A protective material and its application as a protective layer on the surface of a building and repairing the corroded part of a building

A protection material and moisture technology, applied in building maintenance, building construction, construction, etc., can solve the problems of difficult to guarantee the long-term performance of organic coatings, difficult repair and construction, poor anti-aging performance, etc., and achieve the ratio of raw materials and particle size. Scientific and reasonable grading, improving construction difficulty and increasing bond strength

Active Publication Date: 2021-02-19
YELLOW RIVER ENG CONSULTING
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ordinary mortar materials are cement-based materials, which have poor waterproof effect and are easily deteriorated and damaged under decomposition corrosion conditions; while organic coatings have poor anti-aging performance, and the long-term performance of organic coatings is difficult to guarantee under harsh conditions
For parts that have been corroded, due to the uneven surface, repair construction is extremely difficult, and it is easy to cause bulges and punctures

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A protective material and its application as a protective layer on the surface of a building and repairing the corroded part of a building
  • A protective material and its application as a protective layer on the surface of a building and repairing the corroded part of a building
  • A protective material and its application as a protective layer on the surface of a building and repairing the corroded part of a building

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] The protection material described in the present invention is 100g of raw material silicate 42.5 cement; 200g of clean natural fine sand with a particle size less than 1.18mm (can be adjusted within 150~250g according to actual needs, and note that the mud content is not more than 3%. Moisture content not greater than 0.2%); 0.15g of Dura fiber with a nominal length of 20mm and an equivalent diameter of 40μm; 5g of moisture migration inhibitor; 5g of metakaolin mixed;

[0043] Among them, metakaolin is obtained by calcining commercially available kaolin at 750°C~800°C, and then grinding to a fineness of 500 mesh; in order to ensure the use effect of the final protective material, SiO in metakaolin 2The content is not less than 50%, Al 2 o 3 The content is not less than 40%, and the specific surface area is not less than 15000m2 2 / kg.

[0044] In order to improve the waterproof performance of the finished protective material, the water migration inhibitor used in the...

Embodiment 2

[0054] Repair corroded concrete, the corrosive type is heavy carbonic acid decomposition type medium corrosion. According to the actual situation, the damage model of the concrete slab was simulated and made. The model showed that the concrete mortar was lost, the aggregate was exposed, and the corrosion depth was about 15mm.

[0055] Prepare the protective material slurry according to the ratio of Example 1; clean the corroded surface, expose the fresh concrete interface, and keep the interface as smooth as possible. During the construction process, keep the interface moist and free of clear water.

[0056] Apply a total of three layers, the thickness of the first layer is 5.5mm±0.5 mm, and the thickness of each subsequent layer is 5mm, and a layer of glass fiber mesh cloth is covered between the two layers of coating; when applying appropriate pressure, strive to make the coating dense. The maintenance method after smearing is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a protective material, which is prepared by mixing 100 parts of Portland cement, 100-250 parts of natural fine sand, 0.15-0.20 parts of durafiber, 5 parts of moisture migration inhibitor, and 3-8 parts of metakaolin The present invention also discloses the application of the protective material as a protective layer on the surface of a building and repairing a corroded part of a building. The protection material of the present invention has few types of raw materials, scientific and reasonable raw material ratio and particle size distribution, outstanding waterproof effect, and can effectively prevent corrosion of concrete buildings caused by water quality. At the same time, when used as a repair material, the construction is convenient. The difficulty of construction is greatly reduced.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a protective material for buildings. The invention also relates to the application of the protective material as a protective layer on the surface of buildings and for repairing corroded parts of buildings. Background technique [0002] Present building exterior walls all need construction protective coating, and some also need to lay insulation board on exterior wall, and construction protective coating is again outside insulation board. [0003] For high-altitude cold mountainous areas (such as Ganzi Prefecture, Sichuan Province, my country), the outer walls of buildings generally need to be laid with insulation board materials. The ultraviolet radiation in this area is strong, the temperature difference between day and night is more than 30°C, and the environmental conditions are extremely harsh. It is necessary to take protective measures for the outer layer of the insulatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B20/02E04B1/62E04G23/02C04B111/27C04B111/23C04B111/72C04B14/10C04B14/20
CPCC04B20/023C04B28/04C04B2111/00508C04B2111/23C04B2111/27C04B2111/72E04B1/62E04G23/0296C04B14/06C04B14/106C04B16/0633C04B14/20
Inventor 张金良苏茂林尚宏琦吴法辰景来红毛文然杨林陈学理
Owner YELLOW RIVER ENG CONSULTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com