Anti-fog film and preparation method thereof

A thin film and anti-fog technology, applied in the field of plastic materials, can solve problems such as troubles, affecting people's use experience, and fogging of flat mirrors, and achieve the effect of low process conditions, good social value, and reduced haze

Inactive Publication Date: 2018-04-06
ZHENGZHOU CHENGHE INFORMATION TECH CO LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional flat mirrors are prone to fogging, which seriously affects people's experience. Although there is a device for h

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] An anti-fog film, comprising the following components in parts by weight: 20 parts of methyl acetate, 5 parts of titanium dioxide, 2 parts of metallic silver powder, 5 parts of sodium carboxymethyl cellulose, 6 parts of tin oxide, 4 parts of propylene glycol butyl ether 12 parts of nano-zirconia sol, 5 parts of sodium amide, 4 parts of zinc acetate dihydrate, 2 parts of chitosan, 2 parts of fluoroethylene carbonate, 0.1 part of copper selenate, 0.1 part of acrylic resin film-forming agent, Antioxidant 0.1 part. The metal silver powder, tin oxide and titanium dioxide are all in nanometer scale.

[0017] A kind of preparation method of anti-fog film, preparation method is as follows: (1) methyl acetate, titanium dioxide, metal silver powder, carboxymethyl cellulose, tin oxide, propylene glycol butyl ether, nano zirconium dioxide sol, chitosan are mixed , stirring for 15 minutes, stirring speed 120r / min; (2) Add the obtained product from the previous step into the mixer a...

Embodiment 2

[0019] An anti-fog film, comprising the following components in parts by weight: 40 parts of methyl acetate, 10 parts of titanium dioxide, 5 parts of metallic silver powder, 8 parts of sodium carboxymethyl cellulose, 11 parts of tin oxide, 8 parts of propylene glycol butyl ether 17 parts of nano-zirconia sol, 8 parts of sodium amide, 8 parts of zinc acetate dihydrate, 5 parts of chitosan, 5 parts of fluoroethylene carbonate, 1 part of copper selenate, 1 part of acrylic resin film-forming agent, Antioxidant 1 part. The metal silver powder, tin oxide and titanium dioxide are all in nanometer scale.

[0020] A kind of preparation method of anti-fog film, preparation method is as follows: (1) methyl acetate, titanium dioxide, metal silver powder, carboxymethyl cellulose, tin oxide, propylene glycol butyl ether, nano zirconium dioxide sol, chitosan are mixed , stirred for 35min, and the stirring speed was 350r / min; (2) Add the product obtained from the previous step into the mixer...

Embodiment 3

[0022] An anti-fog film, comprising the following components in parts by weight: 37 parts of methyl acetate, 6 parts of titanium dioxide, 3 parts of metallic silver powder, 6 parts of carboxymethyl cellulose, 8 parts of tin oxide, and 5 parts of propylene glycol butyl ether , 13 parts of nano-zirconia sol, 7 parts of sodium amide, 5 parts of zinc acetate dihydrate, 3 parts of chitosan, 3 parts of fluoroethylene carbonate, 0.5 part of copper selenate, 0.6 part of acrylic resin film-forming agent, anti 0.2 parts of oxygen agent. The metal silver powder, tin oxide and titanium dioxide are all in nanometer scale.

[0023] A kind of preparation method of anti-fog film, preparation method is as follows: (1) methyl acetate, titanium dioxide, metal silver powder, carboxymethyl cellulose, tin oxide, propylene glycol butyl ether, nano zirconium dioxide sol, chitosan are mixed , stirred for 28min, and the stirring speed was 255r / min; (2) Add the product obtained from the previous step i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anti-fog film. The anti-fog film comprises the following components in parts by weight: 20-40 parts of methyl acetate, 5-10 parts of titanium dioxide, 2-5 parts of metal silver powder, 5-8 parts of sodium carboxymethyl cellulose, 6-11 parts of tin oxide, 4-8 parts of propylene glycol butyl ether, 12-17 parts of nano-zirconia sol, 5-8 parts of sodium amide, 4-8 parts of zinc acetate dihydrate, 2-5 parts of chitosan, 2-5 parts of fluoroethylene carbonate, 0.1-1 part of copper selenate, 0.1-1 part of acrylic resin film-forming agent, and 0.1-1 part of antioxidant. The anti-fog film can significantly reduce the haze, effectively improve light transmittance, has wide application, and has a better social value; and meanwhile, the preparation method of the anti-fog filmis simple, and is low in process conditions, so that realization of industrial production is facilitated.

Description

technical field [0001] The invention relates to a plastic material, in particular to an anti-fog film and a preparation method thereof. Background technique [0002] Mirrors (English glasses) are commonly used daily necessities in people's daily life. There are two types of mirrors: flat mirrors and curved mirrors. Flat mirrors are often used by people to organize their appearance. Curved mirrors are also divided into concave mirrors and convex mirrors. Mirrors, furniture accessories, architectural decorations, optical instrument components and solar cookers, reflectors for car lights and searchlights, reflecting telescopes, car rearview mirrors, etc. Traditional flat mirrors are prone to fogging, which seriously affects people's use experience. Although there is a device for heating and drying the mirror to remove water mist, further operations such as wiping are required, which is very troublesome. Therefore, the present invention provides an anti-fog film and a preparati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L1/28C08L5/08C08L33/00C08K13/02C08K3/22C08K5/109C08K3/08C08J5/18
Inventor 张强
Owner ZHENGZHOU CHENGHE INFORMATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap