Environment-friendly self-curing epoxy resin adhesive and preparation method thereof

A technology of epoxy resin glue and epoxy resin, which is applied in the direction of adhesives, adhesive additives, non-macromolecular organic compound adhesives, etc., to achieve the effects of simple preparation method, improved bonding strength, and simple operation

Inactive Publication Date: 2018-04-20
BEIJING JUNXIU CONSULTATION CO LTD
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, from the research results, it can be seen that starch-based adhesives are used in wood-based panels,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The adhesive components include 30 parts by weight of fluorine rubber, 10 parts of modified epoxy resin, 10 parts of perchlorethylene resin, 5 parts of polyvinyl alcohol, 4 parts of methyl cellulose, 8 parts of percarbamide, hydrogen 4 parts of potassium oxide, 5 parts of epichlorohydrin, 4 parts of methacrylic acid, 8 parts of carnation extract, 4 parts of turpentine.

[0016] The preparation method of the present embodiment comprises and favorite steps:

[0017] A. After mixing perchlorethylene resin, polyvinyl alcohol, methyl cellulose, percarbamide, potassium hydroxide, epichlorohydrin, and methacrylic acid, add it to a stirring tank and stir at a low speed to obtain a mixture A;

[0018] B. Add carnation extract and turpentine in sequence to mixture A, stir continuously during the addition, and then place it at room temperature for 10 minutes to obtain mixture B;

[0019] C. Add fluororubber and modified epoxy resin to the mixture B, mix and knead in a kneader at ...

Embodiment 2

[0022] The adhesive components include 50 parts by weight of fluororubber, 20 parts of modified epoxy resin, 20 parts of perchlorethylene resin, 15 parts of polyvinyl alcohol, 12 parts of methyl cellulose, 14 parts of percarbamide, hydrogen Potassium oxide 12 parts, epichlorohydrin 10 parts, methacrylic acid 12 parts, carnation extract 20 parts, turpentine 10 parts.

[0023] The preparation method of the present embodiment comprises and favorite steps:

[0024] A. After mixing perchlorethylene resin, polyvinyl alcohol, methyl cellulose, percarbamide, potassium hydroxide, epichlorohydrin, and methacrylic acid, add it to a stirring tank and stir at a low speed to obtain a mixture A;

[0025] B. Add carnation extract and turpentine in sequence to mixture A, stir continuously during the addition, and then place it at room temperature for 10 minutes to obtain mixture B;

[0026] C. Add fluororubber and modified epoxy resin to the mixture B, mix and knead in a kneader at a temperat...

Embodiment 3

[0029] The adhesive components include 35 parts by weight of fluorine rubber, 12 parts of modified epoxy resin, 12 parts of perchlorethylene resin, 7 parts of polyvinyl alcohol, 6 parts of methyl cellulose, 9 parts of percarbamide, hydrogen Potassium oxide 6 parts, epichlorohydrin 6 parts, methacrylic acid 5 parts, carnation extract 10 parts, turpentine 5 parts.

[0030] The preparation method of the present embodiment comprises and favorite steps:

[0031] A. After mixing perchlorethylene resin, polyvinyl alcohol, methyl cellulose, percarbamide, potassium hydroxide, epichlorohydrin, and methacrylic acid, add it to a stirring tank and stir at a low speed to obtain a mixture A;

[0032] B. Add carnation extract and turpentine in sequence to mixture A, stir continuously during the addition, and then place it at room temperature for 10 minutes to obtain mixture B;

[0033] C. Add fluororubber and modified epoxy resin to the mixture B, mix and knead in a kneader at a temperature ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Bonding strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses an environment-friendly self-curing epoxy resin adhesive and a preparation method thereof. The adhesive is prepared from the following components in parts by weight: 30 to 50 parts of fluororubber, 10 to 20 parts of modified epoxide resin, 10 to 20 parts of perchloro-ethylene resin, 5 to 15 parts of polyvinyl alcohol, 4 to 12 parts of methylcellulose, 8 to 14 parts of percarbamide, 4 to 12 parts of potassium hydroxide, 5 to 10 parts of epoxy chloropropane, 4 to 12 parts of methacrylic acid, 8 to 20 parts of dianthus chinensis extracting solution and 4 to 10 parts of turpentine. The preparation method disclosed by the invention is simple; the preparation process is environment-friendly and pollution-free; the prepared adhesive has the advantages of oil resistance, good corrosion resistance, high adhesion as well as no toxicity and no irritating odor.

Description

technical field [0001] The invention relates to the technical field of adhesive preparation, in particular to an environment-friendly self-curing epoxy resin adhesive and a preparation method thereof. Background technique [0002] At present, the adhesives used in the wood-based panel manufacturing industry at home and abroad are mainly urea-formaldehyde resin, phenolic resin, melamine-formaldehyde resin, etc. This type of adhesive has a high content of free formaldehyde, and slowly releases toxic formaldehyde gas during use, causing harm to the human body. In order to reduce the emission of formaldehyde gas, the domestic research idea is to improve the original technical route of synthesizing urea-formaldehyde resin in an attempt to reduce the content of free formaldehyde. Such as adding formaldehyde capture agents such as urea and melamine; on the other hand, trying to use cheap biomass polyhydroxy compounds as raw materials to prepare wood adhesives to replace formaldehy...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J4/06C09J4/02C09J11/04C09J11/06C09J11/08
CPCC09J4/06C09J11/04C09J11/06C09J11/08
Inventor 张婕
Owner BEIJING JUNXIU CONSULTATION CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap