Halogen-free flame-retardant silicone rubber leather and coating process thereof

A coating process, silicone rubber technology, applied in textiles and papermaking, etc., can solve the problems of unsatisfactory flame retardant effect of PU synthetic leather, potential safety hazards, affecting the physical properties and hand feel of PU synthetic leather, etc., to achieve good flame retardant effect, production The effect of high efficiency and low production cost

Inactive Publication Date: 2018-06-08
GUANGDONG TIANYUE NEW MATERIAL CO LTD
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Polyurethane synthetic leather is mainly processed by dry and wet methods. Since its main elements are carbon, hydrogen, nitrogen, and oxygen, the two elements of carbon and hydrogen have the disadvantage of being flammable, and the combustion of carbon and hydrogen will produce a lot of toxic smoke. and gas, making polyurethane synthetic leather bring comfort and convenience to people's production and life, but also leaves a huge safety hazard
PU synthetic leather mainly achieves the purpose of flame retardancy by adding flame retardants or modified polyurethane, but most of the added flame retardants will affect the physical properties and feel of PU synthetic leather, while the flame retardant effect of PU synthetic leather obtained by modified polyurethane is not as good as that of PU synthetic leather. not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Example 1. This example discloses a halogen-free flame-retardant silicone rubber leather. In terms of parts by mass, its raw materials include 100 parts of low-viscosity vinyl fluorine-containing silicone oil, 30 parts of hydrophobic white carbon black, and 20 parts of inorganic fillers. 5 parts, 5 parts of hydrogen-containing silicone oil, 0.1 part of platinum catalyst, 5 parts of color paste pigment, 3 parts of low-viscosity hydroxyl silicone oil and 0.02 part of inhibitor.

[0045] The low-viscosity vinyl fluorine-containing silicone oil has a viscosity of 300-3000cs and a fluorine content of 1-5%.

[0046] The hydroxyl treatment amount on the surface of the hydrophobic silica is greater than 60%;

[0047] The inorganic filler is one or more combinations of silicon micropowder, calcium carbonate, diatomite, aluminum oxide, calcium oxide and montmorillonite.

[0048] The fluorine element has a phenomenon of enrichment on the surface, and the fluorine element content ...

Embodiment 2

[0062] Example 2. This example discloses a halogen-free flame-retardant silicone rubber leather. In terms of parts by mass, its raw materials include 150 parts of low-viscosity vinyl fluorine-containing silicone oil, 50 parts of hydrophobic white carbon black, and 30 parts of inorganic fillers. 20 parts, 20 parts of hydrogen-containing silicone oil, 0.5 parts of platinum catalyst, 20 parts of color paste pigment, 10 parts of low-viscosity hydroxyl silicone oil and 0.1 part of inhibitor.

[0063] The low-viscosity vinyl fluorine-containing silicone oil has a viscosity of 300-3000cs and a fluorine content of 1-5%.

[0064] The hydroxyl treatment amount on the surface of the hydrophobic silica is greater than 60%;

[0065] The inorganic filler is one or more combinations of silicon micropowder, calcium carbonate, diatomite, aluminum oxide, calcium oxide and montmorillonite.

[0066] The fluorine element has a phenomenon of enrichment on the surface, and the fluorine element cont...

Embodiment 3

[0080] Example 3. This example discloses a halogen-free flame-retardant silicone rubber leather. The raw materials include 125 parts of low-viscosity vinyl fluorine-containing silicone oil, 40 parts of hydrophobic white carbon black, and 25 parts of inorganic filler. parts, 12.5 parts of hydrogen-containing silicone oil, 0.3 parts of platinum catalyst, 12.5 parts of color paste pigment, 6.5 parts of low-viscosity hydroxyl silicone oil and 0.06 parts of inhibitor.

[0081] The low-viscosity vinyl fluorine-containing silicone oil has a viscosity of 300-3000cs and a fluorine content of 1-5%.

[0082] The hydroxyl treatment amount on the surface of the hydrophobic silica is greater than 60%;

[0083] The inorganic filler is one or more combinations of silicon micropowder, calcium carbonate, diatomite, aluminum oxide, calcium oxide and montmorillonite.

[0084] The fluorine element has a phenomenon of enrichment on the surface, and the fluorine element content on the surface of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a halogen-free flame-retardant silicone rubber leather, which is prepared from the raw materials in parts by mass: 100 to 150 parts of low-viscosity vinyl fluorine-containing silicone oil, 30 to 50 parts of hydrophobic white carbon black, 20 to 30 parts of inorganic filler, 5 to 20 parts of hydrogen-containing silicone oil , 0.1 to 0.5 part of platinum catalyst, 5 to 20 parts of color paste pigment, 3 to 10 parts of low-viscosity hydroxyl silicone oil, and 0.02 to 0.1 part of inhibitor. The invention also discloses a coating process of the halogen-free flame-retardant silicone rubber leather. The coating process provided by the invention is simple in process, high in production efficiency and low in production cost, and the prepared halogen-free flame-retardant silicone rubber leather cannot damage a hand feeling and a physical property of silicone rubber, and has a favorable flame retardant effect at the same time.

Description

technical field [0001] The invention relates to the technical field of organosilicon and leather manufacturing, in particular to a halogen-free flame-retardant silicone rubber leather and a coating process for the halogen-free flame-retardant silicone rubber leather. Background technique [0002] After years of development, polyurethane synthetic leather has been widely used in industrial, civil and military fields due to its good appearance and feel, wear resistance, solvent resistance, high strength and wide application, and is closely related to people's production and life. [0003] Polyurethane synthetic leather is mainly processed by dry and wet methods. Since its main elements are carbon, hydrogen, nitrogen, and oxygen, the two elements of carbon and hydrogen have the disadvantage of being flammable, and the combustion of carbon and hydrogen will produce a lot of toxic smoke. and gas, making polyurethane synthetic leather bring comfort and convenience to people's prod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/12D06N3/00C08L83/08C08L83/04C08L83/05C08K3/36C08K3/34C08K3/26C08K3/22
CPCC08K2003/2206C08K2003/2227C08K2003/265C08L83/08C08L2201/02C08L2201/22C08L2205/025C08L2205/03D06N3/0095D06N3/128D06N2209/16D06N2209/1664D06N2211/28C08L83/04C08K3/36C08K3/34C08K3/26C08K3/346C08K3/22
Inventor 胥晓群陶玉红
Owner GUANGDONG TIANYUE NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products