Preparation method of filaments for weather-resistant plastic woven bags

A plastic woven bag, weather-resistant technology, applied in the direction of conjugated synthetic polymer man-made filament, etc., can solve the problems of aging, short service life, poor weather resistance and other problems of woven bags, and achieve good oxidation resistance, sun resistance, physical properties Maintaining good, improving physical properties

Inactive Publication Date: 2018-05-01
太和县亚美达塑业有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Plastic woven bags are divided into polypropylene bags and polyethylene bags according to the main material composition. The production process is to use plastic raw materials to extrude film, cut, and unidirectionally stretch into flat wire, and then weave warp and weft to obtain the product, which is generally called a woven bag. The packaging bag made of polypropylene flat wire produced by traditional technology has poor weather resistance. Problems such as hardening, brittleness, peeling, peeling, and fracture are prone to occur in winter in the north. In the south, due to high temperature, strong light, and strong ultraviolet penetration in summer, it is easy to cause aging, corrosion, poor toughness, and low strength of woven bags. Short lifespan and other issues waste resources and pollute the environment, so it is necessary to study how to improve the weather resistance of plastic woven bag materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A preparation method for weather-resistant plastic woven bag silk, comprising the following steps:

[0014] (1) Preparation of raw materials, in parts by weight, including 52 parts of polypropylene, 10 parts of ultra-high molecular weight polyethylene, 3 parts of low molecular weight polyethylene, 3 parts of silane grafted polyethylene, 8 parts of wollastonite powder, carboxymethyl shell Polysaccharide 1.5 parts, microcrystalline cellulose 2 parts, zinc thiophosphate 0.3 parts, methyl methacrylate 8 parts, bis-imidazolidinyl urea 0.4 parts, cedar wood oil 0.5 parts, cross-linking agent 0.2 parts, antioxidant 0.1 parts , 3 parts of diluent;

[0015] (2) The wollastonite powder and carboxymethyl chitosan are mixed and dispersed in ethanol equivalent to 5 times its total weight, and then ultrasonically treated for 15 minutes at an ultrasonic frequency of 26kHz and a temperature of 55°C, and the treatment is completed After standing still for 5 hours, the mixed solution wa...

Embodiment 2

[0020] A preparation method for weather-resistant plastic woven bag silk, comprising the following steps:

[0021] (1) Preparation of raw materials, in parts by weight, including 48 parts of polypropylene, 12 parts of ultra-high molecular weight polyethylene, 1 part of low molecular weight polyethylene, 4 parts of silane grafted polyethylene, 6 parts of wollastonite powder, carboxymethyl shell 1 part of polysaccharide, 1.7 parts of microcrystalline cellulose, 0.2 part of zinc thiophosphate, 10 parts of methyl methacrylate, 0.2 part of bis-imidazolidinyl urea, 0.8 part of cedarwood oil, 0.1 part of cross-linking agent, 0.12 part of antioxidant , 4 parts of diluent;

[0022] (2) The wollastonite powder and carboxymethyl chitosan are mixed and dispersed in ethanol equivalent to 5 times its total weight, and then ultrasonically treated for 10 minutes at an ultrasonic frequency of 28kHz and a temperature of 52°C, and the treatment is completed After standing still for 6 hours, the...

Embodiment 3

[0027] A preparation method for weather-resistant plastic woven bag silk, comprising the following steps:

[0028] (1) Preparation of raw materials, in parts by weight, including 56 parts of polypropylene, 8 parts of ultra-high molecular weight polyethylene, 5 parts of low molecular weight polyethylene, 2 parts of silane grafted polyethylene, 10 parts of wollastonite powder, carboxymethyl shell 2 parts of polysaccharides, 2.4 parts of microcrystalline cellulose, 0.4 parts of zinc thiophosphate, 6 parts of methyl methacrylate, 0.6 parts of bis-imidazolidinyl urea, 0.2 parts of cedarwood oil, 0.3 parts of cross-linking agent, 0.08 parts of antioxidant , 2 parts of diluent;

[0029] (2) The wollastonite powder and carboxymethyl chitosan are mixed and dispersed in ethanol equivalent to 5 times the total weight, and then ultrasonically treated for 20 minutes at an ultrasonic frequency of 24kHz and a temperature of 58°C, and the treatment is completed After standing still for 4 hou...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of materials for plastic woven bags, and in particular relates to a preparation method of filaments for weather-resistant plastic woven bags. The method comprises the steps of preparing raw materials, preparing mixed powder, carrying out melt filtration on the raw materials, extruding to obtain a film, cooling with water, splitting into filaments, drawing the filaments and winding. Compared with the prior art, the preparation method provided by the invention has the advantages that the physical properties of the obtained woven bags can be better improved by proportioning the raw materials with different molecular weights; the compatibility of the materials can be improved due to the use of silane-grafted polyethylene; wollastonite powder is processed, and other raw materials are cooperatively used, so that the weather resistance of the material can be improved; in outdoor atmospheric exposure tests, the physical properties are maintained well; the plastic woven bags made by using the filaments have better oxidation resistance and anti-sunburn property, and are solid, durable and long in service life.

Description

technical field [0001] The invention belongs to the technical field of plastic woven bag materials, and in particular relates to a method for preparing weather-resistant plastic woven bag silk. Background technique [0002] Plastic woven bags are divided into polypropylene bags and polyethylene bags according to the main material composition. The production process is to use plastic raw materials to extrude film, cut, and unidirectionally stretch into flat wire, and then weave warp and weft to obtain the product, which is generally called a woven bag. The packaging bag made of polypropylene flat wire produced by traditional technology has poor weather resistance. Problems such as hardening, brittleness, peeling, peeling, and fracture are prone to occur in winter in the north. In the south, due to high temperature, strong light, and strong ultraviolet penetration in summer, it is easy to cause aging, corrosion, poor toughness, and low strength of woven bags. Problems such as...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/06C08L51/06C08K9/04C08K3/34D01F8/06D01F1/10
CPCC08L23/12C08L2201/08C08L2205/025C08L2205/035C08L2207/068D01F1/10D01F8/06C08L23/06C08L51/06C08K9/08C08K3/34
Inventor 曾原明屈蒙蒙
Owner 太和县亚美达塑业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com