Coating used for expressway guardrails and preparation method thereof

A technology for highways and coatings, applied in anti-corrosion coatings, fire-proof coatings, polyester coatings, etc., can solve the problems of high cost and cumbersome process, and achieve the effect of low cost, high gloss, and easy spraying operation

Active Publication Date: 2018-10-02
BEIJING FAIRVIEW NEW TECH CO LTD
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of this, the present invention provides a coating for highway guardrails and a preparation method thereof, aiming at solving the problems of high cost of existing coatings for highway guardrails and cumbersome processes in surface treatment of highway guardrails

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The coating for expressway guardrail of the present invention comprises in parts by weight: 45g of water-based acrylic acid self-drying resin at room temperature, 0.1g of BYK902, 0.1g of BYK306, 0.2g of ethylene glycol, 30g of acetone, 5g of nano-aluminum powder, and 0.2g of R-760F , THIX-2780.2g;

[0029] Above-mentioned coating is prepared by following method:

[0030] 1) Mix BYK902, BYK306, ethylene glycol, acetone nano-aluminum powder and R-760F in parts by weight and disperse at 800rpm for 45min to obtain a dispersion;

[0031] Step 2) Add water-based acrylic acid self-drying resin at room temperature to the dispersion material in parts by weight and stir for 10 minutes, and add THIX-278 in parts by weight and continue stirring for 5 minutes to obtain the coating.

[0032] The prepared coatings were tested for performance, and the test indicators and results are shown in Table 1.

[0033] Table 1 embodiment test index, method and result

[0034] Test in...

Embodiment 2

[0037] The coating for expressway guardrail of the present invention comprises in parts by weight: 60 g of water-based self-drying alkyd resin, 0.2 g of BYK2015, 0.2 g of EFKA3777, 0.2 g of propylene glycol, 50 g of ethanol, 10 g of nano-silver aluminum powder, and 0.2 g of DH-7940, THIX-108 0.1g;

[0038] Above-mentioned coating is prepared by following method:

[0039] 1) Mix BYK2015, EFKA3777, propylene glycol, ethanol, nano-silver aluminum powder and DH-7940 in parts by weight and disperse at a speed of 1200rpm for 60min to obtain a dispersion;

[0040] Step 2) Add water-based self-drying alkyd resin to the dispersion material in parts by weight and stir for 10 minutes, and add THIX-108 in parts by weight and continue stirring for 5 minutes to obtain the coating.

[0041] The prepared coatings were tested for performance, and the test indicators and results are shown in Table 2.

[0042] Table 2 embodiment test index, method and result

[0043] Test indicators ...

Embodiment 3

[0046]The highway guardrail coating of the present invention comprises by weight: 50g of water-based self-drying epoxy resin, BYK1410.15g, BNK333 0.14g, isopropanol 0.1g, propylene glycol methyl ether 45g, nano aluminum silver paste 8g, FA- 179 0.16g, HD-2010.08g;

[0047] Above-mentioned coating is prepared by following method:

[0048] 1) Mix BYK141, BNK333, isopropanol, propylene glycol methyl ether, nano-aluminum silver paste and FA-179 in parts by weight and disperse at a speed of 1000rpm for 50min to obtain a dispersion liquid;

[0049] Step 2) Add water-based self-drying epoxy resin to the dispersion material in parts by weight and stir for 10 minutes, and add HD-201 in parts by weight and continue stirring for 5 minutes to obtain the coating.

[0050] The prepared coatings were tested for performance, and the test indicators and results are shown in Table 3.

[0051] Table 3 embodiment test index, method and result

[0052] Test indicators

[0053] As show...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a coating used for expressway guardrails and a preparation method thereof. The coating includes a resin base material, a dispersant, a leveling agent, a cosolvent, a solvent, anano-material, an anti-flash rust agent, and a defoamer. The preparation method includes the steps of: mixing and dispersing the dispersant, the leveling agent, the cosolvent, the solvent, the nano-material and the anti-flash rust agent to prepare a dispersion liquid; adding the resin base material into the dispersion liquid with stirring, and adding a defoaming agent and continuously stirring the mixture to obtain the coating. The preparation method is simple and is free of special large-size equipment. The coating can reach more than 9H in hardness, is wearing resistant and anti-scratching,has excellent electrical insulation property and is high temperature-resistant and ultraviolet aging-resistant, can prevent and resist fouling, and is convenient to clean. The coating is simple in spray coating operation and is free of detachment of the expressway guardrails. The coating is low in cost and is adjustable in drying speed after the spray coating operation.

Description

technical field [0001] The invention belongs to the field of chemical industry and relates to a coating, in particular to a coating for expressway guardrails and a preparation method thereof. Background technique [0002] The main form of expressway guardrail is semi-rigid guardrail, which is a continuous structure that is spliced ​​with corrugated steel guardrail panels and supported by main columns. [0003] The surface treatment of highway guardrails is divided into two types: hot-dip galvanizing and galvanizing and spraying: hot-dip galvanizing is to immerse the rust-removed steel parts in a zinc solution melted at about 500 ° C, so that the surface of the steel components is attached with a zinc layer, thereby creating a protective effect. For the purpose of anti-corrosion, the process flow is: pickling of finished products - water washing - adding auxiliary plating solution - drying - rack plating - cooling - chemical chemical - cleaning - grinding - hot-dip galvanizin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/04C09D167/08C09D175/04C09D201/00C09D175/02C09D163/00C09D183/04C09D5/10
CPCC08K2003/0812C08K2201/011C08L2201/08C08L2201/10C09D5/103C09D5/18C09D133/04C09D163/00C09D167/08C09D175/02C09D175/04C09D183/04C09D201/00C08K3/08
Inventor 苏斌
Owner BEIJING FAIRVIEW NEW TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com