Environment-friendly adhesive special for compound cleaning foam cotton and preparation method thereof

A technology for cleaning foam and adhesives, which is applied in the field of adhesive production for bonding melamine foams, can solve the problems of energy waste, air pollution, and high energy consumption, and achieve improved preparation efficiency, good energy saving and environmental protection, and production high efficiency effect

Inactive Publication Date: 2018-05-04
郑州峰泰纳米材料有限公司
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the adhesives currently used for bonding melamine foams are relatively hard after drying, so that there are obvious boundary layers between different melamine foam bonding layers, and the hand feeling is not good when used; Volatile harmful substances will pollute the air during the production process of the agent, and the production process takes a long time, consumes high energy, and wastes energy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] An environmentally friendly adhesive for composite cleaning foam cotton, including the following raw materials: 16 parts of ring-opening phenolic oligomers, 40 parts of formaldehyde, 1.6 parts of potassium hydroxide, 6 parts of polyethylene glycol, 8 parts of silane coupling agent, 4 parts of silicon dioxide, 10 parts of polyvinyl alcohol, 20 parts of silica sol, and 1 part of water-soluble silicone oil emulsion.

[0019] The preparation method of the special environment-friendly adhesive for the composite cleaning foam cotton comprises the following steps:

[0020] S1. Take silicon dioxide and add it to polyethylene glycol solution, ultrasonically disperse it for 3 minutes, heat it in a microwave oven to 85°C, dry it, and grind it to obtain modified silicon dioxide;

[0021] S2. Take ring-opening phenolic oligomer and potassium hydroxide and add them to the reactor, heat to 70°C, stir for 5 minutes, add formaldehyde solution, continue stirring for 20 minutes, add polyv...

Embodiment 2

[0025] An environmentally friendly adhesive for composite cleaning foam cotton, comprising the following raw materials: 25 parts of ring-opening phenolic oligomers, 63 parts of formaldehyde, 3 parts of potassium hydroxide, 15 parts of polyethylene glycol, 30 parts of silane coupling agent, 25 parts of silicon dioxide, 40 parts of polyvinyl alcohol, 55 parts of silica sol, and 4 parts of water-soluble silicone oil emulsion.

[0026] The preparation method of the special environment-friendly adhesive for the composite cleaning foam cotton comprises the following steps:

[0027] S1. Take silicon dioxide and add it to polyethylene glycol solution, disperse it by ultrasonic wave for 5 minutes, heat it in a microwave oven to 85°C, dry it, and grind it to obtain modified silicon dioxide;

[0028] S2. Take ring-opening phenolic oligomer and potassium hydroxide and add them to the reactor, heat to 70°C, stir for 5 minutes, add formaldehyde solution, continue stirring for 20 minutes, ad...

Embodiment 3

[0032] An environmentally friendly adhesive for composite cleaning foam cotton, comprising the following raw materials: 18 parts of ring-opening phenolic oligomers, 45 parts of formaldehyde, 1.8 parts of potassium hydroxide, 13 parts of polyethylene glycol, 20 parts of silane coupling agent, 15 parts of silicon dioxide, 15 parts of polyvinyl alcohol, 35 parts of silica sol, and 2 parts of water-soluble silicone oil emulsion.

[0033] The preparation method of the special environment-friendly adhesive for the composite cleaning foam cotton comprises the following steps:

[0034] S1. Take silicon dioxide and add it to polyethylene glycol solution, ultrasonically disperse it for 4 minutes, heat it in a microwave oven to 85°C, dry it, and grind it to obtain modified silicon dioxide;

[0035] S2. Take ring-opening phenolic oligomer and potassium hydroxide and add them to the reactor, heat to 70°C, stir for 5 minutes, add formaldehyde solution, continue stirring for 20 minutes, add ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an environment-friendly adhesive special for compound cleaning foam cotton. The environment-friendly adhesive is prepared from the following raw materials: 16 to 25 parts of ring-opened phenolic oligomers, 40 to 63 parts of formaldehyde, 1.6 to 3 parts of potassium hydroxide, 6 to 15 parts of polyethylene glycol, 8 to 30 parts of silane coupling agent, 4 to 25 parts of silica, 10 to 40 parts of polyvinyl alcohol, 20 to 55 parts of silica sol, and 1 to 4 parts of water-soluble silicone oil emulsion; a preparation method comprises the following steps that firstly, the ring-opened phenolic oligomers and the potassium hydroxide are mixed under a working condition of 70 DEG C, stirred for 5 min, a formaldehyde solution is added and stirred for 20 min, after adding the polyethylene glycol, the silica sol and the water-soluble silicone oil emulsion, a phenolic resin is prepared. Then the silica modified by polyethylene glycol is added into the phenolic resin, and thesilane coupling agent is added to prepare a nano-silica phenolic resin adhesive; the environment-friendly adhesive special for the compound cleaning foam cotton has the advantages of strong adhesive force, energy saving and environmental protection, and high production efficiency.

Description

technical field [0001] The invention belongs to the technical field of production of adhesives for bonding melamine foams, and in particular relates to an environment-friendly adhesive special for composite cleaning foam cotton and a preparation method thereof. Background technique [0002] Melamine foam is a sponge with good sound-absorbing, heat-insulating and cleaning effects prepared by the cross-linking reaction of melamine and formaldehyde solution, and is widely used in sound insulation of high-speed trains and environmental cleaning. Due to its wide range of applications, and because there are more and more types of derivatives made of melamine foam, in recent years, in order to realize the multifunctionality of melamine foam monomers, different melamine resins have been prepared by modifying melamine resins. The melamine foam with different performance is used, and then the melamine foam with different performance is bonded into a single monomer through adhesives to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J161/06C09J129/04C09J11/04C09J11/06C09J11/08
CPCC08K2201/014C08L2205/03C09J11/04C09J11/06C09J11/08C09J129/04C09J161/06C08L29/04C08L83/04C08K5/54C08K9/08C08K3/36C08L61/06Y02P20/10
Inventor 李洋洋
Owner 郑州峰泰纳米材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com