Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Preparation method of durable anti-slip paint

A non-slip coating and durable technology, applied in polyamide coatings, epoxy resin coatings, coatings, etc., can solve the problems that the anti-slip performance cannot be further improved, poor wear resistance, etc., and achieve improved anti-slip performance and improved adsorption performance , the effect of roughness enhancement

Inactive Publication Date: 2018-12-07
袁杰
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem mainly solved by the present invention is: aiming at the problem that the traditional anti-skid coating has poor wear resistance and the anti-skid performance cannot be further improved, a preparation method of durable anti-skid coating is provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0022]Put talcum powder, alumina, and titanium dioxide in a ball mill at a mass ratio of 1:1:1, and pass through a 90-mesh sieve to obtain a mixed filler; mix gelatin and water in a No. 1 beaker at a mass ratio of 50, and use a glass rod to Stir for 20 minutes, and place the No. 1 beaker in a magnetic stirrer with digital display speed measurement and constant temperature. Under the conditions of temperature 85°C and rotation speed 500r / min, heat and stir to dissolve for 50 minutes to obtain gelatin solution; mix glass beads with a mass fraction of 40% sodium hydroxide solution is placed in a single-necked flask with a mass ratio of 1:20, and the single-necked flask is placed in an ultrasonic disperser. The volume of sodium solution is 0.3 times the dopamine solution with a mass concentration of 2.6g / L. Under the condition of ultrasonic frequency of 75kHz, continue to ultrasonically disperse for 50min to obtain an impregnating solution, and then filter the impregnating solution...

example 2

[0024] Put talcum powder, alumina, and titanium dioxide in a ball mill at a mass ratio of 1:1:1, and pass through a 90-mesh sieve to obtain a mixed filler; mix gelatin and water in a No. 1 beaker at a mass ratio of 50, and use a glass rod to Stir for 20 minutes, and place the No. 1 beaker in a magnetic stirrer with digital display speed measurement and constant temperature. Under the conditions of temperature 85°C and rotation speed 500r / min, heat and stir to dissolve for 50 minutes to obtain gelatin solution; mix glass beads with a mass fraction of 40% sodium hydroxide solution is placed in a single-necked flask with a mass ratio of 1:20, and the single-necked flask is placed in an ultrasonic disperser. The volume of sodium solution is 0.3 times the dopamine solution with a mass concentration of 2.6g / L. Under the condition of ultrasonic frequency of 75kHz, continue to ultrasonically disperse for 50min to obtain an impregnating solution, and then filter the impregnating solutio...

example 3

[0026] Put talcum powder, alumina, and titanium dioxide in a ball mill at a mass ratio of 1:1:1, and pass through a 90-mesh sieve to obtain a mixed filler; mix gelatin and water in a No. 1 beaker at a mass ratio of 50, and use a glass rod to Stir for 20 minutes, and place the No. 1 beaker in a magnetic stirrer with digital display speed measurement and constant temperature. Under the conditions of temperature 85°C and rotation speed 500r / min, heat and stir to dissolve for 50 minutes to obtain gelatin solution; mix glass beads with a mass fraction of 40% sodium hydroxide solution is placed in a single-necked flask with a mass ratio of 1:20, and the single-necked flask is placed in an ultrasonic disperser. The volume of sodium solution is 0.3 times the dopamine solution with a mass concentration of 2.6g / L. Under the condition of ultrasonic frequency of 75kHz, continue to ultrasonically disperse for 50min to obtain an impregnating solution, and then filter the impregnating solutio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

Belonging to the technical field of building materials, the invention discloses a preparation method of a durable anti-slip paint. The preparation method includes: by weight, mixing 10-20 parts of polyamide resin, 30-40 parts of acetone, 8-10 parts of a curing agent, 5-8 parts of a defoamer and 5-8 parts of silicon resin to obtain a No.1 mixed slurry; by weight, mixing 30-40 parts of epoxy resin,70-80 parts of a solvent, 5-8 parts of tung oil, 5-8 parts of pigment and 20-30 parts of mixed filler to obtain a No.2 mixed slurry; and by weight, mixing 20-30 parts of the No.1 mixed slurry, 60-80 parts of the No.2 mixed slurry and 30-40 parts of modified glass beads to obtain the durable anti-slip paint. The durable anti-slip paint provided by the invention has excellent wear resistance and slip resistance.

Description

technical field [0001] The invention discloses a preparation method of a durable anti-skid coating, which belongs to the technical field of building materials. Background technique [0002] Anti-slip coatings are no strangers to people, and anti-slip floors can be seen on pedestrian bridges, stadiums, ship decks, offshore platforms, and floating bridges on water. Anti-slip property is the basic characteristic of anti-slip coating, and it is a special property of coating film. Anti-slip coatings mainly contain anti-slip granules, film-forming resins and other substances. Anti-slip granules are additives to improve the anti-slip performance of the paint film, endow the paint film with anti-slip ability, and prevent people from slipping and falling; the film-forming resin has the function of fixing the anti-slip granules , while protecting the substrate from damage. [0003] The development and utilization of anti-skid coatings has a history of many years. The base material ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D177/00C09D183/04C09D7/62
CPCC08L2205/025C08L2205/035C09D7/62C09D163/00C08L77/00C08L83/04C08K9/10C08K9/02C08K9/08C08K7/20
Inventor 袁杰朱冬梅张烨
Owner 袁杰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com