Wood-plastic profile prepared from added samarskite tailing powder and application of wood-plastic profile

A technology for wood-plastic profiles and tailings powder, applied in the field of wood-plastic profiles, can solve problems such as application limitations, and achieve the effects of wide source of raw materials, simple and convenient preparation, and low cost

Inactive Publication Date: 2018-12-21
HEFEI LONGYANG AGRI TECH CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This kind of wood-plastic composite material has good degradability, low carbon and environmental protection, but its applicability is limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wood-plastic profile prepared from added samarskite tailing powder and application of wood-plastic profile
  • Wood-plastic profile prepared from added samarskite tailing powder and application of wood-plastic profile
  • Wood-plastic profile prepared from added samarskite tailing powder and application of wood-plastic profile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] This embodiment relates to a wood-plastic profile added with niobium-yttrium tailings powder and a preparation method thereof. The wood-plastic profile consists of the following raw materials in parts by weight:

[0046] Polyvinyl chloride resin powder SG-4 72 parts;

[0047] 12 parts of hydroxypropyl methacrylate;

[0048] 34 parts palm leaf fiber;

[0049] 10 parts of niobium yttrium tailings powder;

[0050] 3 parts of nanometer bismuth vanate powders;

[0051] 2 parts of JYM-087B rubber powder;

[0052] 1.5 parts of tributoxyethyl phosphate;

[0053] 1 part of compound dispersant:

[0054] 1 part of compound coupling agent;

[0055] 2 parts of compound foaming agent;

[0056] 1.5 parts of antioxidant antioxidant.

[0057] The selection and preparation of the compound dispersant, compound coupling agent, compound foaming agent and antioxidant anti-aging agent in this embodiment are shown in Table 1 below:

[0058] Table 1

[0059]

[0060] The preparation ...

Embodiment 2

[0065] This embodiment relates to a wood-plastic profile added with niobium-yttrium tailings powder and a preparation method thereof. The wood-plastic profile consists of the following raw materials in parts by weight:

[0066] Polyvinyl chloride resin powder SG-4 76 parts;

[0067] 13 parts of hydroxypropyl methacrylate;

[0068] 36 parts palm leaf fiber;

[0069] 12 parts of niobium yttrium tailings powder;

[0070] 3.5 parts of nanometer bismuth vanate powder;

[0071] JYM-087B rubber powder 2.3 parts;

[0072] 1.7 parts of tributoxyethyl phosphate;

[0073] 1.2 parts of compound dispersant:

[0074] 1.4 parts of compound coupling agent;

[0075] 2.5 parts of compound blowing agent;

[0076] Antioxidant antiaging agent 2 parts.

[0077] The selection and preparation of compound dispersant, compound coupling agent, compound foaming agent and anti-oxidant anti-aging agent in this embodiment are shown in Table 2 below:

[0078] Table 2

[0079]

[0080] The prepar...

Embodiment 3

[0085] This embodiment relates to a wood-plastic profile added with niobium-yttrium tailings powder and a preparation method thereof. The wood-plastic profile consists of the following raw materials in parts by weight:

[0086] Polyvinyl chloride resin powder SG-4 79 parts;

[0087] 14 parts of hydroxypropyl methacrylate;

[0088] 38 parts palm leaf fiber;

[0089] 13 parts of niobium yttrium tailings powder;

[0090] 4 parts of nanometer bismuth vanate powders;

[0091] JYM-087B rubber powder 2.5 parts;

[0092] 2 parts of tributoxyethyl phosphate;

[0093] 1.6 parts of compound dispersant:

[0094] 1.5 parts of compound coupling agent;

[0095] 2.8 parts of compound blowing agent;

[0096] 2.3 parts of antioxidant antioxidant.

[0097] The selection and preparation of compound dispersant, compound coupling agent, compound foaming agent and anti-oxidant anti-aging agent in this embodiment are shown in Table 3 below:

[0098] table 3

[0099]

[0100]

[0101] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wood-plastic profile prepared from added samarskite tailing powder and application of the wood-plastic profile, and relates to the technical field of wood-plastic profiles. The wood-plastic profile is prepared from the following raw materials: polyvinyl chloride resin powder SG-4, hydroxypropyl methacrylate, livistona chinensis leaf fibers, the samarskite tailing powder,nanometer bismuth vanadate powder, JYM-087B rubber powder, tris(2-butoxyethyl), a compound dispersion agent, a compound coupling agent, a compound foaming agent and an antioxidant antiager. The mechanical strength, the physical stability, the purification capability, the antibacterial property, the shielding property and the like of the wood-plastic profile are significantly improved, the overallperformance is better, the applicability is better, and the service life is more secure.

Description

technical field [0001] The invention relates to the technical field of wood-plastic profiles, in particular to a wood-plastic profile added with niobium-yttrium tailings powder and its application. Background technique [0002] Wood-plastic profiles, also known as wood-plastic composite materials, are made of wood powder, agricultural straw powder and other plant fibers and plastics as the main raw materials, processed by advanced technology, and the products can be recycled and reused repeatedly. In recent years, with the depletion of global resources, social awareness of environmental protection is increasing. As a brand-new green environmental protection product, wood-plastic composite material is an ecologically clean composite material. Its production raw materials can use various waste plastics, waste wood and agricultural and forestry residues. It helps to slow down the pollution of plastic waste, and also helps to reduce the environmental pollution caused by the in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L97/02C08K13/02C08K3/24C08K5/521C08K5/18C08K5/3437C08J9/10