High-density thermoplastic plastic for entertainment industry chips and preparing method of plastic

A thermoplastic and high-density technology, which is applied in the field of high-density thermoplastics for chips in the entertainment industry and its preparation, can solve the problems of low physical strength, low physical strength of products, high cost, etc., and achieve high density, good appearance and texture, and high strength Effect

Inactive Publication Date: 2018-08-28
ZHANGJIAGANG OTSUKA CHEM
View PDF9 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The advantages of metal materials are high density and good texture, but the processing of metal materials is difficult and the cost is high; plastic composite materials are generally filled with general-purpose resins such as low-melting polypropylene or polyvinyl chloride or polyethylene terephthalate. Inorganic minerals are used to increase the specific gravity of composite materials and improve the feel of chips. The density is generally around 2.5g / cm3, which is lower than the density of metal materials, and the feel and surface texture are slightly worse than metal materials. General-purpose resins such as ethylene glycol phthalate have low physical strength, so the prepared products have low physical strength and are easily damaged during long-term use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] (1) Put 15 parts by weight of polyphenylene sulfide, 5 parts by weight of ethylene-butyl acrylate copolymer, and 0.5 parts by weight of silicone powder into a rotary mixer with a rotation speed of 60 rpm for mixing, and mix for 10 minutes to obtain a mixture .

[0016] (2) Put the above mixture into the main discharge port of the twin-screw extruder through a weight-loss feeder, and take 79.5 parts by weight of iron powder from the feeding port of the extruder side by a vibrating feeder, and carry out melt mixing and extrusion Strips, the strips are transported to the pelletizer via the conveyor belt to be cut into pellets, cooled and packaged to obtain the finished product.

[0017] Preferably, in step (2), the barrel temperature of each section of the extruder is 310°C, the head temperature is 320°C, the discharge rate is 100Kg / h, the rotation speed is 150rpm, and the vacuum pressure is controlled at -0.08±0.02MPa.

Embodiment 2

[0019] (1) Put 20 parts by weight of polyphenylene sulfide, 5 parts by weight of ethylene-butyl acrylate copolymer, 0.5 parts by weight of silicone powder, and 4.5 parts by weight of titanium dioxide into a rotary mixer with a speed of 60 rpm Mixing, the mixture was obtained after mixing for 10 min.

[0020] (2) Put the above mixture into the main discharge port of the twin-screw extruder through a weight-loss feeder, and take 70 parts by weight of iron powder from the feeding port of the extruder side by a vibrating feeder, and carry out melt mixing and extrusion Strips, the strips are transported to the pelletizer via the conveyor belt to be cut into pellets, cooled and packaged to obtain the finished product.

[0021] Preferably, in step (2), the barrel temperature of each section of the extruder is 310°C, the head temperature is 320°C, the output is 100Kg / h, the rotation speed is 150rpm, and the vacuum pressure is controlled at -0.08±0.02MPa.

[0022] Composite material p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-density thermoplastic plastic for entertainment industry chips and a preparing method of the plastic. The plastic comprises 10-30 parts by weight of polyphenylene sulfide, 50-90 parts by weight of metal powder, 0-10 parts by weight of flexibilizer, 0-1 part by weight of lubricant and 0-5 parts by weight of colorant. The preparing method of the plastic includes the steps of adding polyphenylene sulfide, flexibilizer, lubricant and colorant into a mixer to be mixed in proportion to obtain a mixture, putting the mixture into a main feeding port of a twin-screw extruder through a weightless feeder, putting iron powder into a side feeding port of the extruder through a vibration feeder, conducting melting and mixing to extrude a strip-shaped object, conveying thestrip-shaped object through a conveying belt to a granulator to be granulated, cooled and packaged to obtain a finished product. The physical strength and appearance quality of the prepared plastic are remarkably improved.

Description

technical field [0001] The invention relates to the field of engineering plastic composite materials, in particular to a high-density thermoplastic used for chips in the entertainment industry and a preparation method thereof. Background technique [0002] The substrates of chips used in the entertainment industry are mostly metal or plastic composite materials. The advantages of metal materials are high density and good texture, but the processing of metal materials is difficult and the cost is high; plastic composite materials are generally filled with general-purpose resins such as polypropylene or polyvinyl chloride or polyethylene terephthalate with a low melting point. Inorganic minerals are used to increase the specific gravity of composite materials and improve the feel of chips. The density is generally around 2.5g / cm3, which is lower than the density of metal materials, and the feel and surface texture are slightly worse than metal materials. General-purpose resin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L81/02C08L23/08C08L83/04C08K3/08B29C47/92B29C48/92
CPCB29C48/92B29C2948/92704C08K2003/0856C08L81/02C08L2205/03C08L23/0869C08L83/04C08K3/08
Inventor 张昱郭继光耿昊堤秀介
Owner ZHANGJIAGANG OTSUKA CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap