A model building method for wood softening effect after hydrothermal-microwave combined softening treatment

A technology of softening treatment and construction method, which is applied in the direction of radiation/wave wood treatment, wood heating, wood treatment, etc., and can solve the problems of different softening conditions and inapplicability

Active Publication Date: 2021-04-20
SOUTHWEST FORESTRY UNIVERSITY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, different tree species have different softening conditions due to the different chemical components and structures of their cell walls. That is, a kind of wood in an experiment corresponds to a specific softening treatment process, and the process conditions of a certain wood softening obtained through the experiment may be It cannot be applied to the softening of other woods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A model building method for wood softening effect after hydrothermal-microwave combined softening treatment
  • A model building method for wood softening effect after hydrothermal-microwave combined softening treatment
  • A model building method for wood softening effect after hydrothermal-microwave combined softening treatment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Experimental materials and methods:

[0037] A Hydrothermal softening treatment:

[0038] 1) Sample tree species: white wood, artificial forest teak, Chinese toon, natural forest teak, water Qinggang; different densities of wood have white wood ( Aquilaria sinensis ) (air dry density 0.40g / cm 3 ), plantation teak ( Tectona grandis ) (air dry density 0.50g / cm 3 ), Toon ( Toona sinensis ) (air dry density 0.60g / cm 3 ), natural forest teak (air dry density 0.70g / cm 3 ), Shuiqinggang ( Fagus longipetiolata ) (air dry density 0.80g / cm 3 );

[0039] 2) Sample size: the length direction, that is, the axial direction of the wood sample is 30 mm, the width direction, that is, the chord direction of the wood sample is 20 mm, and the thickness direction, that is, the radial direction of the wood sample is 20 mm.

[0040] 3) Wood initial moisture content: 10%

[0041] 4) Absolute pressure: 0.01-0.02MPa

[0042] 5) Treatment temperature: 90~120℃, treatment time 120~24...

Embodiment 2

[0076] A method for building a model of wood softening effect after hydrothermal-microwave joint softening treatment, comprising the following specific steps:

[0077] A. Hydrothermal softening treatment: for different densities x 1 (0.2-1.0 g / cm 3 ) wood undergoes hydrothermal softening treatment, the temperature of the hydrothermal softening treatment is x 2 (70-150°C), water heating time is x 3 (80-200min) to obtain wood softened by hydrothermal treatment; the size of the wood is 30mm in the axial direction, 10mm in the chord direction, and 10mm in the radial direction;

[0078] B, get the wood processed through step A, use 2 layers of polyvinyl chloride film to wrap the wood, and then carry out microwave softening treatment, the power of the microwave softening treatment is x 4 (400-800 W), microwave time is x 5 (1-6min), to obtain the wood after combined softening treatment by hydrothermal-microwave;

[0079] C, model building: carry out transverse compression t...

Embodiment 3

[0087] A method for building a model of wood softening effect after hydrothermal-microwave joint softening treatment, comprising the following specific steps:

[0088] A. Hydrothermal softening treatment: for different densities x 1 (0.2-1.0 g / cm 3 ) wood undergoes hydrothermal softening treatment, the temperature of the hydrothermal softening treatment is x 2 (70-150°C), water heating time is x 3 (80-200min) to obtain wood softened by hydrothermal treatment; the size of the wood is 3mm in the axial direction, 30mm in the chord direction, and 30mm in the radial direction;

[0089] B, get the timber processed through step A, adopt 10 layers of polyvinyl chloride film to wrap the timber, then carry out microwave softening treatment, the power of described microwave softening treatment is x 4 (400-800 W), microwave time is x 5 (1-6min), to obtain the wood after combined softening treatment by hydrothermal-microwave;

[0090] C, model building: carry out transverse compr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wood softening effect after combined hydrothermal-microwave softening treatment y (i.e.: axial maximum compressibility y 1 and lateral maximum compression ratio y 2 ) model building method. Described method comprises the following steps: first is to different densities x 1 The wood is hydrothermally softened (at different temperatures x 2 ,Different time x 3 conditions); followed by microwave softening treatment (in different power x 4 ,Different time x 5 conditions); Finally, a mathematical model for quantitative control of wood softening effect after hydrothermal-microwave softening combined softening treatment was constructed, and y 1 = f ( x 1 , x 2 , x 3 , x 4 , x 5 ), y 2 = f ( x 1 , x 2 , x 3 , x 4 , x 5 ). The method can realize quantitative control of wood softening effect after hydrothermal-microwave combined softening treatment, has good controllability, high accuracy and wide application.

Description

technical field [0001] The invention belongs to the technical field of quantitative regulation and control of wood softening effect, and in particular relates to a model construction method for wood softening effect after combined hydrothermal-microwave softening treatment. Background technique [0002] The softening process is very important, whether it is compressing the wood laterally to increase its density or longitudinally compressing it to wrinkle it to increase its lateral bending. For the softening of wood, the current treatment methods mainly include physical methods (such as: boiling, steaming, microwave, high-frequency medium heating treatment) and chemical methods (such as: liquid ammonia, gaseous ammonia, ammonia water, hydrazine, urea and alkali processing, etc.) two types (Song Kuiyan, 2006). Normally, wood is essentially in a glassy state without softening. In order to ensure that the wood is compressed and compacted without major microscopic damage, it is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G06F30/20B27K5/00B27K5/06G06F119/08G06F119/18
CPCB27K5/001B27K5/0055B27K5/06G06F30/20G06F2119/08G06F2119/18
Inventor 杨燕邱坚沈华杰王云龙王宪李有贵
Owner SOUTHWEST FORESTRY UNIVERSITY