Special micro-capsule material for electronic skin self-repairing and preparation method thereof

An electronic skin and self-repairing technology, which is applied in the direction of microcapsule preparation, microsphere preparation, adhesives, etc., can solve the problems of microcircuit short circuit and self-repairing of electronic skin

Inactive Publication Date: 2018-09-28
CHENDU NEW KELI CHEM SCI CO LTD
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] In view of the defects that the existing electronic skin is difficult to self-repair after being damaged, and the short circuit of the microcircuit is easily cau

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] (a). Prepare prepolymer in advance: prepare melamine-formaldehyde resin prepolymer;

[0035] (b). Stir and mix 50g graphene, 80g of 1-methyl-3-ethylimidazolium chloride ionic liquid, and 40g of dicyclopentadiene at 25 degrees Celsius at 40 rpm to obtain a mixture, and then in the mixture Add 50g of emulsifier NP-10, and then disperse under the action of ultrasound to obtain an emulsion.

[0036] (c). Add 200g of the emulsion prepared in step (b) into the reaction vessel, slowly add 800g of the prepolymer prepared in step (a) under the condition of sufficient stirring, and raise the temperature to 60°C, keep warm and continue the reaction for 35 minutes. The prepolymer is further polymerized to form a capsule suspension slurry of graphene, ionic liquid, and dicyclopentadiene coated with wall materials. After filtering and drying at 65 degrees Celsius, the rubber-based electronic skin self-repairing special microcapsule material is obtained.

[0037] Mix 50g of the prepa...

Embodiment 2

[0039] (a). Prepare prepolymer in advance: prepare urea-formaldehyde resin prepolymer;

[0040] (b). 40g of graphene, 90g of halogenated 1-alkyl 3-methylimidazolium salt ionic liquid, and 40g of dicyclopentadiene were stirred and mixed uniformly at 50 rpm at 30 degrees Celsius to obtain a mixture, and then added to the mixture 50g of emulsifier Tuwen-80, and then dispersed under the action of ultrasound to obtain emulsion.

[0041] (c). Add 200g of the emulsion prepared in step (b) into the reaction vessel, slowly add 800g of the prepolymer prepared in step (a) under the condition of sufficient stirring, and raise the temperature to 60°C, keep warm and continue the reaction for 35 minutes. The prepolymer is further polymerized to form a capsule suspension slurry of graphene, ionic liquid, and dicyclopentadiene coated with wall materials. After filtering and drying at 65 degrees Celsius, the rubber-based electronic skin self-repairing special microcapsule material is obtained. ...

Embodiment 3

[0044] (a). Prepare prepolymer in advance: prepare melamine urea-formaldehyde resin prepolymer;

[0045] (b). 30g of graphene, 100g of 1-methyl-3-ethylimidazolium chloride ionic liquid, and 40g of dicyclopentadiene are stirred and mixed uniformly at 60 rpm at 25 degrees Celsius to obtain a mixture, and then in the mixture Add 50g of emulsifier Pingping plus OS-15, and then disperse under the action of ultrasound to obtain an emulsion.

[0046] (c). Add 200g of the emulsion prepared in step (b) into the reaction vessel, slowly add 800g of the prepolymer prepared in step (a) under the condition of sufficient stirring, and raise the temperature to 60°C, keep warm and continue the reaction for 35 minutes. The prepolymer is further polymerized to form a capsule suspension slurry of graphene, ionic liquid, and dicyclopentadiene coated with wall materials. After filtering and drying at 65 degrees Celsius, the rubber-based electronic skin self-repairing special microcapsule material i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of electronic skin self-repairing materials, in particular to a special micro-capsule material for electronic skin self-repairing and a preparation methodthereof. The preparation method comprises the following steps: (a). preparing a prepolymer in advance; (b) dispersing graphene, an ionic liquid, and dicyclopentadiene under the action of an emulsifierto obtain emulsion; (c). adding the emulsion prepared in step (b) to a reaction vessel, slowly adding the prepolymer prepared in step (a) under the condition of sufficient stirring, raising the temperature to 50 to 80 DEG C, holding and continuously reacting for at least 30 minutes, allowing the prepolymer to be further polymerized to form a capsule suspension slurry with a wall material coated with the graphene, ionic liquid and dicyclopentadiene, filtering and drying to obtain a rubber-based special micro-capsule material for electronic skin self-repairing. The micro-capsule material is mixed in inner and outer rubber base layers when preparing the electronic skin, and once the electronic skin is damaged, the capsule can realize the complete self-repairing function of the electronic skin.

Description

technical field [0001] The invention relates to the technical field of electronic skin self-repairing materials, in particular to a special microcapsule material for electronic skin self-repairing and a preparation method thereof. Background technique [0002] Human skin is an active, sensitive and highly elastic sensory organ that undertakes functions such as body protection, perspiration, temperature regulation, and perception of cold, heat, and pressure. The human somatosensory system can convert external environmental stimuli into electrical pulse signals through the skin's tactile, temperature, pain and other receptors, and transmit them to the nerve center through neural pathways, so that the skin can obtain sensory functions such as touch and pain. Based on the multifunctional biological model of the skin, scientists have carried out research on an emerging discipline - tactile electronics (commonly known as "electronic skin", Electronic skin, E-skin), which is used t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J13/18C09J4/00C09J11/04
CPCB01J13/185C09J4/00C09J11/04
Inventor 陈庆曾军堂
Owner CHENDU NEW KELI CHEM SCI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap