Polypropylene shielding material

A shielding material, polypropylene technology, applied in the field of materials, can solve the problems of reduced stability, easy aging of materials, low service life, etc., to achieve the effects of improving compatibility, improving mechanical stability and strength, and expanding the scope of application

Inactive Publication Date: 2018-06-01
王家浩
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is widely used in the industry and is one of the common polymer materials. It can be used in various products or applications. These products or applications include films, fibers, moldings, pipes and other products. These materials are exposed to high-energy radiation. After that, its breaking strength, elongation, etc. will be affected to varying degrees, thereby reducing the stability, resulting in easy aging of the material and low service life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A kind of polypropylene shielding material, it is made up of the raw material of following weight part:

[0022] Diphenylsilanediol 3, high-density polyethylene 120, ethylene bisstearamide 1, zinc powder 1, azodicarbonamide 0.8, sucrose acetate isobutyrate 1, polyamide wax micropowder 3, ethoxy Alkylphenol Ammonium Sulfate 1, Light Stabilizer 622 0.1, Dibasic Lead Phosphite 0.7, Triethylamine 2, Epichlorohydrin 1, Bentonite 10.

[0023] A preparation method of polypropylene shielding material, comprising the following steps:

[0024] (1) Take the micro-powder of polyamide wax, add it to 4 times the weight of absolute ethanol, stir evenly, increase the temperature to 60°C, heat and stir for 10 minutes, and obtain the alcohol dispersion;

[0025] (2) Get ethylene bisstearamide, add it to 13 times the deionized water of its weight, stir evenly, and obtain the amide solution;

[0026] (3) Take bentonite, calcinate it at 700° C. for 1 hour, cool to normal temperature, add ...

Embodiment 2

[0033] A kind of polypropylene shielding material, it is made up of the raw material of following weight part:

[0034] Diphenylsilanediol 4, high-density polyethylene 140, ethylene bisstearamide 2, zinc powder 3, azodicarbonamide 1, sucrose acetate isobutyrate 2, polyamide wax micropowder 5, ethoxy Alkylphenol Ammonium Sulfate 2, Light Stabilizer 622 0.2, Dibasic Lead Phosphite 1, Triethylamine 3, Epichlorohydrin 2, Bentonite 14.

[0035] A preparation method of polypropylene shielding material, comprising the following steps:

[0036] (1) Take the polyamide wax micropowder, add it to 7 times its weight in absolute ethanol, stir evenly, increase the temperature to 65°C, keep it warm and stir for 20 minutes, and obtain the alcohol dispersion;

[0037] (2) Get ethylene bis stearamide, add it to 20 times of its weight in deionized water, stir evenly to obtain amide solution;

[0038] (3) Take bentonite, calcinate at 750° C. for 2 hours, cool to normal temperature, add to deion...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a polypropylene shielding material which is composed of, by weight, 3-4 parts diphenyl silanediol, 120-140 parts of high-density polyethylene, 1-2 parts of ethylene bisstearamide, 1-3 parts of zinc powder, 0.8-1 part of azodicarbonamide, 1-2 parts of sucrose acetate isobutyrate, 3-5 parts of polyamide wax micropowder, 1-2 parts of ethoxylated ammonium alkylphenol sulfate, 0.1-0.2 parts of a photo-stabilizer 622, 0.7-1 part of dibasic lead phosphite, 2-3 parts of triethylamine, 1-2 parts of epoxy chloropropane and 10-14 parts of bentonite. By adding the zinc powder, thephoto-stabilizer 622 and the like, ultraviolet light can be effectively absorbed. The material also has certain shielding effects on other irradiation.

Description

technical field [0001] The invention belongs to the field of materials, in particular to a polypropylene shielding material. Background technique [0002] With the continuous development of modern society, various high-energy rays are more and more widely used in military affairs, communications, medicine, industry, agriculture and people's daily life, which directly leads to the annual collective effective dose of radiation dose in the world. All kinds of rays have also brought a lot of harm to people to some extent, and have been considered as the fourth largest public hazard after air pollution, water pollution and noise pollution; [0003] With the advancement of science and technology, in order to reduce the negative effects of various types of radiation pollution on people, it is necessary to develop shielding materials with certain protective functions to resist various rays and microwaves; [0004] Polypropylene material is a semi-crystalline thermoplastic. It has ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/06C08L77/00C08K13/06C08K9/04C08K3/08C08K5/20C08K3/34
CPCC08K2003/0893C08L23/06C08L2201/08C08L2207/062C08L77/00C08K13/06C08K9/04C08K3/08C08K5/20C08K3/346
Inventor 王家浩
Owner 王家浩
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More