Metal piece anti-deformation heat treatment process

A metal parts, anti-deformation technology, applied in heat treatment equipment, manufacturing tools, quenching agents, etc., can solve the problems of single process and large deformation of metal workpieces, and achieve the effect of simple production process, easy to fall off, and reduce oxidation loss

Inactive Publication Date: 2018-03-02
湖州正德轻工机械有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current metal workpiece heat treatment process often has a large deformation of the metal workpiece due to the single process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] The present invention will be further described below in conjunction with the examples, but not as a basis for limiting the present invention.

[0012] Example. The anti-deformation heat treatment process for metal parts includes the following process steps:

[0013] (1) The metal parts are pickled in 15% hydrochloric acid solution, ultrasonically treated in the later stage of the treatment, and finally rinsed with pure water and dried;

[0014] (2) Metal parts are coated with a protective layer, and the components in the protective layer are proportioned according to the following parts by weight: 45 parts of glass frit, 2 parts of iron oxide, 5 parts of chromium oxide, 8 parts of copper oxide, 2 parts of aluminum oxide, acrylic acid 6 parts, 15 parts of polyvinyl acetate emulsion, 15 parts of ethanol solution;

[0015] (3) Heating by laser flame spraying, heating to a temperature of 860°C, and continuing heating for 12 minutes;

[0016] (4) Cooling the metal parts,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a heat treatment process for anti-deformation of metal parts, which comprises the following process steps: (1) pickling treatment of metal parts in 15% hydrochloric acid solution, ultrasonic treatment in the later stage of treatment, and finally washing with pure water, blowing Dry; (2) Metal parts are coated with a protective layer, and the components in the protective layer are proportioned according to the following parts by weight: 45 parts of glass frit, 2 parts of iron oxide, 5 parts of chromium oxide, 8 parts of copper oxide, and 2 parts of aluminum oxide , 6 parts of acrylic acid, 15 parts of polyvinyl acetate emulsion, 15 parts of ethanol solution; (3) Heating by laser flame spraying, heating to a temperature of 860 ° C, and continuing heating for 12 minutes; (4) Cooling metal parts, the temperature is cooled to 120 ° C , the cooling medium is a polyalkylene glycol polymer aqueous solution with a concentration of 14%. The invention can prevent the deformation of the metal parts and ensure the quality of the metal parts.

Description

technical field [0001] The invention relates to a heat treatment process, in particular to a casting anti-deformation heat treatment process. Background technique [0002] Metal heat treatment is a process that heats, heats and cools a metal workpiece in a certain medium, and controls its performance by changing the surface or internal structure of the metal material. Metal heat treatment is one of the important processes in mechanical manufacturing. Heat treatment generally does not change the shape and overall chemical composition of the workpiece, but changes the molecular structure inside the workpiece by heating, or changes the chemical composition of the surface of the workpiece, endows or improves the properties of the workpiece. Use performance. The current metal workpiece heat treatment process often has a large deformation of the metal workpiece due to the single process. Contents of the invention [0003] The purpose of the present invention is to provide a me...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21D1/09C21D1/70C21D1/60
CPCC21D1/09C21D1/60C21D1/70
Inventor 崔红伟
Owner 湖州正德轻工机械有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com