Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Aluminum alloy round ingot casting for computer hard disk drive arm and production method of ingot casting

A technology of a computer hard disk and a production method, which is applied in the field of producing aluminum alloy round ingots for driving arms of computer hard disks, can solve the problems of stable production and can not be produced, and achieves the effects of being beneficial to degassing, dense organization and improving casting speed

Inactive Publication Date: 2018-05-29
HENAN ZHONGFU ALUMINUM ALLOY
View PDF14 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This product is mainly effectively controlled from the aspects of mechanical properties, metallography and cleanliness of the material, and there are many types of control alloys and are relatively strict, which is the reason why many manufacturers are difficult to produce stably or cannot produce

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0048] Embodiment: a kind of aluminum alloy round casting ingot for computer hard disk drive arm, its composition is by weight percent: silicon Si0.60~0.80%, iron Fe 0.10~0.20%, magnesium Mg 0.90~1.1%, copper Cu 0.10~ 0.30%, manganese Mn 0.10~0.20%, chromium Cr 0.10~0.30%, other single impurity content <0.03%, and the balance is aluminum Al.

[0049] The above-mentioned production method of aluminum alloy round ingot for computer hard drive arm, its concrete technological process is as follows:

[0050]A. First add 15-18 tons of solid cold material of pure aluminum ingots, and then add electrolytic aluminum liquid for batching, wherein electrolytic aluminum liquid accounts for 70-75% of the total batching weight, and pure aluminum ingot solid cold feed accounts for the total batching weight part 25-30% of the iron content in the electrolytic aluminum liquid is 0.10%-0.020% Fe, and at the same time, turn on the electromagnetic stirrer for 40 minutes to melt the solid cold mater...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
purityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an aluminum alloy round ingot casting for a computer hard disk drive arm. The ingot casting comprises 0.60 to 0.80% of Si, 0.10 to 0.20% of Fe, 0.90 to 1.1% of Mg, 0.10 to 0.30% of Cu, 0.10 to 0.20% of Mn, 0.10 to 0.30% of Cr, smaller than 0.03% of single impurities and the balance Al. The production method comprises the steps that pure aluminum ingot solid cold charge andelectrolytic aluminum liquid are burdened, heating and melting are carried out at the proper temperature, an electromagnetic stirrer is started to rapidly melt the cold charge, temperature uniformityand component uniformity are kept, according to the chemical components in aluminum melt, alloying treatment is carried out, slagging-off is carried out to kept melt clean, high-purity N2 and a refined powder spraying agent are adopted to carry out powder spraying refining, online filtering, slag removal and gas removal are achieved, and through casting production and uniform heating treatment, the aluminum alloy round ingot casting meeting the requirement is produced. The ingot casting is stable and uniform in component, compact in internal structure, smooth and clean in surface, excellent inmechanical performance, and high in product interior cleanness, and the method is an optimal method for producing the aluminum alloy round ingot casting for the computer hard disk drive arm.

Description

1. Technical field: [0001] The invention relates to an aluminum alloy round ingot for a computer hard disk drive arm and a production method thereof, which are used for producing an aluminum alloy round ingot for a computer hard disk drive arm. 2. Background technology: [0002] Aluminum alloy round ingot is the main basic material for the production of computer hard disk drive arm materials. It is cast into a round ingot by alloy composition ratio, after soaking treatment, and then processed by heat treatment, extrusion, quenching and other processes. [0003] After the original aluminum alloy is rolled into a round aluminum rod, it is formed by re-drawing, heat treatment, stranding, wrapping and other processes. The main requirements are that the tensile strength is ≥165Mpa, the resistivity is ≤28.64n.Ω.m, and the residual strength rate is ≥90. %, the surface requires no pores, trachoma, flash, inclusions and other defects. [0004] The main function of the computer hard ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/08C22C1/03C22C1/06
CPCC22C21/08C22C1/026C22C1/03C22C1/06
Inventor 赵文龙司旭鹏李海峰吴慕天王辉敏赵蕾张涛锋巴振伟
Owner HENAN ZHONGFU ALUMINUM ALLOY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products