High-strength mould-proof woven band for suitcases and bags

A high-strength, anti-mildew technology, applied in textiles, fabrics, textiles and papermaking, etc., can solve the problems of reduced strength of luggage webbing, mildew of luggage and webbing, poor functional stability, etc., to avoid the accumulation of stains, easy to care, Antifungal stability effect

Inactive Publication Date: 2018-11-20
HEFEI SHENGDA GARMENT ACCESSORIES CO LTD
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Ribbon is a narrow or tubular fabric made of various yarns. There are many kinds of ribbons, which are widely used in clothing, shoe materials, luggage, industry, agriculture, military supplies, transportation and other industrial sectors. Luggage is in our It is widely used in daily life, and general luggage needs greater bearing capacity, so there will be higher requirements for the strength of the webbing of the luggage, and there are many types of items contained in the luggage, it is easy to cause damage to the luggage and webbing during use. Mildew will also lead to a decrease in the strength of the luggage webbing and a decrease in its bearing capacity
[0003] The existing patent document CN 102174749 A discloses a method for processing mildew-resistant and antibacterial webbing, specifically disclosing the use of 4.9-19.5 parts of water, 0.1-0.5 parts of heterocyclic derivative compounds, and 80-95 parts of spinning oil. The mixture is treated on the surface of the fiber in the oil cooling process above the polypropylene fiber forming process, so that the polypropylene fiber has the function of anti-mold and antibacterial, but the function obtained by this surface treatment is poor in stability, and the antibacterial function will be obvious after repeated washing weaken or even disappear

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength mould-proof woven band for suitcases and bags
  • High-strength mould-proof woven band for suitcases and bags

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A high-strength anti-mold luggage webbing is made of the following raw materials in parts by weight: 35 parts by weight of polychloride fiber, 30 parts of polyester, 24 modified viscose fiber, 21 ceramic fiber, 21 bamboo fiber, 13 carbon fiber and 10 modified cupro fiber.

[0019] For the modified viscose fiber, dissolve the cellulose xanthate obtained after plant cellulose treatment in a sodium hydroxide solution with a concentration of 40 mg / L, stir evenly, add hexamethylammonium bromide, and turn it clockwise at 10°C Stir and mix for 50 minutes, and wet spinning to obtain modified viscose fiber.

[0020] Described hexamethylammonium bromide, add-on is 0.03% of cellulose xanthate weight.

[0021] The modified cupro ammonia fiber, the hydrated cellulose obtained from the coagulation bath is placed in the hesperetin solution with a concentration of 30mg / L, soaked at 40°C for 2 hours, taken out, and spun to obtain the modified cupro ammonia fiber fiber.

[0022] A prep...

Embodiment 2

[0028] A high-strength mildew-proof luggage webbing is made of the following raw materials in parts by weight: 36 polychloride fibers, 31 polyester fibers, 25 modified viscose fibers, 22 ceramic fibers, 22 bamboo fibers, 14 carbon fibers, and 11 modified cupro fibers.

[0029] For the modified viscose fiber, the cellulose xanthate obtained after the plant cellulose treatment was dissolved in a sodium hydroxide solution with a concentration of 45 mg / L, stirred evenly, and hexamethylammonium bromide was added, and the mixture was clockwise at 13°C. Stir and mix for 55 minutes, and wet-spin to obtain modified viscose fiber.

[0030] Described hexamethylammonium bromide, add-on is 0.04% of cellulose xanthate weight.

[0031] For the modified cupro fiber, the hydrated cellulose obtained from the coagulation bath is placed in a hesperetin solution with a concentration of 35 mg / L, soaked at 45°C for 3 hours, taken out, and spun to obtain modified cupro fiber.

[0032] A preparation...

Embodiment 3

[0038] A high-strength mildew-proof luggage webbing is made of the following raw materials in parts by weight: 37 polychloride fibers, 32 polyester fibers, 26 modified viscose fibers, 23 ceramic fibers, 23 bamboo fibers, 15 carbon fibers, and 12 modified cupro fibers.

[0039] For the modified viscose fiber, the cellulose xanthate obtained after the treatment of plant cellulose was dissolved in a sodium hydroxide solution with a concentration of 50 mg / L, stirred evenly, and hexamethylammonium bromide was added, clockwise at 15°C Stir and mix for 60 minutes, and wet-spin to obtain modified viscose fiber.

[0040] Described hexamethylammonium bromide, add-on is 0.05% of cellulose xanthate weight.

[0041] For the modified cupro fiber, the hydrated cellulose obtained from the coagulation bath is placed in a hesperetin solution with a concentration of 40 mg / L, soaked at 50°C for 3 hours, taken out, and spun to obtain modified cupro fiber.

[0042] A preparation method for a high...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention mainly relates to the technical field of textile processing, and discloses a high-strength mould-proof woven band for suitcases and bags. The woven band is prepared from 35-37 of polyvinyl chloride fibers, 30-32 of terylene, 24-26 of modified viscose, 21-23 of ceramic fiber, 21-23 od bamboo fiber, 13-15 of carbon fiber and 10-12 of modified copper ammonia fiber; according to the high-strength mould-proof woven band for suitcases and bags, the preparation method is simple, the strength of the obtained woven band is high, antimicrobial and mould-proof functions are achieved, the durability is high, the phenomenon that the suitcase and bag bodies are integral, but the woven bands fracture is avoided, and the using life of suitcases and bags is prolonged; the polyvinyl chloride fibers, the terylene and the ceramic fiber are subjected to blending to prepare internal layer yarns, the fracturing strength of the woven band can be strengthened, the adsorbability of fibers is improved, and the anti-bacteria and mould-proof effects are enhanced.

Description

technical field [0001] The invention mainly relates to the technical field of textile processing, in particular to a high-strength mildew-proof luggage webbing. Background technique [0002] Ribbon is a narrow or tubular fabric made of various yarns. There are many kinds of ribbons, which are widely used in clothing, shoe materials, luggage, industry, agriculture, military supplies, transportation and other industrial sectors. Luggage is in our It is widely used in daily life, and general luggage needs greater bearing capacity, so there will be higher requirements for the strength of the webbing of the luggage, and there are many types of items contained in the luggage, it is easy to cause damage to the luggage and webbing during use. Mildew will also lead to a decrease in the strength of the luggage webbing and a decrease in its bearing capacity. [0003] The existing patent document CN 102174749 A discloses a method for processing mildew-resistant and antibacterial webbin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D03D1/00D02G3/44D02G3/38D02G3/16D02G3/04D01F2/08D06M11/46
CPCD03D1/0094D01F2/08D02G3/04D02G3/16D02G3/38D02G3/449D06M11/46D06M16/00D10B2101/08D10B2101/12D10B2201/10D10B2201/22D10B2201/24D10B2321/041D10B2331/04D10B2401/063D10B2401/13D10B2401/14
Inventor 郭运松
Owner HEFEI SHENGDA GARMENT ACCESSORIES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap