrylate into the emulsification kettle , 510 parts of terpene resin, 70 parts of methyl methacrylate, 275 parts of vinyl acetate, 120 parts of methacrylic acid, 65 parts of glycerol dimethacrylate, stirred and emulsified for 26 minutes to make an emulsion;
[0034] (2) 470 parts of deionized water were added to the reaction kettle, 767 parts of the emulsion were added to the reaction kettle, stirred and heated to 78°C, and the potassium persulfate aqueous solution prepared by 0.75 parts of potassium persulfate and 4 parts of deionized water was added, Stir, be warmed up to 88 ℃, then control temperature at 85-90 ℃, drip the remaining 3028 parts of emulsion, dropwise add the potassium persulfate aqueous solution prepared by 2.5 parts of potassium persulfate and 35 pa...