A metal alloy-metal oxide dual magnetic shell-core structure nanocrystal and its preparation method and application

A shell-core structure and metal alloy technology, applied in the field of nanomaterials, can solve the problems of waste of reagents and consumables, cumbersome operation process, etc., and achieve the effects of expanding magnetic properties, simple process and saving time.

Active Publication Date: 2019-12-13
INST OF CHEM CHINESE ACAD OF SCI +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method requires multi-step synthesis, and the synthetic product of each step needs to be purified, the operation process is cumbersome and wastes reagent consumables

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A metal alloy-metal oxide dual magnetic shell-core structure nanocrystal and its preparation method and application
  • A metal alloy-metal oxide dual magnetic shell-core structure nanocrystal and its preparation method and application
  • A metal alloy-metal oxide dual magnetic shell-core structure nanocrystal and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0062] Embodiment 1, FePt@Fe 3 o 4 Preparation of Core-Shell Nanocrystals

[0063] Add 0.5mmol of platinum acetylacetonate, 1.5mmol of 1,2-hexadecanediol and 20mL of 1-octadecene into a 150mL three-necked flask, stir and mix evenly with a magnetic force at 1600rpm / min, vacuumize at 40°C for 30min, blow nitrogen, and add 1.6 mL oleic acid, 1.7 mL oleylamine, and 3 mmol iron acetylacetonate (platinum acetylacetonate: 1,2-hexadecanediol: iron acetylacetonate: oleic acid: oleylamine: 1-octadecene in a ratio of 1:3:6 :10:10:62.5), evacuate at 80°C for 30min, blow nitrogen, raise the temperature to 300°C, and reflux for 30min. Remove the heat source, cool to room temperature, then add an appropriate amount of ethanol, centrifuge at 6000r / min for 10min, take the precipitate, then add an appropriate amount of cyclohexane to dissolve the product, centrifuge again at 6000r / min for 10min, take the upper layer, and repeat ethanol The process of precipitation / cyclohexane dispersion was ...

Embodiment 2

[0066] Embodiment 2, FePt@Fe 3 o 4 Preparation of Core-Shell Nanocrystals

[0067] Add 0.1mmol of platinum acetylacetonate, 0.3mmol of 1,2-hexadecanediol and 20mL of 1-octadecene into a 150mL three-necked flask, stir and mix evenly with a magnetic force at 1600rpm / min, vacuumize at 40°C for 30min, blow nitrogen, and add 1.6 mL oleic acid, 1.7 mL oleylamine, and 2 mmol iron acetylacetonate (platinum acetylacetonate: 1,2-hexadecanediol: iron acetylacetonate: oleic acid: oleylamine: 1-octadecene in a ratio of 1:3:20 :50:50:312.5), vacuumize at 80°C for 30min, blow nitrogen, raise the temperature to 300°C, and reflux for 30min. Remove the heat source, cool to room temperature, then add an appropriate amount of ethanol, centrifuge at 6000r / min for 10min, take the precipitate, then add an appropriate amount of cyclohexane to dissolve the product, centrifuge again at 6000r / min for 10min, take the upper layer, and repeat ethanol The process of precipitation / cyclohexane dispersion w...

Embodiment 3

[0070] Embodiment 3, FePt@Fe 3 o 4 Preparation of Core-Shell Nanocrystals

[0071] Add 0.3mmol of platinum acetylacetonate, 0.9mmol of 1,2-hexadecanediol and 20mL of 1-hexadecene into a 150mL three-necked flask, stir and mix evenly with a magnetic force at 1600rpm / min, vacuumize at 40°C for 30min, blow nitrogen, and add 1.6 mL oleic acid, 1.7 mL oleylamine, and 3 mmol iron acetylacetonate (platinum acetylacetonate: 1,2-hexadecanediol: iron acetylacetonate: oleic acid: oleylamine: 1-octadecene in a ratio of 1:3:10 :16.7:16.7:104.2), vacuumize at 80°C for 30min, pass nitrogen gas, heat up to 300°C, and reflux for 30min. Remove the heat source, cool to room temperature, then add an appropriate amount of ethanol, centrifuge at 6000r / min for 10min, take the precipitate, then add an appropriate amount of cyclohexane to dissolve the product, centrifuge again at 6000r / min for 10min, take the upper layer, and repeat ethanol The process of precipitation / cyclohexane dispersion was per...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a metal alloy-metal oxide double magnetic core-shell structure nanocrystal, a preparation method and application thereof. It includes a core area and a shell layer, the shell layer covers the core area; the material forming the core area is metal alloy; the material forming the shell layer is metal oxide. The preparation method comprises the following steps: in the same reaction vessel, under the protection of an inert atmosphere, the precursor of the metal alloy and the precursor of the metal oxide are mixed, and the oil phase high-temperature thermal decomposition method is used to react to obtain the obtained The metal alloy-metal oxide double magnetic shell-core structure nanocrystal. The invention adopts a one-pot synthesis method, which can not only adjust the shell-core structure in terms of size and shape, but also can universally synthesize shell-core dual magnetic nanocrystals with different components; it has the characteristics of simplicity, high efficiency, and low cost, and can be prepared A large-scale synthesis of metal alloy-metal oxide double magnetic core-shell nanocrystals with good monodispersity and ultra-controllable magnetic properties.

Description

technical field [0001] The invention relates to a metal alloy-metal oxide double magnetic core-shell structure nanocrystal and a preparation method and application thereof, belonging to the technical field of nanomaterials. Background technique [0002] With the miniaturization of magnetic devices, the research of bimagnetic magnetic nanoparticles as the final structural unit has attracted more and more attention. At present, most research methods use the seed-generation method to prepare dual magnetic nanomaterials, that is, a nanocrystal is pre-synthesized, and then the nanocrystal is used as a seed to regenerate heterostructure nanoparticles. However, this method requires multi-step synthesis, and the synthetic product of each step needs to be purified, the operation process is cumbersome and wastes reagent consumables. Contents of the invention [0003] The purpose of the present invention is to provide a metal alloy-metal oxide double magnetic shell-core structure na...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F1/02B22F1/00B22F9/24B82Y30/00B82Y40/00H01F1/01H01F41/00
CPCH01F1/01H01F41/00B82Y30/00B82Y40/00B22F9/24B22F1/07B22F1/16