Insect-proof and moisture-proof wooden veneer

A wood veneer and insect-proof technology, applied in wood processing appliances, household components, flat products, etc., can solve the problems of mildew, poor moisture-proof performance, single performance, etc., to reduce the generation of static charge, strong insulation and heat resistance Sexuality, smell cool and strong effect

Inactive Publication Date: 2018-12-07
湖州韵高木业有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Common decorative panels are divided into natural wood veneer veneer and artificial veneer veneer. Due to the high raw material cost of natural wood veneer, its performance is single. At present, the research on artificial veneer veneer has become the main direction of the development of decorative panels. The production of artificial veneer veneer is also increasing year by year; the existing artificial veneer veneer has poor anti-insect effect, and the interior is prone to moths, and various insect eggs are easy to be laid on the surface after long-term use, which not only affects the appearance, but also It will also cause pollution to the indoor environment; veneer panels are mostly used for interior decoration. During the rainy season in the south from June to July, the air humidity is high, and the indoor wood veneer panels are prone to moisture, and then moldy or swell, which affects the appearance.
Therefore, the existing wood veneer has the problems of poor insect-proof performance, easy moth-eaten, poor moisture-proof performance, and easy moldy problems.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Embodiment 1: an insect-proof and moisture-proof wood veneer, comprising the following components by weight: pine bark, 35 parts; beech wood shavings, 15 parts; camphor wood powder, 1 part; mica powder, 4 parts; nano-alumina powder, 0.5 parts; glass fiber, 0.8 parts; flame retardant, 4 parts; adhesive, 6 parts; desiccant, 5 parts.

[0015] The flame retardant includes magnesium oxide, aluminum hydroxide and zinc borate, and the ratio of parts by weight of magnesium oxide, aluminum hydroxide and zinc borate is 1:1.2:0.8.

[0016] The adhesive is 563 urea-formaldehyde resin glue.

[0017] The desiccant is an activated carbon desiccant, and the mesh number of the activated carbon desiccant is 300 mesh.

Embodiment 2

[0018] Embodiment 2: An insect-proof and moisture-proof wood veneer comprises the following components by weight: pine bark, 55 parts; beech wood shavings, 25 parts; camphor wood powder, 3 parts; mica powder, 8 parts; nano-alumina powder, 1.5 parts; glass fiber, 2.2 parts; flame retardant, 10 parts; adhesive, 12 parts; desiccant, 8 parts.

[0019] The flame retardant includes magnesium oxide, aluminum hydroxide and zinc borate, and the ratio of parts by weight of magnesium oxide, aluminum hydroxide and zinc borate is 1:1.2:0.8.

[0020] The adhesive is 563 urea-formaldehyde resin glue.

[0021] The desiccant is an activated carbon desiccant, and the mesh number of the activated carbon desiccant is 300 mesh.

Embodiment 3

[0022] Embodiment 3: an insect-proof and moisture-proof wood veneer, comprising the following components by weight: pine bark, 45 parts; beech shavings, 20 parts; camphor wood powder, 2 parts; mica powder, 6 parts; nano-alumina powder, 1.1 parts; glass fiber, 1.8 parts; flame retardant, 7 parts; adhesive, 9 parts; desiccant, 6.5 parts.

[0023] The flame retardant includes magnesium oxide, aluminum hydroxide and zinc borate, and the ratio of parts by weight of magnesium oxide, aluminum hydroxide and zinc borate is 1:1.2:0.8.

[0024] The adhesive is 563 urea-formaldehyde resin glue.

[0025] The desiccant is an activated carbon desiccant, and the mesh number of the activated carbon desiccant is 300 mesh.

[0026] A production process of an insect-proof and moisture-proof wood veneer, comprising the following steps:

[0027] A, get 45 parts of pine bark, soak 0.5-1.5h with the sodium hydroxide solution of 20-30% with mass fraction, wash with distilled water, and dry, grind in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an insect-proof and moisture-proof wooden veneer. The wooden veneer comprises the following components of, by weight, 35-55 parts of pine bark, 15-25 parts of beech shavings, 1-3 parts of camphorwood powder, 4-8 parts of mica powder, 0.5-1.5 parts of nano aluminum oxide powder, 0.8-2.2 parts of glass fiber, 4-10 parts of flame retardants, 6-12 parts of adhesives and 5-8 parts of drying agents. The wooden veneer has the advantages of being good in insect-proof performance, not prone to worm damage, good in moisture-proof performance and not prone to mildewing.

Description

technical field [0001] The invention relates to a wooden glued decorative panel, in particular to an insect-proof and moisture-proof wood veneer. Background technique [0002] Common decorative panels are divided into natural wood veneer veneer and artificial veneer veneer. Due to the high raw material cost of natural wood veneer, its performance is single. At present, the research on artificial veneer veneer has become the main direction of the development of decorative panels. The production of artificial veneer veneer is also increasing year by year; the existing artificial veneer veneer has poor anti-insect effect, and the interior is prone to moths, and various insect eggs are easy to be laid on the surface after long-term use, which not only affects the appearance, but also It will also cause pollution to the indoor environment; veneer panels are mostly used for interior decoration. During the rainy season in the south from June to July, the air humidity is high, and t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27N3/02B27N3/10B27N3/14E04F13/075
CPCB27N3/02B27N3/10B27N3/14E04F13/075
Inventor 钱雪峰
Owner 湖州韵高木业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com