Dental repair filling material and preparation method thereof

A filling material and tooth technology, used in dental preparations, dentistry, dental prostheses, etc., can solve the problems of insufficient compressive strength and long coagulation time, and achieve the effects of simple method, short coagulation time and easy-to-obtain raw materials

Inactive Publication Date: 2018-07-27
ANHUI AOZI INFORMATION TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a filling material for tooth repair and its preparation method, whi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0015] The present invention provides a kind of preparation method of filling material for tooth repair, and described preparation method comprises:

[0016] (1) After mixing tetracalcium phosphate, hydroxyapatite, calcium magnesium phosphate, anhydrous calcium hydrogen phosphate, anhydrous magnesium sulfate, sodium chloride and sodium bicarbonate, grind to obtain mixed powder M;

[0017] (2) mixing the mixed powder, solvent, adhesive, fibrous filler and biological filler to obtain a filling material for tooth restoration;

[0018] Wherein, relative to 100 parts by weight of tetracalcium phosphate, the consumption of hydroxyapatite is 40-60 parts by weight, the consumption of calcium magnesium phosphate is 20-40 parts by weight, and the consumption of anhydrous calcium hydrogen phosphate is 10-20 parts by weight, The consumption of anhydrous magnesium sulfate is 4-10 parts by weight, the consumption of sodium chloride is 1-10 parts by weight, and the consumption of sodium bica...

Embodiment 1

[0030] Tetracalcium phosphate, hydroxyapatite, magnesium calcium phosphate, anhydrous calcium hydrogen phosphate, anhydrous magnesium sulfate, sodium chloride and sodium bicarbonate are mixed and ground to obtain mixed powder M; mixed powder, ethanol, acrylate, Glass fiber and bioglass are mixed to obtain dental filling material A1;

[0031] Wherein, relative to the tetracalcium phosphate of 100g, the consumption of hydroxyapatite is 40g, the consumption of calcium magnesium phosphate is 20g, the consumption of anhydrous calcium hydrogen phosphate is 10g, the consumption of anhydrous magnesium sulfate is 4g, the consumption of sodium chloride For 1g, the consumption of sodium bicarbonate is 5g; Relative to the mixed powder of 100g, the consumption of ethanol is 70g, and the consumption of acrylate is 10g, and the consumption of glass fiber is 5g, and the consumption of bioglass is 5g.

Embodiment 2

[0033] Tetracalcium phosphate, hydroxyapatite, magnesium calcium phosphate, anhydrous calcium hydrogen phosphate, anhydrous magnesium sulfate, sodium chloride and sodium bicarbonate are mixed and ground to obtain mixed powder M; mixed powder, propylene glycol, methacrylic acid Salt, polyester fiber and calcium phosphate are mixed to obtain dental filling material A2;

[0034] Wherein, relative to the tetracalcium phosphate of 100g, the consumption of hydroxyapatite is 60g, the consumption of calcium magnesium phosphate is 40g, the consumption of anhydrous calcium hydrogen phosphate is 20g, the consumption of anhydrous magnesium sulfate is 10g, the consumption of sodium chloride For 10g, the consumption of sodium bicarbonate is 15g; Relative to the mixed powder of 100g, the consumption of propylene glycol is 100g, the consumption of methacrylate is 18g, the consumption of polyester fiber is 10g, and the consumption of calcium phosphate is 10g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a dental repair filling material and a preparation method thereof. The preparation method of the dental repair filling material comprises mixing and grinding tetracalcium phosphate, hydroxyapatite, calcium magnesium phosphate, calcium phosphate dibasic, anhydrous magnesium sulfate, sodium chloride and sodium bicarbonate to obtain a mixed powder M; mixing the mixed powder, solvent, bonding agent, fiber filler and biological filler to obtain the dental repair filling material. The dental repair filling material and the preparation method thereof solve the problem of longcoagulation time and relatively poor compressive strength of traditional filling materials.

Description

technical field [0001] The invention relates to the field of dentistry, in particular to a filling material for tooth restoration and a preparation method thereof. Background technique [0002] Clinically, doctors often choose different materials to fill the cavity according to the location of the affected tooth, the location of the cavity, the magnitude of the occlusal force, as well as the patient's health and aesthetic requirements. Currently, the commonly used materials are: silver amalgam, composite Resin and glass ionomer complex. [0003] Silver amalgam is a commonly used restorative material with a history of more than 150 years. Its safety has been well established. So far, there is no direct evidence that it has adverse effects on human health, and it has been widely used in the general population. The incidence of allergic reactions is extremely low. Silver amalgam has the largest compressive strength, hardness and wear resistance, and its performance is stable. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61K6/033A61K6/02A61K6/00A61K6/838
CPCA61K6/15A61K6/60A61K6/76A61K6/77A61K6/80A61K6/838
Inventor 冯敏
Owner ANHUI AOZI INFORMATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products