Differential p-xylene preparation method
A para-xylene and differential technology, applied in the field of differential para-xylene preparation, can solve the problems of single xylene product and shortened service life, and achieve long interaction time, good deep integration and good anti-aging effect. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0043] A preparation method of differentiated p-xylene, comprising the steps of:
[0044] (1) the silver phosphate of 17 parts by weight, the bismuth vanadate of 18 parts, the rutile type titanium dioxide of 5 parts and the white carbon black of 3 parts and the concentration of 80 parts are 4wt% fluorosulfonic acid solution mixing , moved to a hydrothermal reactor, stirred continuously at 130°C and 0.3MPa pressure for 5h, then cooled naturally under stirring, ground with a liquid-phase high-energy ball mill at 45°C for 3.5h, filtered, and then heated at 515°C Calcined at ℃ for 5.5h, fully washed with deionized water, dried in vacuum at 90℃, ground for 5h with a ball mill, and sieved through 250 mesh to obtain a special anti-aging agent;
[0045] (2) P-xylene is added successively with p-xylene weight as 10% acetic acid, 2.5% o-xylene, 1.0% ethylamine co-solvent and 2.5% special anti-oxidant prepared by (1) under continuous stirring. Aging agent, then add 4% potassium hydrogen...
Embodiment 2
[0049] A preparation method of differentiated p-xylene, comprising the steps of:
[0050] (1) 15 parts by weight of silver phosphate, 20 parts of bismuth vanadate, 3 parts of rutile titanium dioxide and 4 parts of white carbon black are mixed with 70 parts of fluorosulfonic acid solution with a concentration of 4wt% , moved to a hydrothermal reactor, continuously stirred and reacted at 140°C and 0.2MPa pressure for 6h, then cooled naturally under stirring, ground with a liquid phase high-energy ball mill at 55°C for 3h, filtered, and then heated at 500°C Calcined for 6 hours, fully washed with deionized water, dried in vacuum at 80°C, ground for 6 hours with a ball mill, and sieved through 200 mesh to obtain a special anti-aging agent;
[0051] (2) P-xylene is added successively with p-xylene weight as 11% acetic acid, 1% o-xylene, 1.2% ethylamine co-solvent and 2% special anti-oxidant prepared by (1) under continuous stirring. Aging agent, then add 5% potassium hydrogen phos...
Embodiment 3
[0055] A preparation method of differentiated p-xylene, comprising the steps of:
[0056] (1) 20 parts by weight of silver phosphate, 15 parts of bismuth vanadate, 6 parts of rutile titanium dioxide and 2 parts of white carbon black are mixed with 90 parts of fluorosulfonic acid solution , moved to a hydrothermal reactor, continuously stirred and reacted at 110°C and 0.4MPa pressure for 4h, then cooled naturally under stirring, ground with a liquid phase high-energy ball mill at 35°C for 4h, filtered, and then heated at 530°C Calcined at low temperature for 5 hours, fully washed with deionized water, dried in vacuum at 95°C, ground for 4 hours with a ball mill, and sieved through 300 mesh to obtain a special anti-aging agent;
[0057] (2) P-xylene is added successively with p-xylene weight as 9% acetic acid, 4% o-xylene, 0.8% ethylamine co-solvent and 3% special anti-oxidant prepared by (1) under continuous stirring. Aging agent, then add 3% potassium hydrogen phosphate dispe...
PUM
Property | Measurement | Unit |
---|---|---|
elongation at break | aaaaa | aaaaa |
elongation at break | aaaaa | aaaaa |
elongation at break | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com