Titanium zirconium conversion liquid applied to surface of 2024 aluminum alloy and using method thereof

A technology of aluminum alloy surface and conversion liquid, which is applied in the coating process of metal materials, etc., can solve the problems of poor corrosion resistance and achieve excellent salt spray resistance and excellent storage stability

Inactive Publication Date: 2018-05-25
INST OF METAL RESEARCH - CHINESE ACAD OF SCI
View PDF4 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the technical shortcomings and deficiencies of the conversion coating on the surface of the 2024 aluminum alloy, a titanium-zirconium conversion solution applied to the surface of the 2024 aluminum alloy and its application method are provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] First, the sample is prepared, the aluminum alloy is polished, then alkali washed, then washed with a large amount of water, then pickled, and then washed with a large amount of water.

[0038] The grinding method is to mechanically polish the surface of the aluminum alloy step by step with 400#, 600#, 800# and 1200# sandpaper, then wash it with deionized water, dry it, and set it aside;

[0039] Alkaline lotion is made by mixing sodium hydroxide, sodium carbonate, sodium silicate, OP-10 emulsifier and water. The content of each component is as follows: sodium hydroxide 20g / L; sodium carbonate 20g / L; sodium silicate 5g / L; OP-10 emulsifier 1g / L; the rest is water.

[0040] The pickling solution is mixed with hydrochloric acid, nitric acid, hydrofluoric acid, sulfuric acid and water. The content of each component is as follows: hydrochloric acid 100g / L; nitric acid 10g / L; hydrofluoric acid 10g / L; sulfuric acid 60g / L; water.

[0041] The preparation method of the presen...

Embodiment 2

[0045] First, the sample is prepared, the aluminum alloy is polished, then alkali washed, then washed with a large amount of water, then pickled, and then washed with a large amount of water.

[0046] The grinding method is to mechanically polish the surface of the aluminum alloy step by step with 400#, 600#, 800# and 1200# sandpaper, then wash it with deionized water, dry it, and set it aside;

[0047] Alkaline lotion is made by mixing sodium hydroxide, sodium carbonate, sodium silicate, OP-10 emulsifier and water. The content of each component is as follows: sodium hydroxide 25g / L; sodium carbonate 30g / L; sodium silicate 10g / L; OP-10 emulsifier 2g / L; the rest is water.

[0048] The pickling liquid is mixed by hydrochloric acid, nitric acid, hydrofluoric acid, sulfuric acid and water, and the content of each component is as follows: hydrochloric acid 120g / L; nitric acid 15g / L; hydrofluoric acid 8g / L; sulfuric acid 50g / L; water.

[0049] The preparation method of the presen...

Embodiment 3

[0053] First, the sample is prepared, the aluminum alloy is polished, then alkali washed, then washed with a large amount of water, then pickled, and then washed with a large amount of water.

[0054] The grinding method is to mechanically polish the surface of the aluminum alloy step by step with 400#, 600#, 800# and 1200# sandpaper, then wash it with deionized water, dry it, and set it aside;

[0055] Alkaline lotion is made by mixing sodium hydroxide, sodium carbonate, sodium silicate, OP-10 emulsifier and water. The content of each component is as follows: sodium hydroxide 15g / L; sodium carbonate 25g / L; sodium silicate 15g / L; OP-10 emulsifier 1g / L; the rest is water.

[0056] The pickling liquid is mixed with hydrochloric acid, nitric acid, hydrofluoric acid, sulfuric acid and water, and the content of each component is as follows: hydrochloric acid 90g / L; nitric acid 10g / L; hydrofluoric acid 12g / L; sulfuric acid 70g / L; water.

[0057] The preparation method of the pres...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of aluminum alloy surface environment-friendly protection, in particular to titanium zirconium conversion liquid applied to the surface of a 2024 aluminum alloy anda using method thereof. The titanium zirconium conversion liquid comprises the following components including, by content, 3-15 g/L of fluorine titanic acid, 1-10 g/L of fluorine zirconium acid, 0.1-5g/L of accelerant, 0.1-4 g/L of corrosion inhibitor, 0.5-8 g/L of oxidizing agent, 0.01-1 g/L of pH modifier and the balance deionized water. The titanium zirconium conversion liquid applied to the surface of the 2024 aluminum alloy does not contain hexavalent chromium, lead, mercury and cadmium heavy metal ion compounds, does not contain volatile poisonous solvent like benzene and xylene, meetsthe requirement of environmental protection, and is simple in technology, industrialization is formed easily, and a conversion film has an excellent corrosion-resisting property.

Description

technical field [0001] The invention relates to the field of environmental protection and protection of the surface of aluminum alloys, in particular to a titanium-zirconium conversion solution applied to the surface of 2024 aluminum alloys and a use method thereof. Background technique [0002] Aluminum alloy has the characteristics of light weight, high specific strength, high thermal conductivity, and good heat dissipation performance. It is widely used in aerospace, chemical industry, transportation and other fields. However, the chemical activity of aluminum and its alloys is high, and a thin oxide film can be formed on the surface in the atmospheric environment. This spontaneously formed oxide film is easily destroyed, especially in the environment of chloride ions. Corrosion, in order to overcome the shortcomings of aluminum alloy surface properties, expand its application range, and prolong its service life, aluminum alloy surface protection is very important. [00...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C22/34C23C22/44C23C22/36C23G1/22C23G1/12
Inventor 李庆鹏张博赵焕刘建国严川伟
Owner INST OF METAL RESEARCH - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap