A technology of corrugated cardboard and glue, applied in the direction of adhesives, non-polymer adhesive additives, adhesive additives, etc., can solve the problems of temperature and composition, adhesive heating and melting, and unstable performance. Achieve good curing speed, good bond strength and low cost

Inactive Publication Date: 2018-05-01
天长市天翔包装有限公司
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the adhesive for corrugated cardboard usually uses starch as raw material. Starch adhesive has a wide range of sources, is non-toxic, non-polluting, and low in cost, but is greatly affected by temperature and composition, and its performance is unstable.
The use environment of corrugated cardboard is changeable. When corrugated cardboard is used for a certain period and needs to be recycled, it is often necessary to heat and melt the adhesive. The organic solvents and chemical substances contained in it will cause serious environmental pollution after being discharged.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0018] A degradable corrugated cardboard glue, comprising the following raw materials in parts by weight: 55 parts of cornstarch, 14 parts of polyvinyl alcohol resin, 12 parts of ethanol, 0.3 parts of caustic soda, 2 parts of polyethylene glycol, and emulsion polysiloxanes 0.4 parts of defoamer, 0.3 parts of di-n-butyltin monooctyl dimaleate stabilizer, 0.06 parts of plasticizer epoxy soybean oil, 0.18 parts of borax, 0.005 parts of n-butyl titanate, triphenyl phosphite 0.006 parts, 135 parts of water.

[0019] The preparation process of the degradable corrugated cardboard glue comprises the following steps:

[0020] (1) Add polyvinyl alcohol resin, ethanol, n-butyl titanate, and triphenyl phosphite into the reaction kettle, raise the temperature to 160°C, and carry out the degradation reaction until the sample is transparent at room temperature to stop the reaction, and the reactants naturally drop to room temperature;

[0021] (2) Add cornstarch into water, slowly add caus...

Embodiment 2

[0024] A degradable corrugated cardboard glue, comprising the following raw materials in parts by weight: 50 parts of corn starch, 18 parts of polyvinyl alcohol resin, 13 parts of ethanol, 0.2 parts of caustic soda, 2 parts of polyethylene glycol, polyether modified silicone 0.4 parts of defoamer, 0.3 parts of monooctyl dimaleic acid stabilizer, 0.3 parts of di-n-octyl tin, 0.05 parts of plasticizer epoxy butyl furfurate, 0.24 parts of borax, 0.006 parts of n-butyl titanate, triphosphite 0.006 parts of phenyl ester, 125 parts of water.

[0025] The preparation process of the degradable corrugated cardboard glue comprises the following steps:

[0026] (1) Add polyvinyl alcohol resin, ethanol, n-butyl titanate, and triphenyl phosphite into the reaction kettle, raise the temperature to 170°C, and carry out the degradation reaction until the sample is transparent at room temperature to stop the reaction, and the reactants naturally drop to room temperature;

[0027] (2) Add corn...

Embodiment 3

[0030] A degradable corrugated cardboard glue, comprising the following raw materials in parts by weight: 55 parts of cornstarch, 20 parts of polyvinyl alcohol resin, 12 parts of ethanol, 0.5 parts of caustic soda, 4 parts of polyethylene glycol, and emulsion polysiloxanes 0.6 parts of defoamer, 0.5 parts of dibutyltin dilaurate as a stabilizer, 0.07 parts of epoxy octyl soybean oil as a plasticizer, 0.23 parts of borax, 0.007 parts of n-butyl titanate, 0.008 parts of triphenyl phosphite, and 140 parts of water share.

[0031] The preparation process of the degradable corrugated cardboard glue comprises the following steps:

[0032] (1) Add polyvinyl alcohol resin, ethanol, n-butyl titanate, and triphenyl phosphite into the reaction kettle, raise the temperature to 180°C, and carry out the degradation reaction until the sample is transparent at room temperature to stop the reaction, and the reactants naturally drop to room temperature;

[0033] (2) Add cornstarch into water,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses degradable corrugated paperboard glue and a preparation process thereof and relates to the technical field of corrugated paperboard glue. The corrugated paperboard glue comprises the following raw materials in parts by weight: 40-60 parts of corn starch, 10-20 parts of polyvinyl alcohol resin, 5-15 parts of ethyl alcohol, 0.2-0.6 part of caustic soda flakes, 1-4 parts of polyethylene glycol, 0.2-0.6 part of defoaming agent, 0.1-0.5 part of stabilizer, 0.02-0.08 part of plasticizer, 0.05-0.3 part of borax, 0.002-0.008 part of titanium tetrabutoxide, 0.005-0.01 part of triphenyl phosphate and 80-150 parts of water; and the preparation process comprises the steps: degrading the polyvinyl alcohol resin; and mixing the materials. The corrugated paperboard glue disclosedby the invention is high in curing speed, bonding strength and degradation rate and incapable of generating environment pollution.

Description

Technical field: [0001] The invention relates to the technical field of corrugated cardboard glue, in particular to a degradable corrugated cardboard glue and a preparation process thereof. Background technique: [0002] Corrugated cardboard, also known as corrugated cardboard, is made of at least one layer of corrugated paper and one layer of cardboard paper. It has good elasticity and extensibility. It is mainly used to make cartons, the sandwich of cartons and other packaging materials for fragile goods. [0003] At present, adhesives for corrugated cardboard usually use starch as raw material. Starch adhesives have a wide range of sources, are non-toxic, non-polluting, and low in cost, but are greatly affected by temperature and composition, and their performance is unstable. The use environment of corrugated cardboard is changeable. When corrugated cardboard is used for a certain period and needs to be recycled, it is often necessary to heat and melt the adhesive. The o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J4/06C09J11/04C09J11/06
CPCC09J4/06C09J11/04C09J11/06
Inventor 侯正云徐乐高
Owner 天长市天翔包装有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap