Waste rubber composite modified asphalt waterproof material and preparation method thereof

A technology for compounding modified asphalt and waste rubber, which can be used in building thermal insulation materials, asphalt layered products, chemical instruments and methods, etc., and can solve the problems of high temperature stability, low temperature crack resistance, aging resistance and poor durability. , to achieve the effect of improving compatibility, improving stability and cross-linking, and excellent high temperature stability

Inactive Publication Date: 2018-12-11
芜湖市颂晖商贸有限公司
View PDF9 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The invention provides a waste rubber composite modified asphalt waterproof material and its preparation method, which solves the problem of poor high temperature stability, low temperature crack resistance, aging resistance and durability of existing waste rubber powder and asphalt modified waterproof coiled materials And other issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waste rubber composite modified asphalt waterproof material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A waste rubber composite modified asphalt waterproofing material, from top to bottom: an upper surface isolation layer, an upper polymer modified asphalt layer, a base layer, a lower polymer modified asphalt layer and a lower surface isolation layer; The upper polymer-modified asphalt layer and the lower polymer-modified asphalt layer are made of waste rubber compound modified asphalt,

[0023] The upper surface isolation layer is a mineral particle layer; the lower surface isolation layer is a PE film; the base layer is a glass fiber reinforced polyester felt.

[0024] The waste rubber composite modified asphalt, in parts by weight, includes 65 parts of petroleum asphalt, 20 parts of SBS rubber, 5 parts of SIS rubber, 10 parts of waste rubber powder, 2 parts of asphalt modifier, and 1 part of modified asphalt stabilizer 0.1 part of graphene, 3 parts of sulfur, 0.5 part of petroleum sulfonate, 2 parts of succinic anhydride, 1 part of wood vinegar, 4 parts of inorganic f...

Embodiment 2

[0031] A waste rubber composite modified asphalt waterproofing material, from top to bottom: an upper surface isolation layer, an upper polymer modified asphalt layer, a base layer, a lower polymer modified asphalt layer and a lower surface isolation layer; The upper polymer-modified asphalt layer and the lower polymer-modified asphalt layer are made of waste rubber compound modified asphalt,

[0032] The upper surface isolation layer is a mineral particle layer; the lower surface isolation layer is a PE film; the base layer is a glass fiber reinforced polyester felt.

[0033] The waste rubber composite modified asphalt, in parts by weight, includes 60 parts of petroleum asphalt, 10 parts of SBS rubber, 8 parts of SIS rubber, 18 parts of waste rubber powder, 2 parts of asphalt modifier, and 2 parts of modified asphalt stabilizer 0.2 parts of graphene, 2 parts of sulfur, 0.7 parts of petroleum sulfonate, 1 part of succinic anhydride, 2 parts of wood vinegar, 3 parts of inorgani...

Embodiment 3

[0040] A waste rubber composite modified asphalt waterproofing material, from top to bottom: an upper surface isolation layer, an upper polymer modified asphalt layer, a base layer, a lower polymer modified asphalt layer and a lower surface isolation layer; The upper polymer-modified asphalt layer and the lower polymer-modified asphalt layer are made of waste rubber compound modified asphalt,

[0041] The upper surface isolation layer is a mineral particle layer; the lower surface isolation layer is a PE film; the base layer is a glass fiber reinforced polyester felt.

[0042] The waste rubber composite modified asphalt, in parts by weight, includes 70 parts of petroleum asphalt, 15 parts of SBS rubber, 10 parts of SIS rubber, 20 parts of waste rubber powder, 3 parts of asphalt modifier, 3 parts of modified asphalt stabilizer 0.3 parts of graphene, 1 part of sulfur, 0.8 parts of petroleum sulfonate, 3 parts of succinic anhydride, 3 parts of wood vinegar, 5 parts of inorganic fil...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a waste rubber composite modified asphalt waterproof material and a preparation method thereof. The waste rubber composite modified asphalt waterproof material sequentially comprises an upper surface isolation layer, an upper polymer modified asphalt layer, a tire basic layer, a lower polymer modified asphalt layer and a lower surface isolation layer from top to bottom, wherein the upper polymer modified asphalt layer and the lower polymer modified asphalt layer are prepared from waste rubber composite modified asphalt; the waste rubber composite modified asphalt is prepared form the following raw materials in parts by weight: 60 to 70 parts of petroleum asphalt, 10 to 20 parts of SBS (Styrene Butadiene Styrene) rubber, 5 to 10 parts of SIS (Styrene Isoprene Styrene) rubber, 10 to 20 parts of waste rubber powder, 2 to 3 parts of an asphalt modifier, 1 to 3 parts of a modified asphalt stabilizer, 0.1 to 0.3 part of graphene, 1 to 3 parts of sulfur, 0.5 to 0.8 part of petroleum sulfonate, 1 to 3 parts of succinic anhydride, 1 to 3 parts of wood vinegar, 3 to 5 parts of inorganic filler and 1 to 3 parts of metal oxide. According to the waste rubber composite modified asphalt waterproof material and the preparation method thereof, disclosed by the invention, an asphalt modification compatilizer is preferably selected, the compatibility of the waste rubber powder and the asphalt is effectively increased, and the prepared waterproof material has excellent high-temperature stability, excellent low-temperature crack resistance, aging resistance, durabilityand the like.

Description

technical field [0001] The invention relates to a waste rubber composite modified asphalt waterproof material and a preparation method thereof, belonging to the field of asphalt waterproof coiled materials. Background technique [0002] SBS modified bitumen waterproofing membrane refers to polyester felt or glass fiber felt as base, styrene-butadiene-styrene (SBS) copolymerized thermoplastic elastomer modified bitumen as coating material, both sides covered with polyester Modified bitumen waterproofing membrane made of vinyl film, fine sand or mineral aggregates. However, the modification by SBS is costly and unfavorable for popularization and use. At present, the production of a large number of automobile waste tires is increasing and the waste rubber particles obtained by crushing them can be used as modifiers to improve the performance of asphalt in various aspects, which not only solves the pollution problem caused by waste tires, but also can achieve waste The recycli...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B9/00B32B9/04B32B11/00B32B11/10B32B17/02B32B27/02B32B27/36B32B11/04B32B27/32B32B27/30C08L95/00C08L53/02C08L19/00C08K13/02C08K3/36C08K3/34C08K3/22C08K3/04
CPCB32B5/16B32B5/02B32B5/08B32B11/00B32B11/04B32B11/10B32B11/12B32B27/30B32B27/32B32B27/36B32B2262/0276B32B2262/101B32B2262/14C08K2003/2227C08K2003/2296C08K2201/011C08L95/00C08L2201/08C08L2205/025C08L2205/035C08L53/02C08L19/003C08K13/02C08K3/36C08K3/346C08K3/22C08K3/042
Inventor 汪琦郭元
Owner 芜湖市颂晖商贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com