Composite wood fire retardant for teaching toys

A flame retardant and wood technology, applied in wood treatment, wood impregnation, wood impregnation, etc., can solve problems such as insufficient flame retardant performance, achieve good flame retardant effect, improve carbon formation rate, and increase carbon formation effect.

Inactive Publication Date: 2018-12-04
钱学华
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing flame retardants have the defect of insufficient performance, and cannot meet people's use needs.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A composite wood flame retardant for teaching toys, which comprises the following components by weight and is prepared by stirring, heating, heating, heat preservation and cooling: 1 part of ammonium sulfate, 1 part of magnesium hydroxide, 5 parts of aluminum hydroxide, super 2 parts of fine zinc borate, 3 parts of sodium molybdate, 2 parts of urea, 5 parts of castor oil, 10 parts of ammonium polyphosphate coated with epoxy resin, 5 parts of dibutyl phthalate, 4 parts of bis fumarate 8 parts of sodium carbonate, 5 parts of carbon forming accelerator, 4 parts of smoke suppressant, 20 parts of dicyandiamide, and 35 parts of water.

[0015] The carbon-forming accelerator is a composition of silicon dioxide and titanium dioxide, and the weight ratio of the two is 1.5-2.8:1.6-3.2.

[0016] The smoke suppressant is a combination of nickel silicate and manganese silicate, and the weight ratio of the two is 1.5-3.8:3.5-5.5.

[0017] During the heating process, the temperature ...

Embodiment 2

[0019] A composite wood flame retardant for teaching toys, which comprises the following components by weight and is prepared by stirring, heating, heating, heat preservation and cooling: 3 parts of ammonium sulfate, 5 parts of magnesium hydroxide, 8 parts of aluminum hydroxide, super 5 parts of fine zinc borate, 5 parts of sodium molybdate, 5 parts of urea, 8 parts of castor oil, 13 parts of ammonium polyphosphate coated with epoxy resin, 9 parts of dibutyl phthalate, 6 parts of bis fumarate 8-10 parts of sodium carbonate, 9 parts of carbon forming accelerator, 9 parts of smoke suppressant, 35 parts of dicyandiamide, and 45 parts of water.

[0020] The carbon-forming accelerator is a composition of silicon dioxide and titanium dioxide, and the weight ratio of the two is 1.5-2.8:1.6-3.2.

[0021] The smoke suppressant is a combination of nickel silicate and manganese silicate, and the weight ratio of the two is 1.5-3.8:3.5-5.5.

[0022] During the heating process, the tempera...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a composite wood fire retardant for teaching toys, belonging to the technical field of fire retardants. In the flame retardant of the invention, epoxy resin coated ammonium polyphosphate integrates a carbon source and an acid source into one, so the compatibility between the flame retardant and a polymer matrix is improved; a carbon formation promoter improves the carbon formation speed and the carbon formation amount of the flame retardant, so high flame retardant efficiency is obtained; metal compounds consisting of magnesium hydroxide, aluminum hydroxide and ultrafinezinc borate are used as inorganic flame retardants and have the advantages of no toxicity, no harm and no smoke, and through synergism with other components, flame retardant efficiency is improved, the amount of smoke exhausted during the combustion of the flame retardant is reduced, the flammability of the flame retardant is suppressed, and the flame retardant is allowed to only undergo carbonization and not to burn when taking effect. The wood flame retardant of the invention has good flame retarding effect, no toxicity, no smoke, no harm to environment and human beings and good stability.

Description

technical field [0001] The invention relates to a composition of a fire retardant, in particular to a composition of a composite wood fire retardant for educational toys, and belongs to the technical field of fire retardants. Background technique [0002] Teaching toys are toys used in conjunction with teaching. They are mainly used in kindergartens, primary and secondary school labor skills classes, experimental classes and extracurricular sports activities. The material is mainly composite wood. [0003] Due to the excessive use of wood by humans, the number of wood is getting smaller and smaller, so artificial composite wood has emerged as the times require. Composite wood boards have a low ignition point and are flammable materials, and the requirements for people's fire protection are more stringent. Composite wood flame retardant is an additive that prevents wood from being ignited and inhibits flame propagation, and has a wide range of applications. However, the exi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27K3/52
CPCB27K3/52B27K2240/30
Inventor 钱学华
Owner 钱学华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com