Fabric-based adhesive tape produced from UV-cured hot-melt pressure-sensitive adhesive and applicable to automobile wiring harness and production technology thereof

A hot-melt pressure-sensitive adhesive, curing heat technology, applied in the direction of adhesives, pressure-sensitive films/sheets, film/sheet adhesives, etc. The effect of good temperature performance and simple operation process

Inactive Publication Date: 2018-07-17
TIANJIN PUZHENG POWER TECH CO LTD
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The present invention overcomes the shortcoming of insufficient temperature resistance of the existing thermoplastic elastomer hot-melt pressure-sensitive adhesive cloth-based adhesive tape, and provides a UV-cured and cross-linked thermoplastic elastomer hot-melt pressure-sensitive adhesive. Cloth Adhesive Tape

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Embodiment 1: The making process of UV curing hot-melt pressure-sensitive adhesive: according to formula, block copolymer thermoplastic elastomer SBS35 weight parts, block copolymer thermoplastic elastomer SEBS 10 weight parts, softener naphthenic oil 5 weight parts parts, 3 parts by weight of dioctyl phthalate (DOP), and 10100.8 parts by weight of antioxidant, first add it to the melt glue tank, pass nitrogen protection for 5 minutes, start stirring and heat, when the temperature reaches 160-170 ° C , kept for 50-60 minutes to completely melt the thermoplastic elastomer, then added 25 parts by weight of petroleum resin, 20 parts by weight of diallyl phthalate, 11731.2 parts by weight of photoinitiator, stopped heating, and stirred for 20-30 Minutes, naturally cooled to about 120°C, then discharged and distributed for use.

[0028] Manufacturing process of the cloth-based adhesive tape: the manufacturing of the cloth-based pressure-sensitive adhesive tape can be carried...

Embodiment 2

[0029]Embodiment 2: The production process of UV curing hot-melt pressure-sensitive adhesive: according to formula, block copolymer thermoplastic elastomer SIS35 weight parts, block copolymer thermoplastic elastomer SBS 13 weight parts, softener naphthenic oil 5 weight parts parts, 3 parts by weight of dioctyl phthalate (DOP), and 10100.8 parts by weight of antioxidant, first add it to the melt glue tank, pass nitrogen protection for 5 minutes, start stirring and heat, when the temperature reaches 160-170 ° C , kept for 50-60 minutes to make the thermoplastic elastomer hot-melt completely, then added 30 parts by weight of rosin resin, 12 parts by weight of bis(2-ethylhexyl) maleate, 11731.2 parts by weight of photoinitiator, and stopped Heating, stirring for 20-30 minutes, naturally cooling to about 120°C, discharging and distributing for equipment.

[0030] The manufacturing process of the cloth-based adhesive tape is the same as in Example 1. The test results are listed in ...

Embodiment 3

[0031] Embodiment 3: The production process of UV curing hot-melt pressure-sensitive adhesive: According to the formula, 35 parts by weight of block copolymer thermoplastic elastomer SIS, 7 parts by weight of block copolymer thermoplastic elastomer SEBS, and 5 parts by weight of softener naphthenic oil Parts, 1 part by weight of dioctyl phthalate (DOP), 10100.8 parts by weight of antioxidant, put them into the melt glue tank first, pass nitrogen protection for 5 minutes, start stirring and heat, when the temperature reaches 160-170 °C , kept for 50-60 minutes to completely melt the thermoplastic elastomer, then added 35 parts by weight of hydrogenated rosin resin, 10 parts by weight of di-n-butyl maleate, 5 parts by weight of 2-ethylhexyl acrylate for photoinitiation 11731.2 parts by weight of the agent, stop heating, stir for 20-30 minutes, naturally cool to about 120°C, then discharge and distribute for use.

[0032] The manufacturing process of the cloth-based adhesive tape...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a novel environment-friendly, temperature-resistant and wear-resistant fabric-based adhesive tape produced from an ultraviolet (UV)-cured hot-melt pressure-sensitive adhesiveand a production technology thereof. The pressure-sensitive adhesive tape is produced by directly coating a polyester fabric or non-woven fabric base material with the novel UV-cured hot-melt pressure-sensitive adhesive by using a hot-melt coating machine equipped with an UV lamp, and curing the pressure-sensitive adhesive by UV irradiation in a crosslinking manner; the UV-cured hot-melt pressure-sensitive adhesive is prepared by heating and blending a block copolymer thermoplastic elastomer, tackifying resin, a softening agent, a long-chain alkyl-containing vinyl monomer, a photoinitiator, anantioxidant and other auxiliary agents according to a certain ratio. The fabric-based adhesive tape not only has excellent mechanical properties, adhesive performance, high temperature resistance andfriction resistance, but also is relatively low in hot-melt coating temperature, simple and convenient in production technology and free of environment pollution, is applicable to packaging and bundling of cable bundles in different parts of an automobile body, particularly can meet the using requirements on high temperature-resistant parts of an engine inside an automobile, and has the long-termtemperature resistance level of 125 DEG C.

Description

Technical field: [0001] The invention relates to a cloth-based adhesive tape made of UV-cured hot-melt pressure-sensitive adhesive for automobile wiring harnesses, including a polyester cloth-based adhesive tape, a non-woven cloth-based adhesive tape and a manufacturing technology thereof. Background technique: [0002] In the field of wrapping and bundling of automotive wiring harnesses, the adhesive tape prepared by using polyester cloth base material and non-woven fabric base material can meet the "Restriction of the Use of Certain Hazardous Substances Directive in Electrical and Electronic Equipment" (ROHS Directive) promulgated by the European Commission. ), and have a good effect on the control of the air quality in the car. At the same time, pressure-sensitive adhesives also play an important role that cannot be ignored in the performance and application of adhesive tapes. [0003] Chinese invention patent ZL 01814153.6 discloses an electrical adhesive tape with non-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J7/21C09J7/38C09J153/02C09J11/08C09J11/06
CPCC08K2201/014C08L2201/08C08L2205/02C08L2205/035C08L2207/04C08L2312/00C09D11/06C09J11/08C09J153/02C09J2301/302C09J2453/00C09J2491/00C08L53/025C08L57/02C08L91/00C08K5/12C08K5/1345C08L93/04C08K5/11C08K5/00C08K5/101
Inventor 郭建英赵鹏媛范晶晶奚羽
Owner TIANJIN PUZHENG POWER TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com