Method for preparing insect-resistant damp-proof wood veneer

A wood veneer and insect-proof technology, applied in the direction of manufacturing tools, wood treatment, wood processing appliances, etc., can solve the problems of high air humidity, mildew, and high cost, achieve strong insulation and heat resistance, and reduce the generation of static charges , the effect of good elasticity and toughness

Inactive Publication Date: 2019-01-04
湖州韵高木业有限公司
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Common decorative panels are divided into natural wood veneer veneer and artificial veneer veneer. Due to the high raw material cost of natural wood veneer, its performance is single. At present, the research on artificial veneer veneer has become the main direction of the development of decorative panels. The production of artificial veneer veneer is also increasing year by year. The preparation of existing artificial veneer veneer is generally to mix several kinds of raw materials and then hot press molding. The process is simple, and the treatment effect on insect repelling is poor. It is easy to be moth-eaten, and after a long time of use, it is easy to lay various insect eggs on its surface, which not only affects the appearance, but also pollutes the indoor environment; the decorative panels are mostly used for interior decoration, and in the rainy season from June to July in the south In seasons, the air humidity is high, and the existing wood veneer preparation process has poor moisture-proof treatment effect. The indoor wood veneer is easy to become damp, and then moldy or swells, which affects the appearance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Embodiment 1: A kind of preparation method of insect-proof and moisture-proof wooden veneer, each raw material is measured in parts by mass, comprising the following steps:

[0021] A, get 45 parts of pine bark, soak 0.5h with the sodium hydroxide solution of 20-30% with mass fraction, wash with distilled water, and dry, grind into pine powder;

[0022] B, get 20 parts of beech wood shavings, soak 1h with the sodium hydroxide solution of 15-20% with mass fraction, wash with distilled water, and dry, grind into beech wood powder;

[0023] C. Put the pine wood powder in step A and the beech wood powder in step B into the mixing barrel and mix evenly, add 12 parts of distilled water and stir, and stir to form a paste mixture. During the stirring process, add 2 parts of camphor wood powder, 6 parts Mica powder, 1.1 parts of nano-alumina powder and 1.8 parts of glass fiber, the stirring speed is 1800r / min, and the stirring time is 30min;

[0024] D. Add 7 parts of flame ret...

Embodiment 2

[0032] Embodiment 2: A preparation method of an insect-proof and moisture-proof wood veneer, each raw material is measured in parts by mass, comprising the following steps:

[0033] A, get 45 parts of pine bark, soak 1.5h with the sodium hydroxide solution of 20-30% with mass fraction, wash with distilled water, and dry, grind into pine powder;

[0034] B, get 20 parts of beech wood shavings, soak 1.5h with the sodium hydroxide solution of 15-20% with mass fraction, wash with distilled water, and dry, grind into beech wood powder;

[0035] C. Put the pine wood powder in step A and the beech wood powder in step B into the mixing barrel and mix evenly, add 12 parts of distilled water and stir, and stir to form a paste mixture. During the stirring process, add 2 parts of camphor wood powder, 6 parts Mica powder, 1.1 parts of nano-alumina powder and 1.8 parts of glass fiber, the stirring speed is 2200r / min, and the stirring time is 50min;

[0036] D. Add 7 parts of flame retardan...

Embodiment 3

[0044] Embodiment 3: A preparation method of an insect-proof and moisture-proof wood veneer, each raw material is measured in parts by mass, comprising the following steps:

[0045] A, get 45 parts of pine bark, soak 1h with the sodium hydroxide solution of 20-30% with mass fraction, wash with distilled water, and dry, grind into pine wood powder;

[0046] B, get 20 parts of beech wood shavings, soak 1.2h with the sodium hydroxide solution of 15-20% with mass fraction, wash with distilled water, and dry, grind into beech wood powder;

[0047] C. Put the pine wood powder in step A and the beech wood powder in step B into the mixing barrel and mix evenly, add 12 parts of distilled water and stir, and stir to form a paste mixture. During the stirring process, add 2 parts of camphor wood powder, 6 parts Mica powder, 1.1 parts of nano-alumina powder and 1.8 parts of glass fiber, the stirring speed is 2000r / min, and the stirring time is 40min;

[0048] D. Add 7 parts of flame retarda...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing insect-resistant damp-proof wood veneer. The method includes steps of A, grinding pine bark to obtain pine powder; B, grinding beech shavings to obtain beech powder; C, placing the pine powder and the beech powder into stirring barrels, uniformly mixing the pine powder and the beech powder with each other to obtain first mixtures, adding distilled water into the first mixtures, stirring the distilled water and the first mixtures, and sequentially adding camphor wood powder, mica powder, nanometer aluminum oxide powder and glass fibers into the distilled water and the first mixtures in stirring procedures to obtain second mixtures; D, sequentially adding flame retardants, adhesive and drying agents into the stirring barrels, stirring the flameretardants, the adhesive, the drying agents and the second mixtures and filling the stirring barrels with nitrogen in stirring procedures; E, pouring materials obtained at the step D into molds, carrying out compression molding by the aid of molding machines and carrying out mold release to obtain wood veneer semi-finished products; F, placing the wood veneer semi-finished products obtained at thestep E into drying ovens and carrying out drying treatment to obtain wood veneer finished products. The method has the advantage that excellent insect-resistant effects and excellent damp-proof effects can be realized by the insect-resistant damp-proof wood veneer prepared by the aid of the method.

Description

technical field [0001] The invention relates to a preparation process of a wooden glued decorative panel, in particular to a preparation method of an insect-proof and moisture-proof wood veneer. Background technique [0002] Common decorative panels are divided into natural wood veneer veneer and artificial veneer veneer. Due to the high raw material cost of natural wood veneer, its performance is single. At present, the research on artificial veneer veneer has become the main direction of the development of decorative panels. The production of artificial veneer veneer is also increasing year by year. The preparation of existing artificial veneer veneer is generally to mix several kinds of raw materials and then hot press molding. The process is simple, and the treatment effect on insect repelling is poor. It is easy to be moth-eaten, and after a long time of use, it is easy to lay various insect eggs on its surface, which not only affects the appearance, but also pollutes t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L61/24C08L97/02C08K13/04C08K3/34C08K3/22C08K7/14C08K3/38C08K7/24H01B3/36B27K3/04B27K5/04B27L11/06
CPCB27K3/04B27K5/04B27L11/06C08K2003/222C08K2003/2227C08K2003/387C08K2201/011C08L61/24C08L2201/02C08L2201/08C08L2205/025C08L2205/03H01B3/36C08L97/02C08K13/04C08K3/34C08K3/22C08K7/14C08K3/38C08K7/24
Inventor 钱雪峰
Owner 湖州韵高木业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products