A kind of environment-friendly waterborne epoxy coal tar pitch anticorrosion coating and preparation method thereof
An epoxy coal tar pitch, environment-friendly technology, applied in the direction of anti-corrosion coatings, asphalt coatings, coatings, etc., can solve the problems of high VOC, danger, acid and alkali resistance, etc., achieve excellent water resistance, improve mixing efficiency, high The effect of bond strength
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0024] The ratio of the mass parts of the component that present embodiment 1 adopts is as follows:
[0025] Group A: 29.2% of low molecular weight 618 liquid epoxy polymer with epoxy equivalent of 184-200, 23.0% of 660A epoxy resin reactive diluent with epoxy equivalent of 140-167, solid coal tar pitch 35.4%, potassium aluminum silicate 12.4 %;
[0026] Group B: water emulsion aromatic amine curing agent 70.0%, water 29.0%, anti-flash rust additive 1.0%. The mass ratio is: Group A: Group B: = 48:52, and the specific preparation method is as follows:
[0027] Step 1: Preparation of finished product containing epoxy coal tar pitch A component: crushing mass parts is 35.4% solid coal tar pitch; 23.0 mass parts of 660A epoxy resin active diluent with epoxy equivalent 140-167, after pulverizing Add the solid coal tar pitch into the dissolution kettle respectively, heat the jacket of the dissolution kettle to 60°C-80°C, stir and dissolve at a high speed (speed ≥ 800 rpm) to form ...
Embodiment 2
[0031] The ratio of the mass parts of the component that present embodiment 2 adopts is as follows:
[0032] Group A: 30.2% of low molecular weight 618 liquid epoxy polymer with epoxy equivalent of 184-200, 24.5% of 660A epoxy resin reactive diluent with epoxy equivalent of 140-167, solid coal tar pitch 37.7%, potassium aluminum silicate 7.6 %;
[0033] Group B: water emulsion aromatic amine curing agent 86.4%, water 12.6%, anti-flash rust additive 1.0%. The mass ratio is: Group A: Group B: = 53:47, and the specific preparation method is as follows:
[0034] Step 1: Preparation of finished product containing epoxy coal tar pitch A component: pulverized mass parts are 37.7% solid coal tar pitch; Add the solid coal tar pitch to the dissolution kettle respectively, heat the jacket of the dissolution kettle to 60°C-80°C, stir and dissolve at high speed (speed ≥ 800 rpm) to form a uniform viscous liquid, filter it for later use; then add the above viscous liquid to 30.2% by mass...