A kind of ceo with ce-mof as cerium precursor 2 /tio 2 Preparation method of low temperature scr catalyst

A technology of SCR catalyst and precursor, which is applied in the field of catalyst preparation, can solve the problems of limited application of MOF-based materials, and achieve the effects of improving dispersion, easy access to experimental raw materials, and simple process

Active Publication Date: 2020-03-27
BEIJING UNIV OF TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, so far the application of MOF-based materials in the field of denitrification is still very limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ceo with ce-mof as cerium precursor <sub>2</sub> /tio <sub>2</sub> Preparation method of low temperature scr catalyst
  • A kind of ceo with ce-mof as cerium precursor <sub>2</sub> /tio <sub>2</sub> Preparation method of low temperature scr catalyst
  • A kind of ceo with ce-mof as cerium precursor <sub>2</sub> /tio <sub>2</sub> Preparation method of low temperature scr catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026]Weigh 29.4g of titanyl sulfate, dissolve it in 300ml of deionized water, stir for 4h, add the prepared Ce-MOF-112.4g, stir for 2h, slowly add ammonia water with a concentration of 25% to adjust the pH of the system to 10, continue stirring for 6h , stop stirring and let stand for 12h. Filter and dry the solid at 80°C for 12h, then put the dried powder into a muffle furnace and calcinate at 450°C for 2h in an air atmosphere to obtain 1# catalyst sample.

Embodiment 2

[0028] Weigh 29.4g of titanyl sulfate, dissolve it in 300ml of deionized water, stir for 4h, add the prepared Ce-MOF-112.4g, stir for 2h, slowly add ammonia water with a concentration of 25% to adjust the pH of the system to 11, continue stirring for 6h , stop stirring and let stand for 12h. Filter and dry the solid at 80°C for 12h, then put the dried powder into a muffle furnace and calcinate at 450°C for 2h in an air atmosphere to obtain 2# catalyst sample.

Embodiment 3

[0030] Weigh 29.4g of titanyl sulfate, dissolve it in 300ml of deionized water, stir for 4h, add the prepared Ce-MOF-112.4g, stir for 2h, slowly add ammonia water with a concentration of 25% to adjust the pH of the system to 10, continue stirring for 6h , stop stirring and let stand for 12h. Filter, dry the solid at 80°C for 12h, then put the dried powder into a muffle furnace, and calcinate at 550°C for 2h in an air atmosphere to obtain 3# catalyst sample.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A kind of CeO using Ce‑MOF as cerium precursor 2 / TiO 2 The preparation method of low-temperature SCR catalyst belongs to the technical field of catalyst preparation. The preparation method includes the following steps: (1) weigh a quantitative cerium source and organic ligands and dissolve them in an appropriate amount of solvent, and prepare a cerium-based metal organic framework material (Ce-MOF) using a solvothermal method; (2) weigh a quantitative soluble titanium source Dissolve in a certain solvent, then add the Ce-MOF prepared in step (1), and prepare the catalyst precursor by co-precipitation method; (3) put the catalyst precursor obtained in step (2) into a muffle furnace for calcination. CeO prepared using Ce‑MOF as cerium precursor can be obtained 2 / TiO 2 Low temperature SCR catalyst. The preparation conditions of the invention are easy to control, the preparation process is simple, and the prepared catalyst has strong NH 3 ‑SCR reaction has excellent catalytic activity and good sulfur and water resistance.

Description

technical field [0001] The invention relates to a CeO with Ce-MOF as the precursor of cerium 2 / TiO 2 The preparation method of the low-temperature SCR catalyst and its application in ammonia selective catalytic reduction of nitrogen oxides belong to the technical field of catalyst preparation. Background technique [0002] Nitrogen oxides (NO x ) is a common air pollutant, which is one of the main substances that form acid rain, and is also an important factor that forms harsh weather conditions such as photochemical smog and smog in the atmosphere, which has a bad impact on the ecological environment. Therefore, it is of great significance to research and develop efficient nitrogen oxide removal technology. Ammonia selective catalytic reduction (Selective Catalysis Reduction, NH 3 -SCR) is currently the most widely used flue gas denitration technology in industry, and its core lies in the development of SCR denitration catalyst. At present, vanadium-titanium base (V ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/10B01J37/08B01J35/10B01D53/86B01D53/56
CPCB01D53/8628B01J23/002B01J23/10B01J37/086B01J37/088B01D2251/2062B01J35/60Y02P20/30
Inventor 邱文革尹孟奇朱红太宋丽云何洪
Owner BEIJING UNIV OF TECH
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com