Tooth repair filling material and preparation method thereof

A filling material and tooth technology, applied in dental preparations, dentistry, dental prostheses, etc., can solve the problems of insufficient compressive strength and long setting time, and achieve the effect of simple method, short setting time and high compressive strength

Inactive Publication Date: 2018-09-07
ANHUI AOZI INFORMATION TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a filling material for tooth repair and its preparation method, which solves the problems of long setting time and relatively insufficient compressive strength of traditional filling materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0015] The present invention provides a kind of preparation method of filling material for tooth repair, and described preparation method comprises:

[0016] (1) Calcium dihydrogen phosphate monohydrate, calcium dihydrogen phosphate anhydrous, calcium hydrogen phosphate dihydrate, calcium hydrogen phosphate anhydrous, magnesium sulfate anhydrous, sodium chloride and sodium bicarbonate are mixed and ground to obtain a mixed powder M;

[0017] (2) mixing the mixed powder, solvent, adhesive, fibrous filler and biological filler to obtain a filling material for tooth restoration;

[0018] Wherein, relative to 100 parts by weight of calcium dihydrogen phosphate monohydrate, the consumption of calcium dihydrogen phosphate anhydrous is 40-60 parts by weight, the consumption of calcium hydrogen phosphate dihydrate is 20-40 parts by weight, and the consumption of calcium hydrogen phosphate anhydrous is 20-40 parts by weight. The consumption is 10-20 parts by weight, the consumption of...

Embodiment 1

[0030] Calcium dihydrogen phosphate monohydrate, calcium dihydrogen phosphate anhydrous, calcium hydrogen phosphate dihydrate, calcium hydrogen phosphate anhydrous, magnesium sulfate anhydrous, sodium chloride and sodium bicarbonate are mixed and ground to obtain mixed powder M; Mixing powder, ethanol, acrylate, glass fiber and bioglass to obtain dental filling material A1;

[0031] Wherein, relative to 100g of calcium dihydrogen phosphate monohydrate, the consumption of calcium dihydrogen phosphate anhydrous is 40g, the consumption of calcium hydrogen phosphate dihydrate is 20g, the consumption of calcium hydrogen phosphate anhydrous is 10g, the consumption of anhydrous magnesium sulfate For 4g, the consumption of sodium chloride is 1g, and the consumption of sodium bicarbonate is 5g; Relative to the mixed powder of 100g, the consumption of ethanol is 70g, and the consumption of acrylate is 10g, and the consumption of glass fiber is 5g, and the consumption of bioglass The dos...

Embodiment 2

[0033] Calcium dihydrogen phosphate monohydrate, calcium dihydrogen phosphate anhydrous, calcium hydrogen phosphate dihydrate, calcium hydrogen phosphate anhydrous, magnesium sulfate anhydrous, sodium chloride and sodium bicarbonate are mixed and ground to obtain mixed powder M; The mixed powder, propylene glycol, methacrylate, polyester fiber and calcium phosphate are mixed to obtain the dental filling material A2;

[0034] Wherein, relative to 100g of calcium dihydrogen phosphate monohydrate, the consumption of calcium dihydrogen phosphate anhydrous is 60g, the consumption of calcium hydrogen phosphate dihydrate is 40g, the consumption of calcium hydrogen phosphate anhydrous is 20g, the consumption of anhydrous magnesium sulfate The amount of sodium chloride is 10g, the amount of sodium chloride is 10g, the amount of sodium bicarbonate is 15g; relative to 100g of mixed powder, the amount of propylene glycol is 100g, the amount of methacrylate is 18g, the amount of polyester f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a tooth repair filling material and a preparation method thereof. The preparation method comprises the following steps: calcium dihydrogen phosphate monohydrate, anhydrous calcium dihydrogen phosphate, calcium hydrogen phosphate dihydrate, anhydrous calcium hydrogen phosphate, anhydrous magnesium sulfate, sodium chloride and sodium bicarbonate are mixed and ground, and mixed powder M is obtained; the mixed powder, a solvent, an adhesive, fiber filler and biological filler are mixed, and the tooth repair filling material is obtained. The problems of longer setting time and relatively insufficient compressive strength of a traditional filling material are solved.

Description

technical field [0001] The invention relates to the field of dentistry, in particular to a filling material for tooth restoration and a preparation method thereof. Background technique [0002] Clinically, doctors often choose different materials to fill the cavity according to the location of the affected tooth, the location of the cavity, the magnitude of the occlusal force, as well as the patient's health and aesthetic requirements. Currently, the commonly used materials are: silver amalgam, composite Resin and glass ionomer complex. [0003] Silver amalgam is a commonly used restorative material with a history of more than 150 years. Its safety has been well established. So far, there is no direct evidence that it has adverse effects on human health, and it has been widely used in the general population. The incidence of allergic reactions is extremely low. Silver amalgam has the largest compressive strength, hardness and wear resistance, and its performance is stable. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61K6/033A61K6/02A61K6/00A61K6/838
CPCA61K6/15A61K6/60A61K6/75A61K6/76A61K6/77A61K6/80A61K6/838
Inventor 冯敏
Owner ANHUI AOZI INFORMATION TECH CO LTD
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com